Synthesis and electrochemical properties of chemically substituted LiMn2O4 prepared by a solution-based gel method.
Lithium manganese oxide, LiMn(2)O(4), and its substituted samples LiM(0.05)Mn(1.95)O(4) (M=Al, Co, and Zn) were first prepared by a cost-saving and effective new solution-based gel method using a mixture of acetate and ethanol as the chelating agent. The physical properties of the synthesized samples were investigated by thermogravimetry/differential thermal analysis, X-ray diffraction, and scanning electronic microscopy. The as-prepared powders were used as positive materials for a lithium-ion battery, whose charge/discharge properties and cycle performance were examined. The results revealed that all the substituted samples had better cycle performance than pure LiMn(2)O(4). Among these synthesized materials, the LiCo(0.05)Mn(1.95)O(4) sample had the best cycle performance. After 30 cycles, its capacity loss was only 3%. Therefore, cyclic voltammetry and electrochemical impedance spectroscopy were employed to characterize the reactions of Li ion insertion into and extraction from LiCo(0.05)Mn(1.95)O(4) electrodes.
He
Ben-Lin
BL
College of Chemistry and Chemical Engineering of Lanzhou University, Lanzhou 730000, People's Republic of China.
Zhou
Wen-Jia
WJ
Liang
Yan-Yu
YY
Bao
Shu-Juan
SJ
Li
Hu-Lin
HL