In vitro apatite formation on polyamide containing carboxyl groups modified with silanol groups.
Modification of organic polymer with silanol groups in combination with calcium salts enables the polymer to show bioactivity, that is, the polymer forms apatite on its surface after exposure to body environment. However, how modification with silanol groups influences ability of apatite formation on the polymer substrate and adhesive strength between polymer and apatite is not yet known. In the present study, polyamide containing carboxyl groups was modified with different amounts of silanol groups, and its apatite-forming ability in 1.5SBF, which contained ion concentrations 1.5 times those of simulated body fluid (SBF), was examined. The rate of apatite formation increased with increasing content of silanol groups in the polyamide films. This may be attributed to enhancement of dipole interactions. A tendency for the adhesive strength of the apatite layer on the polyamide film to be decreased with increasing content of silanol groups was observed. This may be attributed to swelling in 1.5SBF and having a high degree of shrinkage after drying. These findings clearly show that modification of organic polymers with the functional groups induces apatite deposition, and also determines the adhesive strength of the apatite layer to the organic substrates.
Kawai
Takahiro
T
Graduate School of Materials Science, Nara Institute of Science and Technology, 8916-5 Takayama, Ikoma, Nara 630-0192, Japan.
Ohtsuki
Chikara
C
Kamitakahara
Masanobu
M
Hosoya
Kayo
K
Tanihara
Masao
M
Miyazaki
Toshiki
T
Sakaguchi
Yoshimitsu
Y
Konagaya
Shigeji
S
D001031:Apatites / Q000737:chemistry*; D018786:Bone Substitutes / Q000737:chemistry; D002118:Calcium / Q000737:chemistry; D015394:Molecular Structure; D009757:Nylons / Q000737:chemistry*; D012821:Silanes / Q000737:chemistry*; D013499:Surface Properties; D014961:X-Ray Diffraction
D001031:Apatites; D018786:Bone Substitutes; D009757:Nylons; D012821:Silanes; C082343:silanol; D002118:Calcium