Tubular membrane cathodes for scalable power generation in microbial fuel cells.
One of the greatest challenges for using microbial fuel cells (MFCs) for wastewater treatment is creating a scalable architecture that provides large surface areas for oxygen reduction at the cathode and bacteria growth on the anode. We demonstrate here a scalable cathode concept by showing that a tubular ultrafiltration membrane with a conductive graphite coating and a nonprecious metal catalyst (CoTMPP) can be used to produce power in an MFC. Using a carbon paper anode (surface area Aan = 7 cm2, surface area per reactor volume Aan,s = 25 m2/m3), an MFC with two 3-cm tube cathodes (Acat = 27 cm2, Acat,s = 84 m2/m3) generated up to 8.8 W/m3 (403 mW/m2) using glucose [0.8 g/L in a 50 mM phosphate buffer solution (PBS)], which was only slightly less than that produced using a carbon paper cathode with a Pt catalyst (9.9 W/m3, 394 mW/m2; Acat= 7 cm2, Acat,s= 25 m2/m3). Coulombic efficiencies (CEs) with carbon paper anodes were 25-40% with tube cathodes (CoTMPP), compared to 7-19% with a carbon paper cathode. When a high-surface-area graphite brush anode was used (Aan = 2235 cm2, Aan,s = 7700 m2/m3) with two tube cathodes placed inside the reactor (Acat = 27 cm2, Acas, = 93 m2/m3), the MFC produced 17.7 W/m3 with a CE = 70-74% (200 mM PBS). Further increases in the surface area of the tube cathodes to 54 cm2 (120 m2/m3) increased the total power output (from 0.51 to 0.83 mW), but the increase in volume resulted in a constant volumetric power density (approximately 18 W/m3). These results demonstrate that an MFC design using tubular cathodes coated with nonprecious metal catalysts, and brush anodes, is a promising architecture that is intrinsically scalable for creating larger systems. Further increases in power output will be possible through the development of cathodes with lower internal resistances.
Zuo
Yi
Y
Department of Civil and Environmental Engineering, The Pennsylvania State University, University Park, Pennsylvania 16802, USA.
Cheng
Shaoan
S
Call
Doug
D
Logan
Bruce E
BE
D001674:Bioelectric Energy Sources; D002244:Carbon / Q000737:chemistry; D002384:Catalysis; D003035:Cobalt / Q000737:chemistry; D004560:Electricity; D004566:Electrodes; D011091:Polyesters / Q000737:chemistry; D011108:Polymers / Q000737:chemistry; D011166:Porphyrins / Q000737:chemistry; D013450:Sulfones / Q000737:chemistry
D011091:Polyesters; D011108:Polymers; D011166:Porphyrins; D013450:Sulfones; C017662:polysulfone P 1700; D003035:Cobalt; D002244:Carbon