Alkali-silica reactions of mortars produced by using waste glass as fine aggregate and admixtures such as fly ash and Li2CO3.
Use of waste glass or glass cullet (GC) as concrete aggregate is becoming more widespread each day because of the increase in resource efficiency. Recycling of wastes is very important for sustainable development. When glass is used as aggregate in concrete or mortar, expansions and internal stresses occur due to an alkali-silica reaction (ASR). Furthermore, rapid loss in durability is generally observed due to extreme crack formation and an increase in permeability. It is necessary to use some kind of chemical or mineral admixture to reduce crack formation. In this study, mortar bars are produced by using three different colors of glass in four different quantities as fine aggregate by weight, and the effects of these glass aggregates on ASR are investigated, corresponding to ASTM C 1260. Additionally, in order to reduce the expansions of mortars, 10% and 20% fly ash (FA) as mineral admixture and 1% and 2% Li(2)CO(3) as chemical admixture are incorporated by weight in the cement and their effects on expansion are examined. It is observed that among white (WG), green (GG) and brown glass (BG) aggregates, WG aggregate causes the greatest expansion. In addition, expansion increases with an increase in amount of glass. According to the test results, it is seen that over 20% FA and 2% Li(2)CO(3) replacements are required to produce mortars which have expansion values below the 0.2% critical value when exposed to ASR. However, usages of these admixtures reduce expansions occurring because of ASR.
Topçu
Ilker Bekir
IB
Eskişehir Osmangazi University, Civil Engineering Department, 26480 Eskişehir, Turkey. ilkerbt@ogu.edu.tr
Boğa
Ahmet Raif
AR
Bilir
Turhan
T
D000468:Alkalies / Q000737:chemistry*; D002244:Carbon / Q000737:chemistry*; D060729:Coal Ash; D003247:Conservation of Natural Resources; D003252:Construction Materials / Q000032:analysis*; D005898:Glass; D016651:Lithium Carbonate / Q000737:chemistry*; D052638:Particulate Matter / Q000737:chemistry*; D012822:Silicon Dioxide / Q000737:chemistry*
D000468:Alkalies; D060729:Coal Ash; D052638:Particulate Matter; D016651:Lithium Carbonate; D002244:Carbon; D012822:Silicon Dioxide