title: Metallic brackets bonded with resin-reinforced glass ionomer cements under different enamel conditions.
abstract: OBJECTIVE
  To assess the shear bond strength of metallic orthodontic brackets bonded with either Fuji Ortho or Ortho Glass LC resin-reinforced glass ionomer cements to enamel surfaces under different conditions, namely, enamel without etching, enamel conditioned with 37% phosphoric acid and enamel conditioned with Transbond Plus Self Etching Primer (TPSEP).
  
  
  METHODS
  One hundred and five bovine inferior incisors were divided into seven groups (n = 15). In group 1 (control) Transbond XT was used according to the manufacturer's recommendations. In groups 2, 3, and 4 all using Fuji Ortho LC, the brackets were bonded, respectively, to enamel nonetched, enamel etched with 37% phosphoric acid, and enamel etched with TPSEP. In groups 5, 6, and 7, the bonding was performed using Ortho Glass LC under the same enamel conditions observed in the other experimental groups. After 24 hours, shear bond strength tests were performed for all samples at a crosshead speed of 0.5 mm/min.
  
  
  RESULTS
  The results (MPa) showed no statistically significant difference between groups 1, 3, and 4 (P > .05). However, such groups were statistically superior to the others (P < .05). No statistically significant difference was observed between groups 2, 6, and 7 (P > .05). Group 5 showed the lowest shear strength value, which was also statistically inferior to the other groups (P < .05).
  
  
  CONCLUSIONS
  Regardless of the enamel treatment, Fuji Ortho LC yielded shear strength values superior to those from Ortho Glass LC.
authors.affiliation: Specialist of Orthodontics, Alfenas Pharmacy and Dental School-Efoa/Ceufe, Minas Gerais, Brazil. matheuspithon@bol.com.br
authors.forename: Matheus Melo
authors.initials: MM
authors.lastname: Pithon
authors.forename: Rogério Lacerda
authors.initials: RL
authors.lastname: Dos Santos
authors.forename: Márlio Vinícius
authors.initials: MV
authors.lastname: de Oliveira
authors.forename: Antônio Carlos Oliveira
authors.initials: AC
authors.lastname: Ruellas
authors.forename: Fábio Lourenço
authors.initials: FL
authors.lastname: Romano
mesh_terms: D000134:Acid Etching, Dental; D000180:Acrylic Resins / Q000737:chemistry; D000538:Aluminum Silicates / Q000737:chemistry; D000818:Animals; D002417:Cattle; D003722:Dental Alloys / Q000737:chemistry*; D001840:Dental Bonding; D003743:Dental Enamel / Q000648:ultrastructure*; D005899:Glass Ionomer Cements / Q000737:chemistry*; D008422:Materials Testing; D016910:Orthodontic Brackets; D010756:Phosphoric Acids / Q000737:chemistry; D011897:Random Allocation; D019279:Resin Cements / Q000737:chemistry*; D033081:Shear Strength; D013499:Surface Properties; D013997:Time Factors
chemical_list: D000180:Acrylic Resins; D000538:Aluminum Silicates; D003722:Dental Alloys; C095451:Fuji Ortho LC; D005899:Glass Ionomer Cements; D010756:Phosphoric Acids; D019279:Resin Cements; C429625:Transbond Plus Self-Etching Primer; C477790:Transbond XT; C030242:phosphoric acid