Characterization of pyramidal inversion boundaries in Sb2O3-doped ZnO by using electron back-scattered diffraction (EBSD).
The composition planes of the inversion boundary induced by the addition of Sb2O3 to ZnO ceramics were analyzed crystallographically by the application of electron back-scattered diffraction (EBSD) analysis and stereographic projection techniques. The inversion boundary was determined to consist of three discrete composition planes, {0001}, {1011}, {1010}.