Reinforcing effect of glass-fiber-reinforced composite on flexural strength at the proportional limit of denture base resin.
OBJECTIVE
To evaluate the reinforcing effect of fiber-reinforced composite (FRC) on flexural strengths at the proportional limit (FS-PL) of a denture base resin.


METHODS
Bar-shaped acrylic resin specimens and maxillary acrylic resin complete denture specimens were fabricated. The FS-PL of the reinforced bar-shaped specimens was tested. Novel FRC, FibreKor, Remanium, Palatal Bar Wire, and Clasp-Wire were used as reinforcing materials. Likewise, the compressive strength at the proportional limit (CS-PL) of the reinforced maxillary denture specimens was tested.


RESULTS
The FS-PL of the bar-shaped specimens reinforced with the FRCs was significantly higher than that of the unreinforced specimens. The FS-PL of the bar-shaped specimens reinforced with the 1.0-mm-thick FRC was similar to the FS-PL of specimens reinforced with Remanium or Palatal Bar Wire. The FS-PL of specimens reinforced with the 1.5-mm-thick FRC was significantly higher than with the metal-reinforcing materials. The reinforcing efficiency of the 1.0-mm-thick FRC was 1.78-1.79 and of the 1.5-mm-thick FRC 3.14-3.27. The reinforcing effect of the FRC on the CS-PL of the maxillary denture specimen was similar to the effect on the FS-PL of the bar-shaped specimens. The reinforcing efficiency was 1.40 for the 1.0-mm-thick FRC and 1.67 for the 1.5-mm-thick FRC.


CONCLUSIONS
The unidirectional glass-fiber-reinforced composite had a reinforcing effect on the flexural strength at the proportional limit of the denture base resin.
Tsue
Fumitake
F
Division of Removable Prosthodontics, Fukuoka Dental College, Fukuoka, Japan.
Takahashi
Yutaka
Y
Shimizu
Hiroshi
H
D000180:Acrylic Resins / Q000737:chemistry*; D000704:Analysis of Variance; D019245:Compressive Strength; D003799:Dental Stress Analysis; D003819:Denture Bases; D003779:Denture Design; D003824:Denture, Complete; D005898:Glass; D008422:Materials Testing; D018583:Pliability; D013314:Stress, Mechanical
D000180:Acrylic Resins; C009753:fiberglass