Effect of ViscoStat and ViscoStat Plus on composite shear bond strength in the presence and absence of blood.
OBJECTIVE
To examine the effects of the hemostatic agents ViscoStat and ViscoStat Plus on the shear bond strength (SBS) of composite resin (CR) to dentin in the presence and absence of blood.


METHODS
Sixty permanent teeth mounted in acrylic were randomly divided into 5 groups (n = 12): (1) control, C; (2) ViscoStat, VS; (3) ViscoStat Plus, VS+; (4) ViscoStat and blood, VS/B; (5) ViscoStat Plus and blood, VS+/B. Groups 2 and 3 were exposed to VS and VS+, respectively. Freshly drawn human blood was placed on groups 4 and 5 immediately followed by VS and VS+, respectively. Specimens remained undisturbed for 1 min and were rinsed with tap water for 1 min. All groups were etched with 35% phosphoric acid and were bonded utilizing the Ultradent bonding clamp, Optibond Solo Plus, and Z-250 composite resin. Following water storage for 48 hrs at 37 degrees C, specimens were debonded in an Instron test frame at a crosshead speed of 0.5 mm/min. Statistical analysis was done with one-way analysis of variance.


RESULTS
The mean SBS+/-SD in MPa were C: 44.2+/-4.8, VS: 42.3+/-8.7, VS+: 46.2+/-7.8, VS/B: 43.0+/-6.4, VS+/B: 44.0+/-8.1. ANOVA revealed no significant difference (p > 0.05) between SBS of VS or VS+ and the control with or without blood present. ostatic


CONCLUSIONS
This controlled laboratory study concluded that the use of ViscoStat or ViscoStat Plus as a hem agent does not have a significant effect on the shear bond strength of composite resin to dentin when using Optibond Solo Plus.
Kimmes
Nicole S
NS
Creighton University Medical Center, School of Dentistry, 2500 California Plaza, Omaha, NE USA. nsk@creighton.edu
Olson
Travis L
TL
Shaddy
R Scott
RS
Latta
Mark A
MA
D000134:Acid Etching, Dental; D001769:Blood; D002712:Chlorides; D003188:Composite Resins / Q000737:chemistry*; D001840:Dental Bonding; D003764:Dental Materials / Q000737:chemistry*; D003799:Dental Stress Analysis / Q000295:instrumentation; D003804:Dentin / Q000648:ultrastructure*; D005290:Ferric Compounds / Q000737:chemistry*; D006490:Hemostatics / Q000737:chemistry*; D006801:Humans; D008422:Materials Testing; D010756:Phosphoric Acids / Q000737:chemistry; D019279:Resin Cements / Q000737:chemistry; D033081:Shear Strength; D013314:Stress, Mechanical; D013997:Time Factors; D014867:Water / Q000737:chemistry
D002712:Chlorides; D003188:Composite Resins; D003764:Dental Materials; D005290:Ferric Compounds; C444701:Filtek Z250; D006490:Hemostatics; C451600:OptiBond Solo Plus; D010756:Phosphoric Acids; D019279:Resin Cements; D014867:Water; C024823:ferric sulfate; C030242:phosphoric acid; C024555:ferric chloride