Optical characterization of Eu3+ and Tb3+ ions doped zinc lead borate glasses.
This paper reports on the spectral analysis of Eu3+ or Tb3+ ions (0.5 mol%) doped heavy metal oxide (HMO) based zinc lead borate glasses from the measurement of their absorption, emission spectra and also different physical properties. From the XRD, DSC profiles, the glass nature and glass thermal properties have been studied. The measured emission spectrum of Eu3+ glass has revealed five transitions (5D0-->7F0, 7F1, 7F2, 7F3 and 7F4) at 578, 591, 613, 654 and 702 nm, respectively, with lambdaexci=392 nm (7F0-->5L6). In the case of Tb3+:ZLB glass, four emission transitions such as (5D4-->7F6, 7F5, 7F4 and 7F3) that are located at 489, 542, 585 and 622 nm, respectively, have been measured with lambdaexci=374 nm. For all these emission bands decay curves have been plotted to evaluate their lifetimes and the emission processes that arise in the glasses have been explained in terms of energy level schemes.
Thulasiramudu
A
A
Department of Physics, Sri Venkateswara University, Tirupati 517502, India.
Buddhudu
S
S
D001881:Borates / Q000737:chemistry; D005063:Europium / Q000737:chemistry*; D005898:Glass / Q000737:chemistry*; D007854:Lead / Q000737:chemistry; D013050:Spectrometry, Fluorescence / Q000379:methods; D013725:Terbium / Q000737:chemistry*; D015032:Zinc / Q000737:chemistry; D017967:Zinc Compounds / Q000737:chemistry
D001881:Borates; D017967:Zinc Compounds; D013725:Terbium; D007854:Lead; D005063:Europium; D015032:Zinc