Low-temperature adsorption/storage of hydrogen on FAU, MFI, and MOR zeolites with various Si/Al ratios: effect of electrostatic fields and pore structures.
Several zeolites, such as faujasite, mordenite, and ZSM-5, with various aluminum contents have been used to analyze the effect of aluminum or cation concentration (strength of electrostatic field) on hydrogen adsorption at low temperature. Irrespective of the zeolite structure, the adsorption capacity, isosteric heat of adsorption (-DeltaHads), surface coverage, and micropore occupancy increase with increasing aluminum content of a zeolite. Zeolites with a higher amount of aluminum favorably adsorb hydrogen at relatively low pressures. For zeolites with similar aluminum contents, the adsorption capacity, isosteric heat of adsorption, surface coverage, and micropore occupancy are in the order of mordenite>ZSM-5>faujasite, probably due to differing pore sizes and the presence or absence of pore intersections. This work demonstrates that zeolites with strong electrostatic fields and narrow pores without intersections are beneficial for high hydrogen uptake.
Jhung
Sung Hwa
SH
Research Center for Nanocatalysts, Korea Research Institute of Chemical Technology (KRICT), P.O. Box, 107, Yusung, Daejeon 305-600, Korea. sung@krict.re.kr
Yoon
Ji Woong
JW
Lee
Ji Sun
JS
Chang
Jong-San
JS