In vitro testing of Nd:YAG laser processed calcium phosphate coatings.
Nd:YAG laser cladding is a new method for deposition of a calcium phosphate onto metallic surfaces of interest in implantology. The aim of this study was to compare the biologic response of MG-63 human osteoblast-like cells grown on Ti-6Al-4V substrates coated with a calcium phosphate layer applied using different methods: plasma spraying as reference material and Nd:YAG laser cladding as test material. Tissue culture polystyrene was used as negative control. The Nd:YAG laser clad material showed a behaviour similar to the reference material, plasma spray, respective to cell morphology (SEM observations), cell proliferation (AlamarBlue assay) and cytotoxicity of extracts (MTT assay). Proliferation, as measured by the AlamarBlue assay, showed little difference in the metabolic activity of the cells on the materials over an 18 day culture period. There were no significant differences in the cellular growth response on the test material when compared to the ones exhibited by the reference material. In the solvent extraction test all the extracts had some detrimental effect on cellular activity at 100% concentration, although cells incubated in the test material extract showed a proliferation rate similar to that of the reference material. To better understand the scope of these results it should be taken into account that the Nd:YAG clad coating has recently been developed. The fact that its in vitro performance is comparable to that produced by plasma spray, a material commercially available for more than ten years, indicates that this new laser based method could be of commercial interest in the near future.
De Carlos
A
A
Dpto. de Bioquímica, Genética e Inmunología, Universidade de Vigo, Vigo, Spain.
Lusquiños
F
F
Pou
J
J
León
B
B
Pérez-Amor
M
M
Driessens
F C M
FC
Hing
K
K
Best
S
S
Bonfield
W
W
D000497:Alloys; D000535:Aluminum; D002130:Calcium Phosphates; D002460:Cell Line; D020099:Coated Materials, Biocompatible; D006801:Humans; D007834:Lasers; D009354:Neodymium; D014025:Titanium; D015019:Yttrium
D000497:Alloys; D002130:Calcium Phosphates; D020099:Coated Materials, Biocompatible; C503779:yttrium-aluminum-garnet; C031462:titanium alloy (TiAl6V4); D009354:Neodymium; D015019:Yttrium; C020243:calcium phosphate; D000535:Aluminum; D014025:Titanium