Effects of smear layer and surface moisture on dentin bond strength of a waterless all-in-one adhesive.
The purpose of this study was to evaluate the microtensile bond strength (MTBS) of a waterless all-in-one adhesive system, Absolute, to dentin. Eighteen human molars were either ground with 600-grit SiC paper or cut with a diamond bur. The following dentin bonding procedures were then performed: dentin surface was kept moist; dentin surface was dried; or dentin surface was dried but equivalent amount of water was added to the adhesive (1:1 by volume). After adhesive curing, a resin composite was incrementally built up. After the specimens were kept in water for one day, MTBSs were measured at a cross-head speed of 1 mm/min. Two-way ANOVA (p = 0.05) indicated that the MTBS of the adhesive system was not influenced by surface texture, but enhanced by the presence of water on tooth surface. It was concluded that water is essential to obtaining good dentin bonding for this adhesive system.
Umino
Ayuko
A
Cariology and Operative Dentistry, Department of Restorative Sciences, Graduate School, Tokyo Medical and Dental University, 1-5-45 Yushima, Bunkyo-ku, Tokyo 113-8549, Japan. umino.ope@tmd.ac.jp
Nikaido
Toru
T
Sultana
Shamim
S
Ogata
Miwako
M
Tagami
Junji
J
D000704:Analysis of Variance; D016009:Chi-Square Distribution; D001840:Dental Bonding; D003799:Dental Stress Analysis; D003804:Dentin; D003806:Dentin Permeability; D017220:Dentin-Bonding Agents; D006801:Humans; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D008963:Molar; D019279:Resin Cements; D016369:Smear Layer; D013718:Tensile Strength; D017155:Wettability
C514346:Absolute adhesive; D017220:Dentin-Bonding Agents; D019279:Resin Cements