Simultaneous phase- and size-controlled synthesis of TiO(2) nanorods via non-hydrolytic sol-gel reaction of syringe pump delivered precursors.
The simultaneous phase- and size-controlled synthesis of TiO(2) nanorods was achieved via the non-hydrolytic sol-gel reaction of continuously delivered two titanium precursors using two separate syringe pumps. As the injection rate was decreased, the length of the TiO(2) nanorods was increased and their crystalline phase was simultaneously transformed from anatase to rutile. When the reaction was performed by injecting titanium precursors contained in two separate syringes into a hot oleylamine surfactant solution with an injection rate of 30 mL/h, anatase TiO(2) nanorods with dimensions of 6 nm (thickness) x 50 nm (length) were produced. When the injection rate was decreased to 2.5 mL/h, star-shaped rutile TiO(2) nanorods with dimensions of 25 nm x 200 nm and a small fraction of rod-shaped anatase TiO(2) nanorods with dimensions of 9 nm x 100 nm were synthesized. Pure star-shaped rutile TiO(2) nanorods with dimensions of 25 nm x 450 nm were synthesized when the injection rate was further decreased to 1.25 mL/h. The simultaneous phase transformation and length elongation of the TiO(2) nanorods were achieved. Under optimized reaction conditions, as much as 3.5 g of TiO(2) nanorods were produced. The TiO(2) nanorods were used to produce dye-sensitized solar cells, and the photoconversion efficiency of the mixture composed of star-shaped rutile TiO(2) nanorods and a small fraction of anatase nanorods were comparable to that of Degussa P-25.
Koo
Bonil
B
National Creative Research Center for Oxide Nanocrystalline Materials and School of Chemical and Biological Engineering, Seoul National University, Seoul 151-744, Korea.
Park
Jongnam
J
Kim
Yukyeong
Y
Choi
Sang-Hyun
SH
Sung
Yung-Eun
YE
Hyeon
Taeghwan
T
D003460:Crystallization; D005782:Gels / Q000737:chemistry*; D006868:Hydrolysis; D046529:Microscopy, Electron, Transmission; D049329:Nanostructures / Q000737:chemistry* / Q000648:ultrastructure; D044367:Phase Transition; D014025:Titanium / Q000737:chemistry*; D014961:X-Ray Diffraction
D005782:Gels; C009495:titanium dioxide; D014025:Titanium