Development of a 95/5 poly(L-lactide-co-glycolide)/hydroxylapatite and beta-tricalcium phosphate scaffold as bone replacement material via selective laser sintering.
95/5 Poly(L-lactide-co-glycolide) was investigated for the role of a porous scaffold, using the selective laser sintering (SLS) fabrication process, with powder sizes of 50-125 and 125-250 microm. SLS parameters of laser power, laser scan speed, and part bed temperature were altered and the degree of sintering was assessed by scanning electron microscope. Composites of the 125-250 microm polymer with either hydroxylapatite or hydroxylapatite/beta-tricalcium phosphate (CAMCERAM II were sintered, and SLS settings using 40 wt % CAMCERAM II were optimized for further tests. Polymer thermal degradation during processing led to a reduction in number and weight averaged molecular weight of 9% and 12%, respectively. Compression tests using the optimized composite sintering parameters gave a Young's modulus, yield strength, and strain at 1% strain offset of 0.13 +/- 0.03 GPa, 12.06 +/- 2.53 MPa, and 11.39 +/- 2.60%, respectively. Porosity was found to be 46.5 +/- 1.39%. CT data was used to create an SLS model of a human fourth middle phalanx and a block with designed porosity was fabricated to illustrate the process capabilities. The results have shown that this composite and fabrication method has potential in the fabrication of porous scaffolds for bone tissue engineering.
Simpson
Rebecca Louise
RL
Department of Mechanical Engineering, Imperial College London, South Kensington Campus, London, SW7 2AZ, UK.
Wiria
Florencia Edith
FE
Amis
Andrew A
AA
Chua
Chee Kai
CK
Leong
Kah Fai
KF
Hansen
Ulrich N
UN
Chandrasekaran
Margam
M
Lee
Mun Wai
MW
D001672:Biocompatible Materials / Q000737:chemistry*; D018786:Bone Substitutes / Q000737:chemistry*; D002130:Calcium Phosphates / Q000737:chemistry*; D017886:Durapatite / Q000737:chemistry*; D019344:Lactic Acid / Q000737:chemistry*; D007834:Lasers; D008953:Models, Anatomic; D008970:Molecular Weight; D011100:Polyglycolic Acid / Q000737:chemistry*; D000077182:Polylactic Acid-Polyglycolic Acid Copolymer; D011108:Polymers / Q000737:chemistry*; D016062:Porosity; D015203:Reproducibility of Results; D054457:Tissue Scaffolds
D001672:Biocompatible Materials; D018786:Bone Substitutes; D002130:Calcium Phosphates; D011108:Polymers; C485817:beta-tricalcium phosphate; D000077182:Polylactic Acid-Polyglycolic Acid Copolymer; D011100:Polyglycolic Acid; D019344:Lactic Acid; D017886:Durapatite