Influence of contamination on bonding to zirconia ceramic.
The purpose of this study was to investigate the influences of contaminations and cleaning methods on bonding to dental zirconia ceramic. After saliva immersion and using silicone disclosing agent, airborne-particle abraded ceramic specimens were cleaned with isopropanol (AL), acetone (AC), 37% phosphoric acid (PA), additional airborne-particle abrasion (AA), or only with water rinsing (SS). Airborne-particle abraded specimens without contaminations (CL) were used as control group. For chemical analysis specimens of all groups were examined with X-ray photoelectron spectroscopy (XPS). Plexiglas tubes filled with composite resin were bonded to ceramic specimens using a phosphate-monomer containing composite luting resin. After 3-day water storage, tensile bond strengths (TBS) were tested. XPS analysis of group SS showed the presence of saliva and silicone (Si) contamination on the surface. The ratios of carbon/zirconium and oxygen/zirconium for groups PA and AA were comparable to those ratios obtained for group CL, indicating the removal of the organic saliva contamination. Airborne-particle abrasion and acetone completely removed Si contamination from ceramic surfaces. Isopropanol had little cleaning effect on the two contaminants. TBS (median +/- standard deviation) in MPa of the groups SS (11.6 +/- 3.1), AL (10.0 +/- 2.9), and AC (13.0 +/- 2.8) were statistically lower than those of groups PA (33.6 +/- 5.5), AA (40.1 +/- 3.6), and CL (47.0 +/- 8.1) (p < 0.001), while no differences were found in TBS between groups AA and CL (p > 0.5). Contamination significantly reduced bond strengths to zirconia ceramic. Airborne-particle abrasion was the most effective cleaning method.
Yang
Bin
B
Department of Prosthodontics, Christian-Albrechts University at Kiel, Arnold-Heller-Str. 16, 24105 Kiel, Germany. ybin@proth.uni-kiel.de
Scharnberg
Michael
M
Wolfart
Stefan
S
Quaas
Anne C
AC
Ludwig
Klaus
K
Adelung
Rainer
R
Kern
Matthias
M
D002516:Ceramics; D001840:Dental Bonding; D003764:Dental Materials; D003793:Dental Restoration, Permanent; D004340:Drug Contamination; D006801:Humans; D066298:In Vitro Techniques; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D012463:Saliva; D013057:Spectrum Analysis; D013499:Surface Properties; D013718:Tensile Strength; D014965:X-Rays; D015040:Zirconium
D003764:Dental Materials; D015040:Zirconium; C028541:zirconium oxide