Rhodium coated mirrors deposited by magnetron sputtering for fusion applications.
Metallic mirrors will be essential components of all optical spectroscopy and imaging systems for ITER plasma diagnostics. Any change in the mirror performance, in particular, its reflectivity, due to erosion of the surface by charge exchange neutrals or deposition of impurities will influence the quality and reliability of the detected signals. Due to its high reflectivity in the visible wavelength range and its low sputtering yield, rhodium appears as an attractive material for first mirrors in ITER. However, the very high price of the raw material calls for using it in the form of a film deposited onto metallic substrates. The development of a reliable technique for the preparation of high reflectivity rhodium films is therefore of the highest importance. Rhodium layers with thicknesses of up to 2 microm were produced on different substrates of interest (Mo, stainless steel, Cu) by magnetron sputtering. Produced films exhibit a low roughness and crystallite size of about 10 nm with a dense columnar structure. No impurities were detected on the surface after deposition. Scratch tests demonstrate that adhesion properties increase with substrate hardness. Detailed optical characterizations of Rh-coated mirrors as well as results of erosion tests performed both under laboratory conditions and in the TEXTOR tokamak are presented in this paper.
Marot
L
L
Department of Physics, University of Basel, Klingelbergstrasse 82, CH-4056 Basel, Switzerland. laurent.marot@unibas.ch
De Temmerman
G
G
Oelhafen
P
P
Covarel
G
G
Litnovsky
A
A
D004867:Equipment Design; D019544:Equipment Failure Analysis; D006358:Hot Temperature; D007909:Lenses; D008280:Magnetics / Q000295:instrumentation*; D009681:Nuclear Fusion; D015203:Reproducibility of Results; D012238:Rhodium / Q000737:chemistry*; D012680:Sensitivity and Specificity
D012238:Rhodium