On the crystal structure of Cr2N precipitates in high-nitrogen austenitic stainless steel. III. Neutron diffraction study on the ordered Cr2N superstructure.
The ordered structure of Cr(2)N precipitates in high-nitrogen austenitic steel was investigated utilizing high-resolution neutron powder diffractometry (HRPD). On the basis of the Rietveld refinement of neutron diffraction patterns, the ordered Cr2N superstructure was confirmed to be trigonal (space group P31m), with lattice parameters a=4.800 (4) and c=4.472 (5) A, as suggested in previous transmission electron microscopy studies [Lee, Oh, Han, Lee, Kim & Takaki (2005). Acta Cryst. B61, 137-144; Lee, Kim & Takaki (2006). Acta Cryst. B62, 190-196]. The occupancies of the N atoms in four crystallographic sites [1(a), 1(b), 2(d) and 2(c) Wyckoff sites] were determined to be 1.00 (5), 0.0, 0.74 (9) and 0.12 (3), respectively, reflecting a partial disordering of N atoms along the c axis. The position of the metal atom was specified to be x=0.346 (8) and z=0.244 (6), corresponding to a deviation from the ideal position (x=0.333 and z=0.250). This deviation caused the ((1/3 1/3)(0))-type superlattice reflection to appear. A comparison between the ideal and measured crystal structures of Cr2N was performed using a computer simulation of selected-area diffraction patterns.
Lee
Tae-Ho
TH
ECO-Materials Research Center, Korea Institute of Machinery and Materials, 66 Sangnam, Changwon 641-010, Republic of Korea.
Kim
Sung-Joon
SJ
Shin
Eunjoo
E
Takaki
Setsuo
S