Dissolution of human teeth-derived hydroxyapatite.
We have been interested in human teeth which consist of hydroxyapatite (HA), but do not degrade for a long time. In order to overcome dissolution and mechanical degradation of man-made HA, biologically derived hydroxyapatite (BHA) ceramics were prepared from human teeth and their dissolving behavior was investigated in distilled water for 3-14 days and compared with an artificial HA made of synthetic HA powder. BHA ceramics were prepared by calcining freshly extracted human teeth at 900 degrees C and followed by sintering at 1200 degrees C for 2 h. All detectable peaks in the artificial HA are identical to HA lattice planes, whereas BHA consisted of a mixture of HA and beta-tricalcium phosphate (TCP). Although the artificial HA was expected to be stable in water, the surface dissolution initiated at grain boundaries followed by generated many separated grains and their associated pores. On the other hand, BHA showed that definite grains considered as beta-TCP were predominantly dissolved and the grains were separated from the matrix leaving pores. In the mean time, the rest region, mainly consisting of HA, did not show any evidence of dissolution. It indicates that BHA showed rather stable grain boundaries and lack of excessive dissolution in liquid environment.
Seo
Dong Seok
DS
BK21 Education Center of Mould Technology for Advanced Materials & Parts, Chosun University, 375 Seosuk-dong, Dong-gu, Gwangju, 501-759, Republic of Korea.
Lee
Jong Kook
JK
D017886:Durapatite / Q000737:chemistry*; D006801:Humans; D008422:Materials Testing; D008968:Molecular Conformation; D044367:Phase Transition; D012995:Solubility; D014070:Tooth / Q000737:chemistry*
D017886:Durapatite