Effects of anodic oxidation parameters on a modified titanium surface.
Anodic oxidation is an electrochemical treatment that can be used to control the thickness of an oxide layer formed on a titanium surface. This procedure has the advantage of allowing the ions contained in an electrolyte to deposit onto the oxide layer. The characteristics of a layer treated with anodic oxidation can vary according to the type and concentration of the electrolytes as well as the processing variables used during anodic oxidation. In this study, the constant electrolyte for anodic oxidation was a mixed solution containing 0.02 M DL-alpha-glycerophosphate disodium salt and 0.2M calcium acetate. Anodic oxidation was carried out at different voltages, current densities, and duration of anodic oxidation. The results showed that the current density and variation in the duration of anodic oxidation did not have a large effect on the change in the characteristics of the layer. On the other hand, the size of the micropores was increased with increasing voltage of anodic oxidation, and anatase and rutile phases were found to co-exist in the porous titanium dioxide layer. In addition, the thickness of the oxide layer on titanium and the characteristic of corrosion resistance increased with increasing voltage. The MTT test showed that the cell viability was increased considerably as a result of anodic oxidation. The anodizing voltage is an important parameter that determines the characteristics of the anodic oxide layer of titanium.
Park
Il Song
IS
Department of Dental Biomaterials and Institute of Oral Bioscience, School of Dentistry, Chonbuk National University, Chonbuk 561-756, South Korea.
Lee
Min Ho
MH
Bae
Tae Sung
TS
Seol
Kyeong Won
KW
D020099:Coated Materials, Biocompatible / Q000737:chemistry*; D017886:Durapatite / Q000737:chemistry; D004566:Electrodes; D010084:Oxidation-Reduction; D013499:Surface Properties; D014025:Titanium / Q000737:chemistry*
D020099:Coated Materials, Biocompatible; C009495:titanium dioxide; D017886:Durapatite; D014025:Titanium