Nanolubrication: patterned lubricating films using ultraviolet (UV) irradiation on hard disks.
Nanolubrication is emerging to be the key technical barrier in many devices. One of the key attributes for successful device lubrication is self-sustainability using only several molecular layers. For single molecular species lubrication, one desires bonding strength and molecular mobility to repair the contact by diffusing back to the contact. One way to achieve this is the use of mask to shield the surface with a patterned surface texture, put a monolayer on the surface and induce bonding. Then re-deposit mobile molecules on the surface to bring the thickness back to the desired thickness. This paper describes the use of long wavelength UV irradiation (320-390 nm) to induce bonding of a perfluoropolyether (PFPE) on CN(x) disks for magnetic hard disk application. This allows the use of irradiation to control the degree of bonding on CN(x) coatings. The effect of induced bonding based on this wavelength was studied by comparing 100% mobile PFPE, 100% bonded PFPE, and a mixture of mobile and bonded PFPE in a series of laboratory tests. Using a lateral force microscope, a diamond-tipped atomic force microscope, and a ball-on-inclined plane apparatus, the friction and wear characteristics of these three cases were obtained. Results suggested that the mixed PFPE has the highest shear rupture strength.
Zhang
J
J
Data Storage Institute, 5 Engineering Drive 1, SG 117608, Singapore.
Hsu
S M
SM
Liew
Y F
YF
D004867:Equipment Design; D004987:Ethers / Q000737:chemistry*; D005466:Fluorocarbons / Q000737:chemistry*; D016247:Information Storage and Retrieval; D008280:Magnetics; D018625:Microscopy, Atomic Force; D008956:Models, Chemical; D053758:Nanoparticles / Q000737:chemistry; D036103:Nanotechnology / Q000379:methods*; D017550:Spectroscopy, Fourier Transform Infrared; D013314:Stress, Mechanical; D013499:Surface Properties; D013718:Tensile Strength; D014466:Ultraviolet Rays
D004987:Ethers; D005466:Fluorocarbons; C078113:perfluoropolyether