Development of multilayer laminar-type diffraction gratings to achieve high diffraction efficiencies in the 1-8 keV energy region.
W/C and Co/SiO(2) multilayer gratings have been fabricated by depositing a multilayer coating on the surface of laminar-type holographic master gratings. The diffraction efficiency was measured by reflectometers in the energy region of 0.6-8.0 keV at synchrotron radiation facilities as well as with an x-ray diffractometer at 8.05 keV. The Co/SiO(2) and W/C multilayer gratings showed peak diffraction efficiencies of 0.47 and 0.38 at 6.0 and 8.0 keV, respectively. To our knowledge, the peak efficiency of the W/C multilayer grating is the highest measured with hard x rays. The diffraction efficiency of the Co/SiO(2) multilayer gratings was higher than that of the W/C multilayer grating in the energy range of 2.5-6.0 keV. However, it decreased significantly in the energy above the K absorption edge of Co (7.71 keV). For the Co/SiO(2) multilayer grating, the measured diffraction efficiencies agreed with the calculated curves assuming a rms roughness of approximately 1 nm.
Ishino
Masahiko
M
Quantum Beam Science Directorate, Japan Atomic Energy Agency, Kizu, Kyoto, Japan. ishino.masahiko@jaea.go.jp
Heimann
Philip A
PA
Sasai
Hiroyuki
H
Hatayama
Masatoshi
M
Takenaka
Hisataka
H
Sano
Kazuo
K
Gullikson
Eric M
EM
Koike
Masato
M