Gold nanoparticle multilayer films based on surfactant films as a template: preparation, characterization, and application.
Highly ordered gold nanoparticle multilayer films were achieved conveniently using didodecyldimethylammonium bromide (DDAB) films as a template. The template was produced by casting DDAB chloroform solution onto the surface of a (3-aminopropyl)trimethoxysilane-modified indium tin oxide substrate and then evaporating the organic solvent. Gold nanoparticle multilayer films were prepared by soaking the template in 2.6 nm colloidal gold solution for 120 min. The well-ordered superlattice structure of the DDAB template and the gold nanoparticle multilayer films was identified by x-ray diffraction. The characterizations of the gold nanoparticle multilayer films by UV-vis spectroscopy, atomic force microscopy, and cyclic voltammerty were described in detail. The application of the as-prepared gold nanoparticle multilayer films in surface-enhanced Raman spectroscopy (SERS) was investigated by using Rhodamine 6G as a probe molecule. It was found that the colloidal gold nanoparticle multilayer films exhibit remarkable enhancement ability and can be used as SERS substrates.
Li
Yancai
Y
College of Chemistry, Jilin University, Changchun 130012, People's Republic of China.
Zhou
Ji
J
Zhang
Kai
K
Sun
Changqing
C