Site selective micro-patterned rutile TiO2 film through a seed layer deposition.
Micro-patterned films obtained from micro-contact printing (microCP) method are often challenged by site selectivity limitation. For applications site-selectivity requires improvements. In this paper a site-selective deposition of the rutile TiO2 thin films on patterned SnO2 film, which was formed on the patterned octadecyltrichlorosilane (OTS) SAMs through microCP is described. The depositions proceeded in an environmentally friendly aqueous solution (SnCl4 and peroxotitanium acidic solution) at a lower temperature (80 degrees C). It is shown that the OTS SAMs has a good selectivity deposition for SnO2 particles, which was mainly dominated by the heterogeneous nucleation mechanism. The SnO2 layer had a structure-directing effect for growth of the rutile TiO2, which was usually formed above 600 degrees C. The patterned films were characterized by a variety of techniques, including ellipsometry, optical microscopy, SEM, AFM, XPS, and DLS to determine the thicknesses, topologies, microstructures, chemical compositions of the films, particle sizes and zeta potentials of the titanium particles.
Liang
Shan
S
State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000, PR China.
Chen
Miao
M
Xue
Qunji
Q
Qi
Youli
Y
Chen
Jianmin
J