Single step synthesis of high-purity CoO nanocrystals.
Both octahedral and slice-shaped cubic cobalt monoxide (CoO) nanocrystals with narrow size distributions have been successfully synthesized by a simple solvothermal route. It was found that conditions of the solvothermal treatment showed obvious effects on the formation and purity of the as-synthesized CoO nanocrystals, only when cobalt acetate was used as the cobalt source and when temperature reached 190 degrees C could CoO be produced; also, freeze-drying was necessary for obtaining pure CoO. Size of the CoO nanocrystals varied from 30 to 130 nm. Morphology of the products could be controlled by simply changing the type of surfactant in solvent, and the octahedral CoO nanocrystals showed rounded turns. Purity of the products was detected by intensive X-ray photoelectron spectroscopy (XPS) investigation and Fourier transform infrared spectroscopy (FTIR) combined with differential scanning calorimetry/thermal gravity (DSC/TG). The results indicated an absence of unexpected trivalence cobalt series on surface of the samples, thanks to the protection of the surface by trace amount of carbonate ions, adsorbed hydroxylation, and surfactant with a maximum thickness of 2 nm, which were proved by high-resolution transmission electron microscopy (HRTEM). The as-synthesized CoO nanoparticles were added into positive electrode of Ni/MH batteries, and discharge/charge cycling tests were performed under different rates from 0.1C to 5.0C. The results indicated that the specific capacities of batteries with addition of 5% octahedral or slice CoO nanocrystals at 0.1C were 393.3 and 318.1 mAh/g, respectively, which were higher than that without CoO (269.2mAh/g). Specific capacity of battery with addition of 5% octahedral CoO nanocrystals was 40% higher than that without CoO at 5.0C. Octahedral CoO nanocrystals show better electrochemical activity than slice CoO and indicate interesting potential in the field of electrochemical application.
Yang
Huaming
H
Department of Inorganic Materials, School of Resources Processing and Bioengineering, Central South University, Changsha 410083, China. hmyang@mail.csu.edu.cn
Ouyang
Jing
J
Tang
Aidong
A