Renewable-resource thermoplastic elastomers based on polylactide and polymenthide.
An alpha,omega-functionalized polymenthide was synthesized by the ring-opening polymerization of menthide in the presence of diethylene glycol with diethyl zinc as the catalyst. Termination with water afforded the dihydroxy polymenthide. The reaction of this telechelic polymer with triethylaluminum formed the corresponding aluminum alkoxide macroinitiator that was used for the controlled polymerization of lactide to yield biorenewable polylactide-b-polymenthide-b-polylactide triblock copolymers. The molecular weight and chemical composition were easily adjusted by the monomer-to-initiator ratios. Microphase separation in these triblock copolymers was confirmed by small-angle X-ray scattering and differential scanning calorimetry. A representative triblock was prepared with a hexagonally packed cylindrical morphology as determined by small-angle X-ray scattering, and tensile testing was employed to assess the mechanical behavior. On the basis of the ultimate elongations and elastic recovery, these triblock copolymers behaved as thermoplastic elastomers.
Wanamaker
Carolyn L
CL
Department of Chemistry, University of Minnesota, 207 Pleasant Street SE, Minneapolis, MN 55455-0431, USA.
O'Leary
Leslie E
LE
Lynd
Nathaniel A
NA
Hillmyer
Marc A
MA
Tolman
William B
WB
D002152:Calorimetry, Differential Scanning; D020724:Elastomers / Q000737:chemistry*; D009682:Magnetic Resonance Spectroscopy; D015394:Molecular Structure; D010969:Plastics / Q000737:chemistry*; D011091:Polyesters / Q000737:chemistry*; D013696:Temperature
D020724:Elastomers; D010969:Plastics; D011091:Polyesters; C033616:poly(lactide)