Mechanistic study of precursor evolution in colloidal group II-VI semiconductor nanocrystal synthesis.
The molecular mechanism of precursor evolution in the synthesis of colloidal group II-VI semiconductor nanocrystals was studied using 1H, 13C, and 31P NMR spectroscopy and mass spectrometry. Tri-n-butylphosphine chalcogenides (TBPE; E = S, Se, Te) react with an oleic acid complex of cadmium or zinc (M-OA; M = Zn, Cd) in a noncoordinating solvent (octadecene (ODE), n-nonane-d20, or n-decane-d22), affording ME nanocrystals, tri-n-butylphosphine oxide (TBPO), and oleic acid anhydride ((OA)2O). Likewise, the reaction between trialkylphosphine selenide and cadmium n-octadecylphosphonic acid complex (Cd-ODPA) in tri-n-octylphosphine oxide (TOPO) produces CdSe nanocrystals, trialkylphosphine oxide, and anhydrides of n-octadecylphosphonic acid. The disappearance of tri-n-octylphosphine selenide in the presence of Cd-OA and Cd-ODPA can be fit to a single-exponential decay (kobs = (1.30 +/- 0.08) x 10-3 s-1, Cd-ODPA, 260 degrees C, and kobs = (1.51 +/- 0.04) x 10-3 s-1, Cd-OA, 117 degrees C). The reaction approaches completion at 70-80% conversion of TOPSe under anhydrous conditions and 100% conversion in the presence of added water. Activation parameters for the reaction between TBPSe and Cd-OA in n-nonane-d20 were determined from the temperature dependence of the TBPSe decay over the range of 358-400 K (deltaH++ = 62.0 +/- 2.8 kJ.mol-1, deltaS++ = -145 +/- 8 J.mol-1.K-1). A reaction mechanism is proposed where trialkylphsophine chalcogenides deoxygenate the oleic acid or phosphonic acid surfactant to generate trialkylphosphine oxide and oleic or phosphonic acid anhydride products. Results from kinetics experiments suggest that cleavage of the phosphorus chalcogenide double bond (TOP=E) proceeds by the nucleophilic attack of phosphonate or oleate on a (TOP=E)-M complex, generating the initial M-E bond.
Liu
Haitao
H
Department of Chemistry, University of California, and Materials Science Division, Lawrence Berkeley National Laboratory, Berkeley, California 94720, USA.
Owen
Jonathan S
JS
Alivisatos
A Paul
AP
D003102:Colloids / Q000138:chemical synthesis* / Q000737:chemistry; D003460:Crystallization; D007700:Kinetics; D009682:Magnetic Resonance Spectroscopy / Q000379:methods / Q000592:standards; D013058:Mass Spectrometry / Q000379:methods; D019216:Metals, Heavy / Q000737:chemistry*; D049329:Nanostructures / Q000737:chemistry*; D009942:Organometallic Compounds / Q000138:chemical synthesis* / Q000737:chemistry; D012015:Reference Standards; D012666:Semiconductors; D012680:Sensitivity and Specificity; D013696:Temperature
D003102:Colloids; D019216:Metals, Heavy; D009942:Organometallic Compounds