Preparation and structural evolution of SiO(2)-TiO(2) pillared layered manganese oxide nanocomposite upon intercalating reaction.
SiO(2)-TiO(2) pillared layered manganese oxide nanohybrid was successfully synthesized by preliminarily expanding the interlayer of H-type layered manganese oxide using dodecylamine, followed by reacting it with a mixture solution of titanium isopropoxide and tetraethylorthosilicate. The basal spacing and the pillared agent content of the obtained materials connected with the length of intercalated n-alkylamine, incorporated Si/Ti molar ratios and the solvothermal treatment temperature. The structural evolution of SiO(2)-TiO(2) pillared layered manganese oxide nanohybrid was characterized by XRD, DSC-TGA, SEM, IR, N(2) adsorption-desorption and element analyses. TiO(2) particles exhibited a stronger affinity for the negatively charged manganese layers, and the TiO(2) particles incorporated were independently intercalated without any distinct chemical bonding with the co-intercalated SiO(2) particles. SiO(2)-TiO(2) pillared layered manganese oxide nanohybrid had a BET surface area of 98 m(2)/g with a gallery height of about 1.43 nm between layers. The obtained SiO(2)-TiO(2) co-pillared layered manganese oxide nanohybrid is expected as a selective catalyst, or an improved battery material.
Wang
Jianfang
J
Key Laboratory for Macromolecular Science of Shaanxi Province, School of Chemistry and Materials Science, Shaanxi Normal University, Xi'an 710062, People's Republic China.
Liu
Zong-Huai
ZH
Tang
Xiuhua
X
Ooi
Kenta
K