"Schizophrenic" micellization associated with coil-to-helix transitions based on polypeptide hybrid double hydrophilic rod-coil diblock copolymer.
A polypeptide hybrid double hydrophilic diblock copolymer (DHBC), poly( N-isopropylacrylamide)- b-poly( l-glutamic acid) (PNIPAM- b-PLGA), was synthesized via the ring-opening polymerization of gamma-benzyl- l-glutamate N-carboxyanhydride (BLG-NCA) using monoamino-terminated PNIPAM as the macroinitiator, followed by deprotection of benzyl groups under alkaline conditions. Containing a thermoresponsive PNIPAM block and a pH-responsive PLGA block, the obtained polypeptide hybrid diblock copolymer molecularly dissolves in aqueous solution at alkaline pH and room temperature but supramolecularly self-assembles into PNIPAM-core micelles at alkaline pH and elevated temperatures and PLGA-core micelles at acidic pH and room temperature accompanied with coil-to-helix transition of the PLGA sequence. The pH- and thermoresponsive "schizophrenic" micellization behavior of PNIPAM- b-PLGA diblock copolymer has been investigated by (1)H NMR, optical transmittance, fluorescence probe measurement, transmission electron microscopy (TEM), dynamic and static laser light scattering (LLS), and circular dichroism (CD) spectroscopy. Moreover, the micellization process was investigated employing stopped-flow light scattering technique. The pH-induced micelle growth of PNIPAM- b-PLGA in aqueous solution exhibits drastically different kinetics compared to that of conventional pH-responsive DHBCs, probably due to the stabilization effects exerted by the formed alpha-helix secondary structures within the PLGA core at low pH. Exhibiting "schizophrenic" micellization, the polypeptide sequence of PNIPAM- b-PLGA can either locate within micelle cores or stabilizing coronas. The incorporation of polypeptide block into DHBCs can endow them with structural versatility, tunable spatial arrangement of chain segments within self-assembled nanostructures, and broader applications in the field of biomedicines.
Rao
Jingyi
J
Department of Polymer Science and Engineering, Joint Laboratory of Polymer Thin Films and Solution, Hefei National Laboratory for Physical Sciences at the Microscale, University of Science and Technology of China, Hefei, Anhui Province 230026, China.
Luo
Zhaofeng
Z
Ge
Zhishen
Z
Liu
Hao
H
Liu
Shiyong
S
D000180:Acrylic Resins / Q000737:chemistry*; D008823:Micelles; D010455:Peptides / Q000737:chemistry*; D017433:Protein Structure, Secondary
D000180:Acrylic Resins; D008823:Micelles; D010455:Peptides; C052970:poly-N-isopropylacrylamide