In vitro hydrolytic degradation of composite quartz fiber-post bonds created by hydrophilic silane couplings.
The hydrolytic stability of a pre-activated MPS silane (Monobond-S) and a 2-component 4-META/ gamma-MPTS silane (Porcelain Liner M) to H202-etched quartz fiber posts was investigated using a modeling approach. Composite build-ups around silanized posts were stored dry for 24 hours, stored in deionized water at 37 degrees C for 24 hours, 1 week, 1 month or they were thermocycled. Sectioned specimens were prepared for microtensile bond testing and SEM examination; 4-META/gamma-MPTS silane produced a rapid decline in bond strength after 1 week and 1 month of water storage and after thermocycling. This was not apparent in pre-activated MPS silane. SEM revealed debonding along the post-composite interfaces, which were coupled with 2-component silane. The use of a hydrophilic resin monomer (4-META) for on-demand hydrolysis of the gamma-MPTS silane expedited interfacial water sorption and hydrolytic degradation, which may be prevented with alternative coupling strategies.
Monticelli
Francesca
F
Department of Restorative Dentistry and Dental Materials, Policlinico Le Scotte, University of Siena, Siena, Italy. francescamondti@hotmail.it
Osorio
Raquel
R
Toledano
Manuel
M
Tay
Franklin R
FR
Ferrari
Marco
M
D003188:Composite Resins; D001840:Dental Bonding; D003738:Dental Cements; D003799:Dental Stress Analysis; D017220:Dentin-Bonding Agents / Q000737:chemistry*; D006868:Hydrolysis; D008422:Materials Testing; D008689:Methacrylates; D011176:Post and Core Technique; D011791:Quartz; D012821:Silanes / Q000737:chemistry*; D013718:Tensile Strength; D017155:Wettability
D003188:Composite Resins; D003738:Dental Cements; D017220:Dentin-Bonding Agents; D008689:Methacrylates; C076808:Monobond S; D012821:Silanes; D011791:Quartz; C017492:methacryloxypropyltrimethoxysilane; C034139:4-methacryloxyethyltrimellitic acid anhydride