Experimental investigation of basic oxygen furnace slag used as aggregate in asphalt mixture.
Chinese researchers have commenced a great deal of researches on the development of application fields of basic oxygen steel making furnace slag (BOF slag) for many years. Lots of new applications and properties have been found, but few of them in asphalt mixture of road construction engineering. This paper discussed the feasibility of BOF steel slag used as aggregate in asphalt pavement by two points of view including BOF steel slag's physical and micro-properties as well as steel slag asphalt materials and pavement performances. For the former part, this paper mainly concerned the mechanochemistry and physical changes of the steel slag and studied it by performing XRD, SEM, TG and mercury porosimeter analysis and testing method. In the second part, this paper intended to use BOF steel slag as raw material, and design steel slag SMA mixture. By using traditional rutting test, soak wheel track and modified Lottman test, the high temperature stability and water resistance ability were tested. Single axes compression test and indirect tensile test were performed to evaluate the low temperature crack resistance performance and fatigue characteristic. Simultaneously, by observing steel slag SMA pavement which was paved successfully. A follow-up study to evaluate the performance of the experimental pavement confirmed that the experimental pavement was comparable with conventional asphalt pavement, even superior to the later in some aspects. All of above test results and analysis had only one main purpose that this paper validated the opinion that using BOF slag in asphalt concrete is feasible. So this paper suggested that treated and tested steel slag should be used in a more extensive range, especially in asphalt mixture paving projects in such an abundant steel slag resource region.
Xue
Yongjie
Y
School of Resource and Environment Science, Wuhan University, Wuhan 430072, Hubei, PR China. Xueyj@mail.whut.edu.cn
Wu
Shaopeng
S
Hou
Haobo
H
Zha
Jin
J
D006838:Hydrocarbons; D007220:Industrial Waste; D008669:Metallurgy; D008855:Microscopy, Electron, Scanning; D008903:Minerals; D010100:Oxygen; D016062:Porosity; D017640:Silicates; D013314:Stress, Mechanical; D013499:Surface Properties; D013696:Temperature
D006838:Hydrocarbons; D007220:Industrial Waste; D008903:Minerals; D017640:Silicates; C060346:basalt; C006647:asphalt; D010100:Oxygen