Biomimetic implant coatings.
Biomaterials and tissue engineering technologies are becoming increasingly important in biomedical practice, particularly as the population ages. Cellular responses depend on topographical properties of the biomaterial at the nanometer scale. Structures on biomaterial surfaces are used as powerful tools to influence or even control interactions between implants and the biological system [; ]. The influence of nanometer sized surface structures on osteoblastlike cell interactions was tested with niobium oxide coatings on polished titanium slices (cp-Ti grade 2). The aim of the study was to investigate the influence of nanoscopic surface structures on osteoblast interactions in order to support collagen I production and cell adhesion. The coatings were done by means of the sol-gel process. The surface structure was adjusted by annealing of the metaloxide ceramic coatings due to temperature depended crystal growth. The applied annealing temperatures were 450, 550 and 700 degrees C for 1 h, corresponding to Ra-numbers of 7, 15 and 40 nm. The surfaces were characterized by means of AFM, DTA/TG, diffractometry and white light interferometry. The cell reactions were investigated concerning adhesion kinetics, migration, spreading, cell adhesion, and collagen I synthesis. The smooth surface (Ra=7 nm) resulted in the fastest cell anchorage and cell migration. The closest cell adhesion was reached with the surface structure of Ra=15 nm. The roughest surface (Ra=40 nm) impedes the cell migration as well as a proper spreading of the cells. The best results concerning cell adhesion and spreading was reached with an intermediate surface roughness of Ra=15 nm of the niobium oxide coating on cp-titanium slices.
Eisenbarth
E
E
Hamburg University of Technology, Department of Biomechanics, Hamburg, Germany. eva.eisenbarth@tuhh.de
Velten
D
D
Breme
J
J
D016475:3T3 Cells; D000818:Animals; D040761:Biomimetic Materials / Q000737:chemistry*; D002448:Cell Adhesion / Q000502:physiology; D002465:Cell Movement / Q000502:physiology; D049109:Cell Proliferation; D020099:Coated Materials, Biocompatible / Q000737:chemistry*; D008422:Materials Testing; D051379:Mice; D049329:Nanostructures / Q000737:chemistry / Q000648:ultrastructure; D009556:Niobium / Q000737:chemistry; D010006:Osteoblasts / Q000166:cytology* / Q000502:physiology*; D010087:Oxides / Q000737:chemistry; D010316:Particle Size; D019736:Prostheses and Implants; D013499:Surface Properties; D023822:Tissue Engineering / Q000379:methods*; D014025:Titanium / Q000737:chemistry*
D020099:Coated Materials, Biocompatible; D010087:Oxides; D009556:Niobium; D014025:Titanium; C073337:niobium pentoxide