A sol-gel-modified poly(methyl methacrylate) electrophoresis microchip with a hydrophilic channel wall.
A sol-gel method was employed to fabricate a poly(methyl methacrylate) (PMMA) electrophoresis microchip that contains a hydrophilic channel wall. To fabricate such a device, tetraethoxysilane (TEOS) was injected into the PMMA channel and was allowed to diffuse into the surface layer for 24 h. After removing the excess TEOS, the channel was filled with an acidic solution for 3 h. Subsequently, the channel was flushed with water and was pretreated in an oven to obtain a sol-gel-modified PMMA microchip. The water contact angle for the sol-gel-modified PMMA was approximately 27.4 degrees compared with approximately 66.3 degrees for the pure PMMA. In addition, the electro-osmotic flow increased from 2.13x10(-4) cm2 V(-1) s(-1) for the native-PMMA channel to 4.86x10(-4) cm2 V(-1) s(-1) for the modified one. The analytical performance of the sol-gel-modified PMMA microchip was demonstrated for the electrophoretic separation of several purines, coupled with amperometric detection. The separation efficiency of uric acid increased to 74,882.3 m(-1) compared with 14,730.5 m(-1) for native-PMMA microchips. The result of this simple modification is a significant improvement in the performance of PMMA for microchip electrophoresis and microfluidic applications.
Chen
Gang
G
Department of Pharmaceutical Analysis, School of Pharmacy, Fudan University, Shanghai 200032, P.R. China. gangchen@fudan.edu.cn
Xu
Xuejiao
X
Lin
Yuehe
Y
Wang
Joseph
J
D046209:Electrophoresis, Microchip / Q000295:instrumentation / Q000379:methods*; D018625:Microscopy, Atomic Force; D019904:Polymethyl Methacrylate / Q000737:chemistry*; D012821:Silanes / Q000737:chemistry; D017550:Spectroscopy, Fourier Transform Infrared
D012821:Silanes; C040733:tetraethoxysilane; D019904:Polymethyl Methacrylate