Nanoscale characterisation and imaging of partially amorphous materials using local thermomechanical analysis and heated tip AFM.
OBJECTIVE
The purpose is to investigate the use of thermal nanoprobes in thermomechanical and heated tip pulsed force modes as novel means of discriminating between amorphous and crystalline material on a sub-micron scale.


METHODS
Indometacin powder was compressed and partially converted into amorphous material. Thermal nanoprobes were used to perform localised thermomechanical analysis (L-TMA) and heated tip pulsed force mode imaging as a function of temperature.


RESULTS
L-TMA with submicron lateral spatial resolution and sub-100 nm depth penetration was achieved, allowing us to thermomechanically discriminate between amorphous and crystalline material at a nanoscale for the first time. The amorphous and crystalline regions were imaged as a function of temperature using heated tip pulsed force AFM and a resolution of circa 50 nm was achieved. We are also able to observe tip-induced recrystallisation of the amorphous material.


CONCLUSIONS
The study demonstrates that we are able to discriminate and characterise amorphous and crystalline regions at a submicron scale of scrutiny. We have demonstrated the utility of two methods, L-TMA and heated tip pulsed force mode AFM, that allow us to respectively characterise and image adjacent amorphous and crystalline regions at a nanoscale.


CONCLUSIONS
The study has demonstrated that thermal nanoprobes represent a novel method of characterising and imaging partially amorphous materials.
Harding
Ljiljana
L
School of Chemical Sciences and Pharmacy, University of East Anglia, Norwich, Norfolk, NR4 7TJ, UK.
King
William P
WP
Dai
Xuan
X
Craig
Duncan Q M
DQ
Reading
Mike
M
D003460:Crystallization; D006358:Hot Temperature; D007213:Indomethacin / Q000737:chemistry*; D018625:Microscopy, Atomic Force; D036103:Nanotechnology
D007213:Indomethacin