Pt and Ru X-ray absorption spectroscopy of PtRu anode catalysts in operating direct methanol fuel cells.
In situ X-ray absorption spectroscopy, ex situ X-ray fluorescence, and X-ray powder diffraction enabled detailed core analysis of phase segregated nanostructured PtRu anode catalysts in an operating direct methanol fuel cell (DMFC). No change in the core structures of the phase segregated catalyst was observed as the potential traversed the current onset potential of the DMFC. The methodology was exemplified using a Johnson Matthey unsupported PtRu (1:1) anode catalyst incorporated into a DMFC membrane electrode assembly. During DMFC operation the catalyst is essentially metallic with half of the Ru incorporated into a face-centered cubic (FCC) Pt alloy lattice and the remaining half in an amorphous phase. The extended X-ray absorption fine structure (EXAFS) analysis suggests that the FCC lattice is not fully disordered. The EXAFS indicates that the Ru-O bond lengths were significantly shorter than those reported for Ru-O of ruthenium oxides, suggesting that the phases in which the Ru resides in the catalysts are not similar to oxides.
Stoupin
Stanislav
S
Physics Division, Department of Biological, Chemical, and Physical Sciences, Illinois Institute of Technology, Chicago, 60616, USA.
Chung
Eun-Hyuk
EH
Chattopadhyay
Soma
S
Segre
Carlo U
CU
Smotkin
Eugene S
ES
D002384:Catalysis; D004566:Electrodes; D005583:Fourier Analysis; D000432:Methanol / Q000737:chemistry*; D015233:Models, Statistical; D010984:Platinum / Q000737:chemistry*; D012428:Ruthenium / Q000737:chemistry*; D013057:Spectrum Analysis
D010984:Platinum; D012428:Ruthenium; D000432:Methanol