Structure of oxidized bismuth nanoclusters.
Synchrotron X-ray diffraction has determined that beta-Bi(2)O(3) is the dominant oxide phase covering hexagonal bismuth nanoclusters produced in an inert gas aggregation source. Simulated Debye-Scherrer patterns have indicated that the oxide is 20 +/- 5 Angstroms thick on average, at the surface of 320 +/- 40 Angstroms diameter clusters. A Williamson-Hall analysis of the peak broadening was used to measure the non-uniform strain in clusters. The oxidized clusters were in -0.11 +/- 0.06% uniform compressive strain compared with other clusters without oxides detectable by X-ray diffraction which only have a small tensile uniform strain. High-resolution transmission electron microscopy (HRTEM) and multislice image simulations indicated a beta-Bi(2)O(3) thickness of 20-50 Angstroms. The HRTEM micrographs show the relative orientation between the oxide and the cluster core.
Stevens
K J
KJ
MPT Solutions Ltd, PO Box 38-096, Lower Hutt, New Zealand. k.stevens@mptsolutions.com
Ingham
B
B
Toney
M F
MF
Brown
S A
SA
Partridge
J
J
Ayesh
A
A
Natali
F
F