Surface roughness of glass ionomer cements indicated for atraumatic restorative treatment (ART).
The purpose of this study was to evaluate the surface roughness of four conventional chemically cured glass ionomer cements (Fuji IX, Ketac Molar, Vidrion R and Vitromolar) commonly used in atraumatic restorative treatment (ART) immediately after material preparation. Twenty specimens of each glass ionomer cement were fabricated and surface roughness was measured after material setting. The specimens were further examined under scanning electron microscopy. Data were analyzed statistically by Kruskal-Wallis test and Mann-Whitney test at 5% significance level. Two-by-two comparisons showed statistically significant difference (p<0.05) between all materials, except for Ketac Molar and Vidrion R, which had statically similar results (p>0.05). Regarding their results of surface roughness, the materials can be presented in a crescent order, as follows: Ketac Molar < Vidrion R < Fuji IX < Vitromolar. In conclusion, from the tested glass ionomer cements, Fuji IX, Ketac Molar and Vidrion R presented acceptable surface roughness after setting reaction while Vitromolar showed remarkably higher surface roughness.
da Silva
Renata Cristiane
RC
Department of Pediatric Dentistry and Orthodontics, Faculty of Dentistry of Araraquara, São Paulo State University, São Paulo, SP, Brazil.
Zuanon
Angela Cristina Cilense
AC
D003764:Dental Materials / Q000737:chemistry*; D003793:Dental Restoration, Permanent; D005899:Glass Ionomer Cements / Q000737:chemistry*; D013499:Surface Properties
D003764:Dental Materials; D005899:Glass Ionomer Cements; C577195:Vitromolar