Facile synthesis of ZnS-AgInS2 solid solution nanoparticles for a color-adjustable luminophore.
Nanoparticles of ZnS-AgInS2 solid solution (ZAIS) were synthesized by the thermal decomposition of (AgIn)xZn2(1-x)(S2CN(C2H5)2)4 precursors in a hot oleylamine solution. X-ray powder diffraction analyses revealed that the resulting nanoparticle powders were not a mixture of ZnS and AgInS2 but a ZnS-AgInS2 solid solution in which the fraction of ZnS was enlarged with a decrease in the value of x, that is, an increase in the content of Zn2+ in the precursors used. The energy gap of ZAIS nanoparticles could be controlled by the composition of solid solution. Intense emission was observed at room temperature, regardless of the kind of the particles, the peak wavelength of PL being blue-shifted from 720 to 540 nm with a decrease in the value of x. The highest quantum yield of ca. 24% was obtained for nanoparticles prepared with x = 0.86, which was much higher than the quantum yields reported for I-III-VI2-based semiconductor nanoparticles, such as CuInS2 and ZnS-CuInS2 solid solution.
Torimoto
Tsukasa
T
Department of Crystalline Materials Science, Graduate School of Engineering, Nagoya University, Chikusa-ku, Nagoya 464-8603, Japan.
Adachi
Tomohiro
T
Okazaki
Ken-Ichi
K
Sakuraoka
Miwa
M
Shibayama
Tamaki
T
Ohtani
Bunsho
B
Kudo
Akihiko
A
Kuwabata
Susumu
S
D003116:Color; D007204:Indium / Q000737:chemistry*; D008163:Luminescent Measurements; D053768:Metal Nanoparticles / Q000737:chemistry*; D009942:Organometallic Compounds / Q000737:chemistry*; D012834:Silver / Q000737:chemistry*; D012996:Solutions; D013440:Sulfides / Q000737:chemistry*; D014961:X-Ray Diffraction; D017967:Zinc Compounds / Q000737:chemistry*
D009942:Organometallic Compounds; D012996:Solutions; D013440:Sulfides; D017967:Zinc Compounds; D007204:Indium; D012834:Silver; C031238:zinc sulfide