A study of interface-sustained ferromagnetism in 1/2(1-x)Ln2O3-xSrO/1/3Co3O4 nano-composite.
The binary oxide composite, consisting of rock salt-type SrO and spinel Co3O4 nano-domains, exhibits soft ferromagnetic properties at ambient temperature. This ferromagnetism is originated from interface-induction, and the magnitude of the magnetic properties can be enhanced when the spinel phase of the composite is doped by a small amount of Ln2O3 (Ln = La, Nd, for instance). In this work, we study the composites of tri-oxide, 1/2(1-x)Ln2O3-xSrO/1/3Co3O4, where 0.01 < or =1-x < or = 0.6, by focusing on three areas: (i) generation of nano-composite dominant by interfacial phase via the pyrolysis of preceramic metallo-organic gel; (ii) influence of post-pyrolysis calcination and Ln2O3 content on the phase composition of the composite; and (iii) elucidation of different magnetic responses caused by the nature of Ln2O3 dissolved in the Co3O4 phase. The Ln(3+)-doped Co3O4 oxide displays only paramagnetic behavior at room temperature, but the ferromagnetic response is attained upon its mixing with SrO in nano-scale. The SrO phase plays the role in assisting Co3O4 phase with aligning unpaired electrons through interfacial induction.
Tay
Siok Wei
SW
Department of Chemical and Biomolecular Engineering, National University of Singapore, BLK E5 02-02, 4 Engineering Drive 4, 117576 Singapore; Institute of Materials Research and Engineering, 3 Research Link, 117602 Singapore.
Hong
Liang
L
Liu
Zhaolin
Z