Surface morphologies of Langmuir-Blodgett monolayers of PEOnPSn multiarm star copolymers.
Star polymers composed of equal numbers of poly(ethylene oxide) (PEO) and polystyrene (PS) arms with variable lengths and a large (up to 38 total) number of arms, PEO(n)PS(n), have been examined for their ability to form domain nanostructures at the air-water and air-solid interfaces. All PEO(n)PS(n) star polymers formed stable Langmuir-Blodgett (LB) monolayers transferable to a solid substrate. A range of nanoscale surface morphologies have been observed, ranging from cylindrical to circular domains to bicontinuous structures as the weight fraction of the PEO block varied from 19% to 88% and n from 8 to 19. For the PS-rich stars and at elevated surface pressure, a two-dimensional supramolecular netlike nanostructure was formed. In contrast, in the PEO-rich star polymer with the highest PEO content, we observed peculiar dendritic superstructures caused by intramolecular segregation of nonspherical core-shell micellar structures. On the basis of Langmuir isotherms and observed monolayer morphologies, three different models of possible surface behavior of the star polymers at the interfaces were proposed.
Gunawidjaja
Ray
R
Department of Materials Science and Engineering, Iowa State University, Ames, Iowa 50011, USA.
Peleshanko
Sergiy
S
Genson
Kirsten L
KL
Tsitsilianis
Constantinos
C
Tsukruk
Vladimir V
VV