Effect of different surfaces and surface applications on bonding strength of porcelain repair material.
This study was done to analyze the effect of different surfaces and different surface applications on the bonding strength of porcelain repair material and to compare these factors with one another. Three different substructures of 10 mm diameter and 4 mm thickness were used for the repair surface: metal, metal on porcelain and porcelain. The surfaces of half of the samples were roughened with an air abrasion tool; the surfaces of the other half were treated with a diamond bur. The specimens were ultrasonically cleaned in distilled water. A silane coupling agent and a bonding agent were applied to the surfaces of all the samples. Resin composite was applied to each specimen. All specimens were stored in distilled water for 24 hours before being thermocycled. After thermocycling, specimens were stored in distilled water for an additional seven days before being subjected to a shear load. The highest bonding strength was observed in the samples with a metal substructure, the surfaces of which were prepared with an air abrasion tool; the lowest bonding strength was observed in the samples with a metal substructure, the surfaces of which were prepared with a diamond bur. When different substructures were examined in terms of bonding strength, the highest bonding strength was statistically observed in metal-on-porcelain substructures, and the lowest bonding strength was observed in the porcelain substructure. When they were examined in terms of surface processes, the highest bonding strength was statistically observed in the samples whose surfaces were prepared with an air abrasion tool, and the lowest bonding strength was observed in the samples whose surfaces were prepared with a diamond bur.
Yesil
Zeynep Duymus
ZD
Department of Prosthodontics, Faculty of Dentistry, Atatürk University, Erzurum, Turkey.
Karaoglanoglu
Serpil
S
Akgül
Nilgün
N
Ozdabak
Nur
N
Ilday
Nurcan Ozakar
NO
D020906:Air Abrasion, Dental; D000704:Analysis of Variance; D002858:Chromium Alloys; D001840:Dental Bonding; D003776:Dental Porcelain; D017269:Dental Prosthesis Repair; D003799:Dental Stress Analysis; D008422:Materials Testing; D016876:Metal Ceramic Alloys; D019279:Resin Cements; D033081:Shear Strength; D012821:Silanes; D013499:Surface Properties
D002858:Chromium Alloys; C438313:Clearfil SE Bond; D016876:Metal Ceramic Alloys; D019279:Resin Cements; D012821:Silanes; D003776:Dental Porcelain