Formation of orientation-ordered superlattices of magnetite magnetic nanocrystals from shape-segregated self-assemblies.
Magnetic magnetite (Fe3O4) nanocrystals have been synthesized by combining nonhydrolytic reaction with seed-mediated growth. The shape of these magnetite nanocrystals can be controlled either as pure spheres or a mixture of mainly faceted nanocrystals. Faceted magnetite nanocrystals consist of truncated tetrahedral platelets (TTPs), truncated octahedrons (TOs), and octahedrons (OTs). Transmission electron microscopy analysis indicates that the faceted nanocrystal mixture tends to self-segregate based upon the shape in a self-assembly process, and each shape forms its own distinct crystallographic orientation-ordered superlattice assemblies. Self-assemblies of the Fe3O4 nanocrystals in the shapes of TTP, TO, and OT show hexagonal, primitive cubic, and distorted body-centered cubic (bcc) superlattice structures, respectively. The possible mechanism for the formation of different superstructures is attributed to van der Waals interactions. Nanocrystals with different shapes provide diverse building blocks for bottom-up approaches in building nano- and mesosystems. Furthermore, the self-segregation phenomenon of different shaped nanocrystals in self-assembly processes could be very important in envisioning efficient assembly strategies for nanoscience- and nanotechnology-based devices.
Song
Qing
Q
School of Chemistry and Biochemistry, Georgia Institute of Technology, Atlanta, Georgia 30332-0400, USA.
Ding
Yong
Y
Wang
Zhong Lin
ZL
Zhang
Z John
ZJ
D003460:Crystallization; D052203:Ferrosoferric Oxide / Q000138:chemical synthesis* / Q000737:chemistry; D008280:Magnetics; D046529:Microscopy, Electron, Transmission; D049329:Nanostructures / Q000737:chemistry*; D010316:Particle Size; D033362:Powder Diffraction; D012680:Sensitivity and Specificity
D052203:Ferrosoferric Oxide