Effects of sonic and ultrasonic scaling on the surface roughness of tooth-colored restorative materials for cervical lesions.
This study investigated the effects of sonic and ultrasonic scaling on the surface roughness of five commonly used tooth-colored restorative materials for Class V cavities, including a flowable resin composite (Tetric Flow), a compomer (Compoglass F), a glass ionomer (Fuji II), a resin-modified glass ionomer (Fuji II LC Imp) and a resin composite (Z100). Twenty rectangular block specimens (16 x 6 x 1.5 mm) of each material were cured against matrix strips, then stored in artificial saliva for two months before performing the periodontal instrumentation. Each specimen was divided into two experimental zones, and both scaling treatments were performed on each sample. The surface roughness (Ra) of these materials was determined before and after the different instrumentations, and differences were evaluated with the use of a profilometer. Data were statistically analyzed using repeated measures of ANOVA with Tukey's multiple comparisons and paired t-tests at a significance level of 0.05. Significant increases in surface roughness of all test materials were recorded from both scaling treatments. With the exception of Tetric Flow, ultrasonic scaling had more adverse effects on the surface roughness of all test materials compared to sonic scaling. For the test materials Z100 and Tetric Flow, resin composites showed the least surface changes in both scaling treatments, while Fuji II glass ionomer demonstrated the greatest roughness after instrumentation. More importantly, the mean surface roughness values of several materials after instrumentation were above the critical threshold roughness of 0.2 microm.
Lai
Yu-lin
YL
Department of Periodontology, Taipei Veterans General Hospital, Taiwan, Republic of China.
Lin
Yi-chun
YC
Chang
Che-shoa
CS
Lee
Shyh-yuan
SY
D000704:Analysis of Variance; D020770:Compomers; D003188:Composite Resins; D003793:Dental Restoration, Permanent / Q000379:methods*; D012534:Dental Scaling / Q000295:instrumentation* / Q000379:methods; D005899:Glass Ionomer Cements; D008422:Materials Testing; D017213:Root Caries / Q000628:therapy*; D013499:Surface Properties; D014465:Ultrasonics
D020770:Compomers; D003188:Composite Resins; D005899:Glass Ionomer Cements