High strength, low stiffness, porous NiTi with superelastic properties.
Near-stoichiometric NiTi with up to 18% closed porosity was produced by expansion at 1200 degrees C of argon-filled pores trapped by powder metallurgy within a NiTi billet. When optimally heat-treated, NiTi with 6-16% porosity exhibits superelasticity, with recoverable compressive strains up to 6% at a maximum compressive stress up to 1700 MPa. The apparent Young's modulus of NiTi with 16% porosity, measured during uniaxial compression, is in the range of 15-25 GPa (similar to human bone), but is much lower than measured ultrasonically (approximately 40 GPa), or predicted from continuum elastic mechanics. This effect is attributed to the reversible stress-induced transformation contributing to the linear elastic deformation of porous NiTi. The unique combination of low stiffness, high strength, high recoverable strains and large energy absorption of porous superelastic NiTi, together with the known biocompatibility of NiTi, makes this material attractive for bone-implant applications.
Greiner
Christian
C
Department of Materials Science and Engineering, Northwestern University, Evanston, IL 60208, USA.
Oppenheimer
Scott M
SM
Dunand
David C
DC
D018786:Bone Substitutes / Q000032:analysis / Q000737:chemistry*; D019245:Compressive Strength; D004548:Elasticity; D006358:Hot Temperature; D008422:Materials Testing; D009532:Nickel / Q000032:analysis / Q000737:chemistry*; D016062:Porosity; D013499:Surface Properties; D013718:Tensile Strength; D014025:Titanium / Q000032:analysis / Q000737:chemistry*
D018786:Bone Substitutes; C040654:titanium nickelide; D009532:Nickel; D014025:Titanium