Evaluation of the enamel etching capacity of six contemporary self-etching adhesives.
OBJECTIVE
The purpose of this study was to evaluate the capacity of six contemporary self-etch primers/adhesives to demineralize ground enamel by means of ultrastructural analysis of the etching surface under SEM and by spectroscopic measurement of the percentage of calcium and phosphate ions dissolved.


METHODS
Seventy non-carious extracted human third molars were sub-divided into 2 groups of 35 teeth each. The teeth of the first group were ground to expose flat, polished enamel surfaces 3-4mm thick. The samples thus obtained were treated with six self-etch bonding systems and a phosphoric acid gel (control group). The self-etch priming agent was then eliminated and the etched enamel surface observed by SEM. From the teeth of the second group, disc-shaped specimens were made from ground enamel and subjected to application of each of the six self-etchants. Once the etching product had been rinsed off, the rinse solution was analyzed by atomic flame spectroscopy to evaluate the percentage of calcium and phosphate ions dissolved.


RESULTS
SEM images show that AdheSE, Adper Prompt L-Pop and Xeno III, despite having a less intensive etching efficacy than phosphoric acid, gave a regular pattern over a considerable surface area and depth. iBond and One-Up Bond F gave less regular demineralization. For Clearfil SE Bond, the demineralization was ineffective. Results of the percentage of mineral loss show that Adper Prompt L-Pop and Xeno III were the most efficient self-etch products. AdheSE, iBond and One-Up Bond F, respectively exhibited decreasing demineralizing capacity. Clearfil SE Bond, however, gave low proportions of calcium and phosphate ions loss and was considered unsatisfactory.


CONCLUSIONS
The action on enamel was not the same for all self-etch systems tested. The etching potential of the self-etch adhesives was lower than that of phosphoric acid but some self-etch systems, particularly those with monomers containing phosphate derivatives, gave results close to those obtained with phosphoric acid.
Grégoire
Geneviève
G
Biomaterials Laboratory, Faculty of Odontology, University of Toulouse III, Toulouse, France. gregoire@cict.fr
Ahmed
Yasin
Y
D000134:Acid Etching, Dental; D002118:Calcium / Q000032:analysis; D003743:Dental Enamel / Q000187:drug effects* / Q000648:ultrastructure; D003747:Dental Enamel Solubility; D017220:Dentin-Bonding Agents / Q000494:pharmacology*; D006801:Humans; D008855:Microscopy, Electron, Scanning; D008964:Molar, Third; D010756:Phosphoric Acids / Q000494:pharmacology; D010758:Phosphorus / Q000032:analysis; D019279:Resin Cements / Q000494:pharmacology*
D017220:Dentin-Bonding Agents; D010756:Phosphoric Acids; D019279:Resin Cements; D010758:Phosphorus; C030242:phosphoric acid; D002118:Calcium