Polymerization shrinkage of experimental short glass fiber-reinforced composite with semi-inter penetrating polymer network matrix.
OBJECTIVE
The aim of this study was to determine the magnitude of short fiber-reinforced composite resin, with a semi-IPN-polymer matrix, on polymerization resin shrinkage-strain, shrinkage stress and marginal microleakage of the restoration.


METHODS
Experimental composite FC resin was prepared by mixing 22.5 wt.% of short E-glass fibers, 22.5 wt.% of IPN-resin and 55 wt.% of silane treated silica fillers using a high speed mixing machine. As control material, commercial particulate filler composite resin (PFC) was used. Polymerization shrinkage-strain and stress of the specimens (n=5) were measured using the bonded-disc technique and tensilometer, respectively with respect to time. FC composite and PFC were placed incrementally in class II cavities sized 4 mm x 4 mm x 6 mm (n=8/group) using total-etch adhesive system according to manufacturer's instructions. After the class II restorations were completed, the specimens were finished and polished, thermocycled, stained, sectioned, and viewed under a stereo-microscope for leakage at occlusal/enamel and gingival/dentin margins. The data were analyzed using ANOVA.


RESULTS
ANOVA revealed that restorations made from experimental FC composite had a significantly lower shrinkage stress and microleakage than those made from PFC (p<0.05). The data show that gingival margins had higher microleakage than that obtained from occlusal margins of restorations (p<0.05).


CONCLUSIONS
The use of short fiber filler with semi-IPN polymer matrix reduced polymerization shrinkage stress and microleakage compared to a conventional restorative composite.
Garoushi
Sufyan
S
Department of Prosthetic Dentistry & Biomaterials Science, Institute of Dentistry, University of Turku, Turku, Finland. sufgar@utu.fi
Vallittu
Pekka K
PK
Watts
David C
DC
Lassila
Lippo V J
LV
D017438:Bisphenol A-Glycidyl Methacrylate / Q000737:chemistry; D003188:Composite Resins / Q000737:chemistry*; D001840:Dental Bonding; D003737:Dental Cavity Preparation / Q000145:classification; D003743:Dental Enamel / Q000648:ultrastructure; D003763:Dental Leakage / Q000145:classification; D003764:Dental Materials / Q000737:chemistry*; D003775:Dental Polishing; D003793:Dental Restoration, Permanent / Q000145:classification; D003804:Dentin / Q000648:ultrastructure; D017220:Dentin-Bonding Agents / Q000737:chemistry; D005898:Glass / Q000737:chemistry*; D006801:Humans; D008422:Materials Testing; D011092:Polyethylene Glycols / Q000737:chemistry; D011108:Polymers / Q000737:chemistry; D011109:Polymethacrylic Acids / Q000737:chemistry; D012821:Silanes / Q000737:chemistry; D012822:Silicon Dioxide / Q000737:chemistry; D013314:Stress, Mechanical; D013499:Surface Properties; D013696:Temperature; D013718:Tensile Strength; D013997:Time Factors
D003188:Composite Resins; D003764:Dental Materials; D017220:Dentin-Bonding Agents; D011108:Polymers; D011109:Polymethacrylic Acids; D012821:Silanes; C496140:everStick; C009753:fiberglass; C020946:triethylene glycol dimethacrylate; D011092:Polyethylene Glycols; D017438:Bisphenol A-Glycidyl Methacrylate; D012822:Silicon Dioxide