Apatite-forming ability of alumina and zirconia ceramics in a supersaturated Ca/P solution.
The apatite-forming ability of alumina and zirconia ceramics was investigated using a supersaturated Ca/P solution. After 2h of immersion, a thin, needle-like nanocrystalline layer with micron-sized clusters of an irregular shape was formed on the alumina and zirconia surfaces. With a longer immersion time the layer thickness increased and the clusters became more spherical. The substrate material has little or no effect on the forming ability of the coating. The XPS Ca/P ratio for the sputtered coating on the zirconia substrate that was immersed in the Ca/P solution for 27 h was 1.66. The EDS, XRD and XPS analyses confirmed that the coated layer was hydroxyapatite. The thickness of the hydroxyapatite coating on the zirconia and alumina substrates after immersion in the Ca/P solution for 8 and 27 h was from 0.8 to 1.1 microm.
Klopcic
Sabina Beranic
SB
Jozef Stefan Institute, Ljubljana, Slovenia. sabina.beranic@ijs.si
Kovac
Janez
J
Kosmac
Tomaz
T
D000537:Aluminum Oxide / Q000737:chemistry*; D002130:Calcium Phosphates / Q000737:chemistry*; D002516:Ceramics / Q000737:chemistry*; D020099:Coated Materials, Biocompatible / Q000737:chemistry*; D017886:Durapatite / Q000737:chemistry*; D008855:Microscopy, Electron, Scanning; D010316:Particle Size; D012996:Solutions / Q000737:chemistry; D013053:Spectrophotometry; D013499:Surface Properties; D014961:X-Ray Diffraction; D014965:X-Rays; D015040:Zirconium / Q000737:chemistry*
D002130:Calcium Phosphates; D020099:Coated Materials, Biocompatible; D012996:Solutions; D017886:Durapatite; D015040:Zirconium; D000537:Aluminum Oxide; C028541:zirconium oxide