Study of neutral Fe(III) complexes of pyridoxal-N-substituted thiosemicarbazone with desolvation-induced spin-state transformation above room temperature.
The preparation and characterization of two new neutral ferric complexes with desolvation-induced discontinuous spin-state transformation above room temperature are reported. The compounds, [Fe(Hthpy)(thpy)].CH3OH.3H2O (1) and [Fe(Hmthpy)(mthpy)].2H2O (2), are low-spin (LS) at room temperature and below, whereas their nonsolvated forms are high-spin (HS), exhibiting zero-field splitting. In these complexes, Hthpy, Hmthpy, and thpy, mthpy are the deprotonated forms of pyridoxal thiosemicarbazone and pyridoxal methylthiosemicarbazone, respectively; each is an O,N,S-tridentate ligand. The molecular structures have been determined at 100(1) K using single-crystal X-ray diffraction techniques and resulted in a triclinic system (space group P1) and monoclinic unit cell (space group P21/c) for 1 and 2, respectively. Structures were refined to the final error indices, where RF = 0.0560 for 1 and RF = 0.0522 for 2. The chemical inequivalence of the ligands was clearly established, for the "extra" hydrogen atom on the monodeprotonated ligands (Hthpy, Hmthpy) was found to be bound to the nitrogen of the pyridine ring. The ligands are all of the thiol form; the doubly deprotonated chelates (thpy, mthpy) have C-S bond lengths slightly longer than those of the singly deprotonated forms. There is a three-dimensional network of hydrogen bonds in both compounds. The discontinuous spin-state transformation is accompanied with liberation of solvate molecules. This is evidenced also from DSC analysis. Heat capacity data for the LS and HS phases are tabulated at selected temperatures, the values of the enthalpy and entropy changes connected with the change of spin state were reckoned at DeltaH = 12.5 +/- 0.3 kJ mol-1 and DeltaS = 33.3 +/- 0.8 J mol-1 K-1, respectively, for 1 and DeltaH = 6.5 +/- 0.3 kJ mol-1 and DeltaS = 17.6 +/- 0.8 J mol-1 K-1, respectively, for 2.
Tido
Eddy W Yemeli
EW
Stratingh Institute for Chemistry and Zernike Institute for Advanced Materials, University of Groningen, Nijenborgh 4, 9747 AG, Groningen, The Netherlands.
van Ekenstein
Gert O R Alberda
GO
Meetsma
Auke
A
van Koningsbruggen
Petra J
PJ