Influence of alkyl chain length on phosphate self-assembled monolayers.
A series of alkyl phosphates with alkyl chain lengths ranging from C10 to C18 have been synthesized. Self-assembled monolayers (SAMs) of these molecules were prepared on titanium oxide surfaces by immersion of the substrates in alkyl phosphate solutions of 0.5 mM concentration in n-heptane/isopropanol. The SAMs were characterized by means of dynamic water contact angle (dCA) measurements, variable-angle spectroscopic ellipsometry (VASE), X-ray photoelectron spectroscopy (XPS), and polarization-modulated infrared reflection-absorption spectroscopy (PM-IRRAS). A higher degree of order and packing density within the monolayers was found for alkyl phosphates with alkyl chain lengths exceeding 15 carbon atoms. This is reflected in a lower dCA hysteresis, as well as a film thickness measured by VASE and XPS close to the expected values for SAMs with an average alkyl chain tilt angle of 30 degrees to the surface normal. Additionally a shift of the symmetric and antisymmetric C-H stretching modes in the PM-IRRAS spectra to lower wave numbers was observed. These findings imply a higher two-dimensional crystallinity of the films derived from alkyl phosphates with a longer alkyl chain length.
Spori
Doris M
DM
Laboratory for Surface Science and Technology, Department of Materials, ETH Zurich, Wolfgang-Pauli-Strasse 10, CH-8093 Zurich, Switzerland.
Venkataraman
Nagaiyanallur V
NV
Tosatti
Samuele G P
SG
Durmaz
Firat
F
Spencer
Nicholas D
ND
Zürcher
Stefan
S