The marginal fit of porcelain veneers on titanium copings: an in vitro study.
OBJECTIVE
To compare the cervical microleakage of titanium copings veneered with 3 porcelain-based materials with that of titanium copings veneered with 2 indirect polymeric materials.


METHODS
Commercially pure, grade 2 titanium was veneered with 3 porcelain systems specially designed for fusing on titanium: Ti22 (Noritake), Triceram (Esprident), and Vitatitankeramik (Vita). Additionally, 2 polymeric materials were used for veneering titanium: Chromasit and Targis (Ivoclar). Four veneer crowns for each titanium-veneer combination were obtained. After storing the specimens in basic fuchsin, the microleakage between titanium and veneer in the cervical area was assessed by measuring the extent of dye penetration within the interface. ANOVA and post hoc statistics were used to analyze the data.


RESULTS
Chromasit exhibited the highest mean microleakage score (3 +/- 0.816). The least mean microleakage at the interface was recorded for Ti22 porcelain (0 +/- 0.0), followed by Triceram (0.25 +/- 0.50), Vitatitankeramik (0.75 +/- 0.957), and Targis (1.5 +/- 1.732). Only the differences between each porcelain system and Chromasit were significant (P <.05).


CONCLUSIONS
Within the limitations of this in vitro study, there was no significant microleakage between titanium copings and the porcelain veneers, regardless of the porcelain system. The microleakage between titanium and the polymeric materials depended on the veneering material. Leakage was significantly higher when Chromasit was used.
Lakatos
Sorin
S
Department of Prostheses Technology and Dental Materials, University School of Dentistry, Timişoara, Romania. sorin26@rdslink.ro <sorin26@rdslink.ro>
Romînu
Mihai
M
Floriţa
Zeno
Z
Laneş
Camil
C
Negruţiu
Meda
M
D003763:Dental Leakage; D018772:Dental Marginal Adaptation; D003764:Dental Materials / Q000737:chemistry*; D003776:Dental Porcelain / Q000737:chemistry*; D005899:Glass Ionomer Cements / Q000737:chemistry; D008689:Methacrylates / Q000737:chemistry; D012823:Silicate Cement / Q000737:chemistry; D014025:Titanium / Q000737:chemistry; D014520:Urethane / Q000737:chemistry
D003764:Dental Materials; D005899:Glass Ionomer Cements; D008689:Methacrylates; C113531:chromasit; C111282:dental polyglass; D003776:Dental Porcelain; D012823:Silicate Cement; D014520:Urethane; D014025:Titanium