Direct solid-state NMR spectroscopic evidence for the NH4AlF4 crystalline phase derived from zeolite HY dealuminated with ammonium hexafluorosilicate.
Multinuclear (1)H, (19)F, and (27)Al MAS (magic angle spinning) and corresponding 2D HETCOR (heteronuclear correlation) NMR spectroscopy, in combination with powder XRD measurements, provide the direct evidence for the NH(4)AlF(4) crystalline phase, which was formed from zeolite HY dealuminated with an aqueous (NH(4))(2)SiF(6) solution at 80 degrees C. The NH(4)AlF(4) crystalline phase exhibits a characteristic second-order quadrupolar-induced (27)Al NMR line shape spreading from 0 to -90 ppm (in a magnetic field of 11.7 T) and two (19)F resonances at -151 and -166 ppm in the (19)F NMR spectrum. An( 27)Al quadrupolar coupling constant (C(Q)) of 9.5 MHz and an asymmetry parameter (eta) of 0.1 were identified, for the first time, for the NH(4)AlF(4) crystalline phase observed. On the basis of the (19)F{(27)Al} TRAPDOR (transfer population in double resonance) NMR results, the (19)F resonances at -151 and -166 ppm are therefore assigned to (19)F spins associated with the fluorines in the terminal Al-F and the bridging Al-F-Al groups, respectively.
Kao
Hsien-Ming
HM
Chang
Pai-Ching
PC