Effects of Fe-doping on the photocatalytic activity of mesoporous TiO2 powders prepared by an ultrasonic method.
Highly photoactive nanocrystalline mesoporous Fe-doped TiO(2) powders were prepared by the ultrasonic-induced hydrolysis reaction of tetrabutyl titanate (Ti(OC(4)H(9))(4)) in a ferric nitrate aqueous solution (pH 5) without using any templates or surfactants. The as-prepared samples were characterized by thermogravimetry and differential thermal analysis (TG-DTA), X-ray diffraction (XRD), N(2) adsorption-desorption measurements, UV-visible adsorbance spectra (UV-vis) and X-ray photoelectron spectroscopy (XPS). The photocatalytic activities were evaluated by the photocatalytic oxidation of acetone in air. The results showed that all the Fe-doped TiO(2) samples prepared by ultrasonic methods were mesoporous nanocrystalline. A small amount of Fe(3+) ions in TiO(2) powders could obviously enhance their photocatalytic activity. The photocatalytic activity of Fe-doped TiO(2) powders prepared by this method and calcined at 400 degrees C exceeded that of Degussa P25 (P25) by a factor of more than two times at an optimal atomic ratio of Fe to Ti of 0.25. The high activities of the Fe-doped TiO(2) powders could be attributed to the results of the synergetic effects of Fe-doping, large BET specific surface area and small crystallite size.
Zhou
Minghua
M
State Key Laboratory of Advanced Technology for Material Synthesis and Processing, Wuhan University of Technology, Luoshi Road 122, Wuhan 430070, PR China.
Yu
Jiaguo
J
Cheng
Bei
B
D002384:Catalysis; D007501:Iron / Q000737:chemistry*; D007700:Kinetics; D009584:Nitrogen / Q000737:chemistry; D010777:Photochemistry; D011208:Powders; D013057:Spectrum Analysis; D013696:Temperature; D014025:Titanium / Q000737:chemistry*; D014465:Ultrasonics; D014961:X-Ray Diffraction
D011208:Powders; C009495:titanium dioxide; D014025:Titanium; D007501:Iron; D009584:Nitrogen