Promotion of the electrochemical activity of a bimetallic platinum-ruthenium catalyst by oxidation-induced segregation.
An alloy catalyst of 15 wt % Pt(50)Ru(50)/C was prepared by the method of incipient wetness impregnation and activated by hydrogen reduction at 620 K. Physical characterization of the freshly reduced catalyst indicated that bimetallic crystallites, Pt rich in the shell and Ru rich in the core, were finely dispersed in a diameter of dPtRu approximately 2 nm on carbon support. The reduced catalyst was subsequently modified by oxidization in air. On increasing the temperature of oxidation (T(o)), atoms of Ru in the core were found segregated to the surface of bimetallic crystallites and oxidized to amorphous RuO(2). Crystalline RuO(2) (RucO(2)) was formed on extensive segregation at To > 520 K. Catalytic activity of the alloy catalyst for electro-oxidation of methanol was examined by cyclic voltammetry. Electrochemical activity of the Pt-Ru/C catalyst was found to be significantly enhanced by oxidation treatments. The enhancement was, therefore, attributed to the segregation of Ru and the formation of RucO(2). Extensive oxidation treatment at elevated temperatures of To > 600 K, however, caused the deactivation of the electroactivity. The deactivation should be the result of excessive oxidation of the carbon support.
Huang
Sheng-Yang
SY
Department of Chemistry, National Tsing Hua University, Hsinchu, Taiwan 30013, Republic of China.
Chang
Shu-Min
SM
Lin
Chia-Ling
CL
Chen
Chun-Hsien
CH
Yeh
Chuin-Tih
CT