Histological study of surface modified three dimensional poly (D, L-lactic acid) scaffolds with chitosan in vivo.
Biocompatibility and tissue regenerating capacity are essential for biomaterials that used in tissue engineering. The aim of this study was to histologically assess the tissue reactions and bone conductivities of surface modified three dimensional (3-D) poly (D, L-lactic acid) (PDLLA) scaffolds, which were coated with chitosan via a physical entrapment method. The native PDLLA scaffold was prepared via thermally induced phrase separation technique and was characterized by scanning electron microscopy (SEM) and differential scanning calorimetry (DSC). Osteocalcin assay, a method to evaluate the bone formation potential, has shown that the osteocalcin production in chitosan-modified 3-D PDLLA scaffold group was significantly higher (p < 0.05) than that of in control. The tissue reactions and bone conductivities between surface modified PDLLA and native PDLLA scaffolds were evaluated using a rabbit radialis defect model in vivo and compared at different implantation intervals (2, 4, 8 and 12 weeks). The histological results have shown a higher bone formation potential and better biocompatibility of chitosan-modified 3-D PDLLA scaffolds as compared with the control group scaffolds.
Cai
Kaiyong
K
College of Bioengineering, Chong Qing University, Chong Qing, 400044, PR China. Kaiyong_cai@cqu.edu.cn
Yao
Kangde
K
Yang
Zhiming
Z
Qu
Yanlong
Y
Li
Xiuqiong
X
D020341:Absorbable Implants; D000818:Animals; D001861:Bone Regeneration; D048271:Chitosan / Q000737:chemistry*; D019344:Lactic Acid / Q000737:chemistry*; D008422:Materials Testing; D016348:Osseointegration / Q000502:physiology; D015675:Osteocalcin / Q000032:analysis / Q000097:blood; D011091:Polyesters; D011108:Polymers / Q000737:chemistry*; D011817:Rabbits; D013499:Surface Properties; D013997:Time Factors; D054457:Tissue Scaffolds / Q000737:chemistry*
D011091:Polyesters; D011108:Polymers; D015675:Osteocalcin; D019344:Lactic Acid; C033616:poly(lactide); D048271:Chitosan