ESR studies of poly(aniline-co-m-aminophenol) in the solid state and nonaqueous solution.
The copolymers, poly(aniline-co-m-aminophenol)s, used for the ESR studies were synthesized chemically in the solutions consisting of different concentration ratios of m-aminophenol to aniline. On the basis of the ESR measurements, the unpaired spin (polaron) densities of the copolymers were calculated to be 1.14 x 10(19) spins per gram for copolymer-A with the conductivity of 7.02 x 10(-6) S cm-1 and 2.03 x 10(20) spins per gram for copolymer-C with the conductivity of 2.34 S cm-1. The ESR measurements of the copolymers in the solid states show that the peak-to-peak line width DeltaHpp decreases with a decreasing concentration ratio of m-aminophenol to aniline, but the g-value hardly changes. A conversion of Curie spins to Pauli spins for the copolymers is observed as the temperature changes in going from low temperature to high temperature between 136 and 356 K. The ESR studies of the copolymers in a nonaqueous solution first reveal that there are two free radicals in the copolymer, and the unpaired spins in the copolymers arise from nitrogen nuclei.
Mu
Shaolin
S
Department of Chemistry, Yangzhou University, Yangzhou, Jiangsu Province, China. slmu@yzu.edu.cn
Chen
Chong
C