Glass nanopore-based ion-selective electrodes.
Glass nanopore-based all-solid-state ion-selective electrodes (ISEs) have been developed to probe the distribution of ionic species at micro- or submicrometer-length scales, e.g., mapping of ion flux through micrometer-sized pores. The all-solid-state ISE was fabricated by sealing a conically etched platinum wire (d = 25-microm; radius of etched tip <10 nm) into a soda lime glass capillary. A Pt disk was exposed by gentle polishing the glass and the disk etched to form a conical pore of submicrometer dimension (radius < approximately 500 nm; depth < approximately 30 microm). Ag was electroplated on the Pt electrode in the pore and gently chloridated to obtain a AgCl/Ag layer within the pore. The AgCl/Ag layer-coated ISE was used as a highly selective Cl- probe in scanning electrochemical microscope experiments to map the ion flux through a micropore. The same ISE was also used as the base transducer of the neutral carrier-doped solvent polymeric membrane. The optimized polymer membranes used for the glass nanopore-based all-solid-state ISE require a higher ratio of plasticizer/polymer (9/1) compared to those for conventional ISE (2/1). An ISE based on deposition of an IrO2 layer at the base of a glass nanopore electrode exhibited a highly sensitive response (79.7 +/- 2.3 mV/pH) to variations in pH and could be used for approximately 3 weeks.
Shim
Jun Ho
JH
Chemical Sensor Research Group, Department of Chemistry, Kwangwoon University, Seoul 139-701, Republic of Korea.
Kim
Juneho
J
Cha
Geun Sig
GS
Nam
Hakhyun
H
White
Ryan J
RJ
White
Henry S
HS
Brown
Richard B
RB