Catalytic water dissociation using hyperbranched aliphatic polyester (Boltorn series) as the interface of a bipolar membrane.
The effect of hyperbranched aliphatic polyester (Boltorn series) on the water dissociation in bipolar membranes was firstly investigated in this paper. The bipolar membranes were prepared by immersing the anion exchange layer in a hyperbranched aliphatic polyester solution and then coating on the layer a polyphenylene oxide (SPPO) solution. The SEM observations proved the existence of hyperbranched aliphatic polyester at the membrane intermediate layer. The adsorption amount was evaluated by the oxygen content via XPS. The junction thickness of the prepared bipolar membrane was determined by electrochemical impedance spectroscopy (EIS), and the membrane performances were evaluated by current-voltage curves. The results showed that the amount and generation of Boltorn series, and temperature all affected I-V behaviors of the fabricated bipolar membranes, and the former two played the critical role. These effects were explained on the basis of the water dissociation theory and the characteristics of hyperbranched aliphatic polyester.
Xue
Yanhong
Y
Laboratory of Functional Membranes, School of Chemistry and Materials Science, University of Science and Technology of China, Hefei 230026, PR China.
Xu
Tongwen
T
Fu
Rongqiang
R
Cheng
Yiyun
Y
Yang
Weihua
W
D002384:Catalysis; D006860:Hydrogen Bonding; D008567:Membranes, Artificial; D008958:Models, Molecular; D015394:Molecular Structure; D010316:Particle Size; D011091:Polyesters / Q000737:chemistry*; D013499:Surface Properties; D013696:Temperature; D014867:Water / Q000737:chemistry
D008567:Membranes, Artificial; D011091:Polyesters; D014867:Water