Adsorption of hydrogen isotopes on micro- and mesoporous adsorbents with orderly structure.
The equilibrium and dynamic adsorption data of H(2) and D(2) on different micro- and mesoporous adsorbents with orderly structure including 3A, 4A, 5A, Y, and 10X zeolites; carbon CMK-3; silica SBA-15; and so forth were collected. Critical effect of the nanodimension of adsorbents on the adsorption behavior of hydrogen and its isotopes is shown. The highest adsorption capacity was observed at pore size 0.7 nm, but equal or even larger isotope difference in the equilibrium adsorption was observed at larger pore sizes, whereas the largest isotope difference in the dynamic adsorption was observed at 0.5 nm. The adsorption rate of D(2) is larger than that of H(2) in microporous adsorbents, but the sequence could be switched over in mesoporous materials. Linear relationship was observed between the adsorption capacity for hydrogen and the specific surface area of adsorbents although the adsorbents are made of different material, which provides a convincing proof of the monolayer mechanism of hydrogen adsorption. The linear plot for microporous adsorbents has a larger slope than that for mesoporous adsorbents, which is attributed to the stronger adsorption potential in micropores.
Chu
Xiao-Zhong
XZ
Department of Chemistry, School of Science, Tianjin University, Tianjin 300072, P. R. China.
Zhou
Ya-Ping
YP
Zhang
Yu-Zhe
YZ
Su
Wei
W
Sun
Yan
Y
Zhou
Li
L