Ultrasensitive chemiresistors based on electrospun TiO2 nanofibers.
Nanostructured semiconducting metal oxides and particularly single nanowire devices offer exceptional gas sensitivity but at the expense of statistical variations and excessive noise levels. In this study TiO2/poly(vinyl acetate) composite nanofiber mats were directly electrospun onto interdigitated Pt electrode arrays, hot pressed at 120 degrees C, and calcined at 450 degrees C. This resulted in a novel multiple nanowire network composed of sheaths of 200-500 nm diameter cores filled with readily gas accessible approximately 10 nm thick single-crystal anatase fibrils. TiO2 nanofiber sensors tested for NO2, in dry air, exhibited exceptional sensitivity showing with, for example, a 833% increase in sensor resistance when exposed to 500 ppb NO2 at 300 degrees C, consistent with a detection limit estimated to be well below 1 ppb. Unusual response patterns were observed at high NO2 concentrations (> 12.5 ppm), consistent with n to p inversion of the surface-trap limited conduction facilitated by the high surface-to-volume ratio of this material.
Kim
Il-Doo
ID
Optoelectronic Materials Research Center, Korea Institute of Science and Technology, Cheongryang, Seoul, Republic of Korea.
Rothschild
Avner
A
Lee
Byong Hong
BH
Kim
Dong Young
DY
Jo
Seong Mu
SM
Tuller
Harry L
HL
D003460:Crystallization / Q000379:methods*; D017097:Electric Impedance; D004563:Electrochemistry / Q000295:instrumentation* / Q000379:methods; D004867:Equipment Design; D019544:Equipment Failure Analysis; D008422:Materials Testing; D043942:Nanotubes / Q000737:chemistry* / Q000648:ultrastructure; D009569:Nitric Oxide / Q000032:analysis* / Q000737:chemistry*; D012399:Rotation; D014025:Titanium / Q000737:chemistry*; D014159:Transducers
C009495:titanium dioxide; D009569:Nitric Oxide; D014025:Titanium