Two organically templated niobium and zinconiobium fluorophosphates: low temperature hydrothermal syntheses of NbOF(PO4)2(C2H10N2)2 and Zn3(NbOF)(PO4)4(C2H10N2)2.
Two new niobium and zinconiobium fluorophosphates, NbOF(PO4)2(C2H10N2)2 (1) and Zn3(NbOF)(PO4)4-(C2H10N2)2 (2), have been prepared under hydrothermal conditions using ethylenediamine as a template. The structures were determined by single crystal diffraction to be triclinic, space group P1 (No. 2), a = 8.1075 (6) A, b = 9.8961 (7) A, c = 10.1420(8) A, alpha = 111.655(1) degrees, beta = 111.51(1) degrees, gamma = 93.206(1) degrees, V = 686.19(9) A3, and Z = 2 for 1 and orthorhombic, space group Fddd (No. 70), a = 9.1928(2) A, b = 14.2090(10) A, c = 32.2971 (6) A, V = 4218.66(12) A3, and Z = 8 for 2, respectively. Compound 1 is an infinite linear chain consisting of corner-sharing [Nb2P2] 4-MRs bridged at the Nb centers with organic amines situated between chains, and compound 2, containing the chains similar to that in 1, forms a zeotype framework with organic amines situated in the gismondine-type [4684] cavities. The topology of 2 was previously unknown with vertex symbol 4 x 4 x 4 x 4 x 8 x 8 (vertex 1), 4 x 4 x 4 x 82 x 8 x 8 (vertex 2), 4 x 4 x 8 x 8 x 82 x 82 (vertex 3), and 4 x 4 x 4 x 82 x 8 x 8 (vertex 4). The topological relationships between the 4-connected network of 2 and several reported (3,4)-connected networks were discussed.
Liu
Guang-Zhen
GZ
State Key Laboratory of Structural Chemistry, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, Fuzhou, Fujian 350002, China.
Zheng
Shou-Tian
ST
Yang
Guo-Yu
GY