[Polyethylene abrasion: cause or consequence of an endoprosthesis loosening? Investigations of firm and loosened hip implants].
OBJECTIVE
Periprosthetic tissue was analysed by the combination of different investigation techniques without destruction. The localisation and geometry of polyethylene abrasion particles were determined quantitatively to differentiate between abrasion due to function and abrasion due to implant loosening. Non-polyethylene particles from implant components which contaminate the tissue were micro-analytically measured. The results will help us to understand loosening mechanisms and thus lead to implant optimisations.


METHODS
A non-destructive particle analysis using highly sensitive proton-induced X-ray emission (PIXE) was developed to achieve a better histological allocation. Five autopsy cases with firmly fitting hip endoprosthesis (2 x Endo-Modell Mark III, 1 x St. Georg Mark II, LINK, Germany; 2 x Spongiosa Metal II, ESKA, Germany) were prepared as ground tissue specimens. Wear investigations were accomplished with a combined application of different microscopic techniques and microanalysis. The abrasion due to implant loosening was histologically evaluated on 293 loosened cup implants (St. Georg Mark II, LINK, Germany).


RESULTS
Wear particles are heterogeneously distributed in the soft tissue. In cases of cemented prostheses, cement particles are dominating whereas metal particles could rarely be detected. The concentration of the alloy constituent cobalt (Co) is increased in the mineralised bone tissue. The measured co-depositions depend on the localisation and/or lifetime of an implant. Functional polyethylene (PE) abrasion needs to be differentiated from PE abrasion of another genesis (loosening, impingement) morphologically and by different tissue reactions.


CONCLUSIONS
In the past a reduction of abrasion was targeted primarily by the optimisation of the bearing surfaces and tribology. The interpretation of our findings indicates that different mechanisms of origin in terms of tissue contamination with wear debris and the alloy should be included in the improvement of implants or implantation techniques.
Busse
B
B
Zentrum für Biomechanik und Skelettbiologie, Universitätsklinikum Hamburg-Eppendorf.
Niecke
M
M
Püschel
K
K
Delling
G
G
Katzer
A
A
Hahn
M
M
D002102:Cadaver; D019544:Equipment Failure Analysis; D005547:Foreign Bodies / Q000209:etiology* / Q000473:pathology*; D006622:Hip Prosthesis / Q000009:adverse effects*; D006801:Humans; D007593:Joint Instability / Q000209:etiology* / Q000473:pathology*; D008422:Materials Testing; D010316:Particle Size; D020959:Polyethylene / Q000009:adverse effects* / Q000737:chemistry; D011474:Prosthesis Design
D020959:Polyethylene