Combined magnetic and single-crystal X-ray structural study of the linear chain antiferromagnet [(CH3)4N][MnCl3] under varying pressure.
The magnetic susceptibility and single-crystal X-ray structure of the one-dimensional Heisenberg antiferromagnetic chain tetramethylammonium manganese trichloride (TMMC) have been studied under pressure as a facile route to develop structure-property relationships. The X-ray structure of TMMC was determined at 0, 2.1, 3.8, 6.8, 12.2, and 17.0 kbar using diamond-anvil cell techniques and synchrotron radiation. The space group is confirmed to be P6(3)/m up to 17 kbar, and structural refinement shows that the Mn-Mn separations between and along the chains change by about 3.4 and 2.5%, respectively, over 17 kbar. A structural transition from hexagonal to monoclinic symmetry possibly occurs at 17 kbar, associated with a loss of crystal quality. Variable-temperature magnetic susceptibility data were taken at 0, 0.3, 1.5, 2.9, 4.0, 5.2, and 6.5 kbar and show that the intrachain coupling constant changes from -6.85 to -7.81 K over this range. The interchain coupling constant of -0.54 K can also be extracted from the Fisher model modified for interacting chains. The pressure-temperature diagram shows the slope of the intrachain antiferromagnetic coupling with pressure, DeltaT(IAF)/DeltaP, changes from 0.5 to 1.6 K/kbar at 2 kbar where the structure changes from P2(1)/a to P2(1)/m. Comparison of the magnetic and structural data are consistent with the power-law relationship developed by Bloch where J proportional, variant r-n, r = Mn...Mn separation and n approximately 10.
Tancharakorn
Somchai
S
Contribution from the Centre for Science at Extreme Conditions, School of Engineering and Electronics, School of Chemistry, University of Edinburgh, King's Buildings, Mayfield Road, Edinburgh EH9 3JZ, United Kingdom.
Fabbiani
Francesca P A
FP
Allan
David R
DR
Kamenev
Konstantin V
KV
Robertson
Neil
N