Effect of air abrasion on tensile bond strength of a single-bottle adhesive/indirect composite system to enamel.
This study evaluated the efficiency of air abrasion alone and associated with phosphoric acid etching on tensile bond strength of a single-bottle adhesive/indirect composite restorative system (Bond 1/Alert) to human enamel. Forty enamel surfaces from extracted human third molars were assigned to 4 groups (n= 10). Mach 4.1 (Kreativ Inc.) air abrasion equipment was used for 20 s. A special system of rod pairs aligned in a specific apparatus was used for tensile strength tests, according to ISO/TR 11405 standard (1994) with some modifications. Bond strength means were: G1 (air abrasion + rinsing + condensable composite resin Alert) = 3.46 +/- 0.83 MPa; G2 (air abrasion + rinsing + Bond 1 adhesive system + Alert) = 4.00 +/- 1.60 MPa; G3 (air abrasion + rinsing + 37% phosphoric acid + rinsing + Bond 1 + Alert) = 20.80 +/- 3.95 MPa; and G4 (37% phosphoric acid + rinsing + Bond 1 + Alert) = 17.00 +/- 2.74 MPa. The statistical analysis by Kruskal-Wallis test revealed that G1 and G2 presented statistically significant difference (p< 0.05) from G3 and G4 (p<0.01) and G1 and G3 did not differ significantly (p> 0.05) from G2 and G4, respectively.
Silva
Paulo César G
PC
Department of Restorative Dentistry, School of Dentistry of Ribeirão Preto, University of São PauloRibeirão Preto, SP, Brazil. manakelpc@yahoo.com.br
Gonçalves
Mariane
M
Nascimento
Telma N do
TN
Centola
André Luiz B
AL
D000180:Acrylic Resins / Q000737:chemistry; D020906:Air Abrasion, Dental / Q000379:methods*; D003188:Composite Resins / Q000737:chemistry; D001840:Dental Bonding / Q000379:methods*; D003743:Dental Enamel / Q000737:chemistry; D003764:Dental Materials; D006801:Humans; D010756:Phosphoric Acids / Q000008:administration & dosage; D011140:Polyurethanes / Q000737:chemistry; D018709:Statistics, Nonparametric; D013718:Tensile Strength
D000180:Acrylic Resins; C029012:Composite Dental Resin; D003188:Composite Resins; D003764:Dental Materials; D010756:Phosphoric Acids; D011140:Polyurethanes; C030242:phosphoric acid