Synthesis of layered (2-D) V-based bimetallic oxalates from non-aqueous media that cannot be synthesized from aqueous media.
The reaction of (NBu4)3[V(III)(ox)3] (1, ox = oxalate) and M(II) (M = Fe, Co, Ni, Cu) ions in MeCN, leads to the isolation of V-based coordination polymers of [N(n-Bu)4][Fe(II)V(II)I(ox)3].0.30[[N(n-Bu)4](BF4)] (2), [N(n-Bu)4][Co(II)V(III)(ox)3].0.75[[N(n-Bu)4](BF4)] (3), [N(n-Bu)4][Ni(II)V(III)(ox)3].0.20[[N(n-Bu)4](BF4)].0.20MeCN (4), and [N(n-Bu)4][Cu(II)V(III)(ox)2](BF4)2 (5) composition. Due to the lability of [V(III)(ox)3]3- to dissociate ox2-, these compounds cannot be prepared from aqueous media. 5 is best described as [N(n-Bu)4][V(III)Cu(II)(ox)2](BF4)2, and 2, 3, 4, and 5 are proposed to have a layered (2-D) motif for the MM(ox)x (x = 2, 3) extended framework. The [V(III)Cu(II)(ox)2] composition of 5 is reported for the first time for a bimetallic oxalate. 2 shows a weak antiferromagnetic interaction between Fe(II), S = 2 and V(III), S = 1 ions (theta = -9.4 K) within the 2-D layers. 3 and 5 do not magnetically order above 2 K. 4 magnetically order as ferromagnets below 2.55 K [taken as the onset of magnetization in chi''(T)], and has a glass transition temperature (chi'(max) at 1000 Hz) at 2.26 K.
Min
Kil Sik
KS
Department of Chemistry, University of Utah, 315 S. 1400 E. RM 2124, Salt Lake City, UT 84112-0850, USA.
Miller
Joel S
JS