title: The role of whole blood in thrombin generation in contact with various titanium surfaces.
abstract: Understanding of the thrombotic response (activation of the intrinsic coagulation system followed by platelet activation) from blood components upon contact with a titanium dental implant is important and not fully understood. The aims of this study were to evaluate: (1) the thrombogenic response of whole blood, platelet-rich plasma (PRP) and platelet-poor plasma (PPP) in contact with a highly thrombogenic surface as titanium, (2) the thrombogenic response of clinically used surfaces as hydroxyapatite (HA), machined titanium (mTi), TiO2 grit-blasted titanium (TiOB) and fluoride ion-modified grit-blasted titanium (TiOB-F). An in vitro slide chamber model, furnished with heparin, was used in which whole blood, PRP or PPP came in contact with slides of the test surfaces. After incubation (60 min rotation at 22 rpm in a 37 degrees C water bath), blood/plasma was mixed with EDTA or citrate, further centrifuged at +4 degrees C (2200 g at 10 min). Finally, plasma was collected pending analysis. Whole blood in contact with Ti alloy resulted in the binding of platelets to the material surface and in the generation of thrombin-antithrombin (TAT) complexes. With whole blood TAT levels increased 1000-fold compared with PRP and PPP, in which both almost no increase of TAT could be detected. In addition, the platelet activation showed a similar pattern with a 15-fold higher release of beta-TG in whole blood. In the in vitro chamber model with the clinically relevant materials, the fluoride-modified surface (TiOB-F) showed pronounced TAT generation compared with TiOB, mTi and HA. Similar results were achieved for platelet consumption and activation markers of the intrinsic coagulation system. Taken together these results implicate first that whole blood is necessary for sufficient thrombin generation and platelet activation during placement of implants. Second, a fluoride ion modification seems to augment the thrombogenic properties of titanium.
authors.affiliation: Department of Surgical Sciences; Oral & Maxillofacial Surgery, Uppsala University Hospital, SE-751 85 Uppsala, Sweden. andreas.thor@lul.se
authors.forename: Andreas
authors.initials: A
authors.lastname: Thor
authors.forename: Lars
authors.initials: L
authors.lastname: Rasmusson
authors.forename: Ann
authors.initials: A
authors.lastname: Wennerberg
authors.forename: Peter
authors.initials: P
authors.lastname: Thomsen
authors.forename: Jan-Michael
authors.initials: JM
authors.lastname: Hirsch
authors.forename: Bo
authors.initials: B
authors.lastname: Nilsson
authors.forename: Jaan
authors.initials: J
authors.lastname: Hong
mesh_terms: D001672:Biocompatible Materials / Q000737:chemistry*; D001777:Blood Coagulation / Q000502:physiology*; D001790:Blood Physiological Phenomena; D002478:Cells, Cultured; D006801:Humans; D008422:Materials Testing; D015539:Platelet Activation / Q000502:physiology*; D013499:Surface Properties; D013917:Thrombin / Q000378:metabolism*; D014025:Titanium / Q000737:chemistry*
chemical_list: D001672:Biocompatible Materials; D014025:Titanium; D013917:Thrombin