Surface characteristics of aesthetic restorative materials - an SEM study.
To determine the degree of surface roughness of glass-ionomer cements (GICs) and polyacid-modified resin composite (PAMRC) after polishing and immersion in various foodstuffs. Three tooth-coloured restorative materials were used: a PAMRC (F2000), a conventional glass-ionomer cement (CGIC) (Fuji IX) and a resin-modified glass-ionomer cements (RM-GIC) (Fuji II LC). Disk-shaped specimens were prepared and tested with either a plastics matrix finish or after polishing with wet silicon carbide papers up to 2000-grit. All specimens were immersed in 37 degrees C-distilled water for 1 week, followed by three different foodstuffs (red wine, coffee or tea) for a further 2 weeks. Replicas of specimens were prepared by taking polyvinyl siloxane impressions, casting in epoxy resin, gold sputter-coating and examining using a Field-Emission Scanning Electron Microscope. The polished and matrix finish specimens of F2000 showed many microcracks at low magnification, and eroded surfaces with missing and protruding particles at high magnification in the polished specimens. The surface-polished specimens of Fuji II LC were considerably rougher than the matrix-finish specimens, with large voids and protruding filler particles. The effects of foodstuffs on Fuji II LC and F2000 were not noticeable. The CGIC became noticeably rougher after exposure to coffee and tea. All specimens had the smoothest surface when they were cured against a plastics matrix strip, and all materials had a rougher surface after polishing. None of the foodstuffs produced a perceptible increase in roughness on RM-GIC and PAMRC surfaces, whereas coffee and tea markedly increased the surface roughness of Fuji IX.
Bagheri
R
R
School of Dental Science, The University of Melbourne, Melbourne, Australia.
Burrow
M F
MF
Tyas
M J
MJ
D003069:Coffee; D003188:Composite Resins / Q000592:standards; D003775:Dental Polishing / Q000009:adverse effects*; D019554:Dental Restoration Wear; D003793:Dental Restoration, Permanent; D005899:Glass Ionomer Cements / Q000592:standards*; D008855:Microscopy, Electron, Scanning; D019279:Resin Cements / Q000592:standards*; D013499:Surface Properties; D013662:Tea; D014920:Wine
D003069:Coffee; D003188:Composite Resins; D005899:Glass Ionomer Cements; D019279:Resin Cements; D013662:Tea