Enamel bonding of self-etch and phosphoric acid-etch orthodontic adhesive systems.
This study was conducted to examine the shear bond strengths of orthodontic brackets to ground enamel with two self-etching adhesives (Beauty Ortho Bond and Transbond XT) and two phosphoric acid-etching adhesives (Kurasper F and Orthomite Superbond). After the bonded specimens were stored in water at 37 degreees C for 24 hours, they were subjected to thermal cycling (TC) at 0 and 5000 cycles. Then, shear bond test was performed at a crosshead speed of 1 mm/min. Results indicated that the self-etching adhesives did not significantly differ in bond strength before and after TC (p>0.05), while the phosphoric acid-etching adhesives showed a significant reduction after TC (p<0.05). The predominant modes of bracket failure for the self-etching adhesives were at the enamel-resin interface, leaving less than 50% of the adhesive on the enamel surface. It was concluded that the self-etching adhesives exhibited stable bond strength to ground enamel without causing decalcification nor damage to the enamel surface.
Kitayama
Shuzo
S
Cariology and Operative Dentistry, Department of Restorative Science, Graduate School, Tokyo Medical and Dental University, 1-5-45, Yushima, Bunkyo-ku, Tokyo 113-8549, Japan. nuevo_centro@yahoo.co.jp
Nikaido
Toru
T
Ikeda
Masaomi
M
Foxton
Richard M
RM
Tagami
Junji
J
D000134:Acid Etching, Dental / Q000379:methods; D000704:Analysis of Variance; D000818:Animals; D002417:Cattle; D001840:Dental Bonding; D003743:Dental Enamel; D003799:Dental Stress Analysis; D019544:Equipment Failure Analysis; D008855:Microscopy, Electron, Scanning; D016910:Orthodontic Brackets; D010756:Phosphoric Acids; D019279:Resin Cements; D033081:Shear Strength; D018709:Statistics, Nonparametric
C519484:Beauty Ortho Bond; D010756:Phosphoric Acids; D019279:Resin Cements; C477790:Transbond XT; C030242:phosphoric acid