Raman imaging of two orthogonal planes within cortical bone.
The lamellar bone's strength is mainly affected by the organization of its mineralized collagen fibers and material composition. In the present study, Raman microspectroscopic and imaging analyses were employed to study a normal human femoral midshaft bone cube-like specimen with a spatial resolution of approximately 1-2 microm. Identical bone lamellae in both longitudinal and transverse directions were analyzed, which allowed us to separate out orientation and composition dependent Raman lines, depending on the polarization directions. This approach gives information about lamellar bone orientation and variation in bone composition. It is shown that the nu1 PO4 to amide I ratio mainly displays lamellar bone orientation; and nu2 PO4 to amide III and CO3 to nu2 PO4 ratios display variation in bone composition. The nu2 PO4 to amide III ratio is higher in the interstitial bone region, whereas the CO3 to nu2 PO4 ratio has lower values in the same region. The present study provides fresh insights into the organization of a lamellar bone tissue from two orthogonal orientations.
Kazanci
M
M
Max Planck Institute of Colloids and Interfaces, Department of Biomaterials, 14424 Potsdam, Germany, and Ludwig Boltzmann Institute of Osteology at the Hanusch Hospital of WGKK, Vienna, Austria.
Wagner
H D
HD
Manjubala
N I
NI
Gupta
H S
HS
Paschalis
E
E
Roschger
P
P
Fratzl
P
P
D000328:Adult; D003094:Collagen / Q000648:ultrastructure; D005260:Female; D005269:Femur / Q000033:anatomy & histology*; D006253:Haversian System / Q000648:ultrastructure; D006801:Humans; D013059:Spectrum Analysis, Raman
D003094:Collagen