Extrusion foaming of semi-crystalline PLA and PLA/thermoplastic starch blends.
Low density open-cell foams were obtained from polylactic acid (PLA) and from blends of PLA with thermoplastic starch (TPS) using CO(2) as a blowing agent. Two unexpected features were found. First, a 2D cavitation process in the fractured cell walls was unveiled. Elliptical cavities with dimensions in the 100-300 nm range were aligned perpendicular to large cell cracks clearly exhibiting 2D crazing prior to macroscopic cell rupture. Secondly, a significant crystallization rate increase associated with the CO(2) foaming of PLA was discovered. While the PLA used in this study crystallized very slowly in isothermal crystallization, the PLA foams exhibited up to 15% crystallinity, providing evidence that CO(2) plasticization and the biaxial stretching upon foam expansion provided conditions that could increase the crystallization rate by several orders of magnitude.
Mihai
Mihaela
M
CREPEC, Chemical Engineering Department, Ecole Polytechnique de Montréal, P.O. Box 6079, Station Centre-Ville, Montréal, Québec, Canada, H3C 3A7.
Huneault
Michel A
MA
Favis
Basil D
BD
Li
Hongbo
H
D002245:Carbon Dioxide; D003460:Crystallization; D007700:Kinetics; D019344:Lactic Acid / Q000737:chemistry*; D010969:Plastics / Q000138:chemical synthesis*; D011091:Polyesters; D011108:Polymers / Q000737:chemistry*; D013213:Starch / Q000737:chemistry*; D013696:Temperature
D010969:Plastics; D011091:Polyesters; D011108:Polymers; D002245:Carbon Dioxide; D019344:Lactic Acid; C033616:poly(lactide); D013213:Starch