[Comparative study of bond strength between zirconia ceramics and 4 luting cements].
OBJECTIVE
To study the bonding strength of zirconia ceramics with 4 kinds of luting cement materials.


METHODS
Blocks of sintered zirconia ceramics were cut and randomly divided into 4 groups with 16 slices in each group. They were treated with sandblasting and bonded with 4 kinds of luting cements respectively. After preserved in 37 degrees C distilled-water for 24 hours and 30 days, the shear bonding strength of these specimens was tested and the data were analyzed by SAS6.12 software package and bond section were observed by scanning electron microscope.


RESULTS
Two-way ANOVA revealed that the group of PanaviaF could attain the highest shear bonding strength: (34.7+/-3.44) MPa (after 24 hours), (31.5+/-3.44) MPa (after 1 month), which was significantly different from other treatment methods (P<0.01). The initial shear bonding strength of the groups of resin-reinforced glass ionomer was (15.5+/-2.71) MPa, (16.0+/-1.77) MPa (after 24 hours) but dropped markedly to (6.80+/-1.24) MPa, (3.38+/-2.32) MPa after 30 days (P<0.05).


CONCLUSIONS
Resin luting cement containing phosphate monomer (MDP) can provide zirconia ceramics a strong and long-lasting bonding. Resin-reinforced glass ionomer can get good bonding strength too, but can't last long.
Zheng
Hu
H
Department of Prosthodontics, Xuhui District Dahua Hospital, Shanghai 200237, China. woodstigero@sohu.com
Zhang
Xian-Fang
XF
Han
Dong-Wei
DW
D002516:Ceramics / Q000737:chemistry*; D001840:Dental Bonding; D003738:Dental Cements / Q000737:chemistry*; D005899:Glass Ionomer Cements; D008422:Materials Testing; D019279:Resin Cements; D033081:Shear Strength; D013499:Surface Properties; D015040:Zirconium / Q000737:chemistry*
D003738:Dental Cements; D005899:Glass Ionomer Cements; D019279:Resin Cements; D015040:Zirconium; C028541:zirconium oxide