Effect of surface treatment and type of cement on the retentive strength of orthodontic bands on gold alloy crowns.
BACKGROUND
The objective of this study was to evaluate the effect of surface treatment of gold alloy crowns and type of cement on the retentive strength of orthodontic bands cemented on gold alloy crowns.


METHODS
Two hundred eight crowns, made of type IV dental gold alloy, were divided into 16 groups based on surface treatment (C, no treatment; S, sandblasting; V, V-Primer; and S + V, sandblasting and V-Primer) and band cement (resin-modified glass ionomer cement, compomer, composite resin, and adhesive resin cement). Bands were cemented on the crowns, and tensile loads were applied to measure the retentive strength. Two-way analysis of variance (ANOVA) was performed for the retentive strength with the factors of surface treatment and type of cement, and the Scheffé multiple comparison test was performed as a post-hoc test (alpha = 0.05).


RESULTS
The retentive strength of the bands was influenced by surface treatment and type of cement, and there was significant interaction between the 2 variables based on 2-way ANOVA (P <.05). Resin-modified glass ionomer cement showed the highest retentive strength regardless of surface treatment (>1.26 MPa).


CONCLUSIONS
Resin-modified glass ionomer cement is the most desirable cement for attaching a band to a gold alloy crown. When an adhesive resin cement is used, sandblasting of the gold crown is recommended.
Youn
Young-Ah
YA
Department of Dentistry, College of Medicine, Korea University, Seoul, Korea.
Lee
Yong-Keun
YK
Lee
Dong-Yul
DY
Kim
Na-Yeon
NY
Lim
Yong-Kyu
YK
D000537:Aluminum Oxide; D000704:Analysis of Variance; D002484:Cementation / Q000379:methods*; D020770:Compomers; D003442:Crowns; D045662:Dental Etching / Q000379:methods; D003799:Dental Stress Analysis; D005899:Glass Ionomer Cements; D006047:Gold Alloys; D006801:Humans; D008963:Molar; D009969:Orthodontic Wires; D019279:Resin Cements; D013499:Surface Properties; D013718:Tensile Strength; D014227:Triazines
D020770:Compomers; D005899:Glass Ionomer Cements; D006047:Gold Alloys; D019279:Resin Cements; D014227:Triazines; C107059:V-Primer; D000537:Aluminum Oxide