Microstructure and wear properties of LENS deposited medical grade CoCrMo.
There is a growing interest in metal-on-metal bearing surfaces for orthopedic implants. Although some success has been achieved in applications like hip implants which involve a large contact area, non-conforming joints, such as knees, have proved more difficult. The current work examines the applicability of a novel additive manufacturing process, Laser Engineered Net Shaping (LENS), the registered trademark and service mark of Sandia National Laboratories and Sandia Corporation), for producing CoCrMo implants. A series of experiments were conducted to determine the optimum parameters for deposition of CoCrMo. Microstructural studies, hardness tests, and dry sand/rubber wheel abrasive wear tests were conducted on the LENS deposits. The results showed that metallurgically sound deposits can be produced using the LENS process under optimized conditions. The hardness of the LENS deposited CoCrMo was found to be comparable to that of standard CoCrMo wrought material; however, wear tests indicated that LENS deposits were considerably less resistant to abrasive wear than wrought CoCrMo. The reasons for this behaviour are discussed based on microstructural observations.
Janaki Ram
G D
GD
Department of Mechanical and Aerospace Engineering, Utah State University, Logan, UT 84322-4130, USA. durgagabbita@cc.usu.edu
Esplin
C K
CK
Stucker
B E
BE
D000497:Alloys; D002857:Chromium / Q000737:chemistry*; D002858:Chromium Alloys / Q000737:chemistry; D003035:Cobalt / Q000737:chemistry*; D004867:Equipment Design; D006244:Hardness; D006245:Hardness Tests; D008422:Materials Testing; D008670:Metals / Q000737:chemistry; D008855:Microscopy, Electron, Scanning; D008982:Molybdenum / Q000737:chemistry*; D011474:Prosthesis Design; D011475:Prosthesis Failure; D013499:Surface Properties; D013718:Tensile Strength
D000497:Alloys; D002858:Chromium Alloys; D008670:Metals; D002857:Chromium; D003035:Cobalt; D008982:Molybdenum