Production and characterization of glazed tiles containing incinerated sewage sludge.
In this article, glaze with different colorants was applied to tile specimens manufactured by incinerated sewage sludge ash (ISSA) and clay. Improvements using different amounts of colorants, and glaze components and concentrations on tile bodies were investigated. Four different proportions of clay (by weight ratio) were replaced by ISSA. Tiles of size 12 cm x 6 cm x 1 cm were made and left in an electric furnace to make biscuit tiles at 800 degrees C. Afterwards, four colorants, Fe2O3 (red), V2O5 (yellow), CoCO3 (blue), and MnO2 (purple), and four different glaze concentrations were applied on biscuit tile specimens. These specimens were later sintered into glazed tiles at 1050 degrees C. The study shows that replacement of clay by sludge ash had adverse effects on properties of tiles. Water absorption increased and bending strength reduced with increased amounts of ash. However, both water absorption and bending strength improved for glazed ash tiles. Abrasion of grazed tiles reduced noticeably from 0.001 to 0.002 g. This implies glaze can enhance abrasion resistance of tiles. Effects like lightfastness and acid-alkali resistance improved as different glazes were applied on tiles. In general, red glazed tiles showed the most stable performance, followed by blue, yellow, and purple.
Lin
D F
DF
Department of Civil and Ecological Engineering, I-Shou University, 1, Section 1, Hsueh-Cheng Road, Ta-Hsu Hsiang, Kaohsiung County 84008, Taiwan, ROC. dflin@isu.edu.tw
Chang
W C
WC
Yuan
C
C
Luo
H L
HL
D000538:Aluminum Silicates; D000077215:Clay; D003247:Conservation of Natural Resources / Q000379:methods; D003252:Construction Materials / Q000032:analysis*; D017745:Incineration; D007221:Industry; D012722:Sewage / Q000737:chemistry*; D013672:Technology
D000538:Aluminum Silicates; D012722:Sewage; D000077215:Clay