Effect of temperature and chain length on the bimodal emission properties of single polyfluorene copolymer molecules.
Fluorescence emission spectra were recorded for isolated polymer chains of the polyfluorene copolymer, F8BT [poly(9,9-di-n-octylfluorene-alt-benzothiadiazole)], at 298 and 20 K for two molecular weights (chain lengths). For long-chain F8BT at 298 K, the observed distribution of single-molecule emission maxima G(Emax) is bimodal, with peaks at approximately 2.35 eV ("blue") and approximately 2.25 eV ("red"). Previously, the red forms have been assigned to polymer chains that possess intrachain contacts, which lowers the local singlet exciton energy. At approximately 20 K, G(Emax) collapses into a single broad distribution centered at approximately 2.3 eV for long-chain F8BT. However, this distribution can be further divided into a high-energy edge that is dominated by the "blue" form, while the remainder of the distribution is composed of the "red" form. Low-molecular-weight F8BT samples emit exclusively from the blue form, and no shift in peak maxima with low temperature was observed. A Franck-Condon analysis reveals a decrease in emitting state displacements between spectra measured at 298 and 20 K, suggesting that temperature-induced structural displacements are responsible for the change in the bimodal emission.
Grey
John K
JK
Center for Nano and Molecular Science and Technology and Department of Chemistry and Biochemistry, University of Texas at Austin, Austin, Texas 78712, USA.
Kim
Doo Young
DY
Donley
Carrie L
CL
Miller
William L
WL
Kim
Ji Seon
JS
Silva
Carlos
C
Friend
Richard H
RH
Barbara
Paul F
PF