Effects of advanced oxidation on green sand properties via iron casting into green sand molds.
The effects of advanced oxidation (AO) processing on the properties of green sand were studied via pouring cast iron into green sand molds. Upon cooling, the green sand molds were autopsied at various distances from the metal-sand interface. Autopsy green sand samples collected from a mold that incorporated AO water were characterized and compared to controlled samples collected from a similar autopsied mold made with conventional tap water (TAP). It was found that the AO processing removed a coating of coal pyrolysis products from the clay surface that typically accumulated on the clay surface. As a result, the AO-conditioned green sand retained 10-15% more active clay as measured bythe standard ultrasonic methylene blue titration than did the TAP-conditioned green sand. The AO processing also nearly doubled the generation of activated carbon from the normalized amount of coal composition of the green sand during the casting process. The AO-enhanced activated carbon generation and the AO-incurred clay surface cleaning provided the AO-conditioned green sand with higher normalized pore volume, and thus higher normalized m-xylene adsorption capacity, i.e., relative to before-metal-pouring conditions. Furthermore, mathematical analysis indicated that the AO-conditioned green sand better retained its important properties after pouring than did the TAP-conditioned green sand. Effectively, this meant after metal pouring, the AO-conditioned sample offered about the same net properties as the TAP-conditioned sample, even though the AO-conditioned sample contained less clay and coal before metal pouring. These results conformed to the full-scale foundry empirical finding that when AO is used, foundries need less makeup clay and coal addition through each casting cycle, and they release less air emissions.
Wang
Yujue
Y
The Pennsylvania State University, University Park, Pennsylvania 16802, USA.
Cannon
Fred S
FS
Voigt
Robert C
RC
Komarneni
Sridhar
S
Furness
J C
JC
D000393:Air Pollutants; D000538:Aluminum Silicates; D001546:Bentonite / Q000032:analysis; D000077215:Clay; D003031:Coal; D007501:Iron / Q000032:analysis*; D008670:Metals / Q000032:analysis; D008962:Models, Theoretical; D010084:Oxidation-Reduction; D010100:Oxygen / Q000032:analysis*; D012822:Silicon Dioxide; D014874:Water Pollutants, Chemical; D014992:Xylenes
D000393:Air Pollutants; D000538:Aluminum Silicates; D003031:Coal; D008670:Metals; D014874:Water Pollutants, Chemical; D014992:Xylenes; D001546:Bentonite; D012822:Silicon Dioxide; D007501:Iron; D010100:Oxygen; D000077215:Clay