Synthesis, structure, and bonding of Sc4MgxCu15-xGa approximately 7.5 (x=0, 0.5). Two incommensurately modulated scandium substitution derivatives of cubic Mg2Cu6Ga5.
The substitution of scandium for magnesium in Mg2Cu6Ga5 (Mg2Zn11-type) yields an irrational superstructure phase that includes the refined compositions, Sc4Mg0.50(2)Cu14.50(2)Ga7.61(2) and Sc4Cu14.76(2)Ga7.51(2). These crystallize in Cmmm, a=approximately 8.31 A, b=approximately 21.72 A, c=approximately 8.30 A. The structures feature Sc2 dimers, Cu6 octahedra, a 3D CuGa (Cu12Ga2) framework, and arachno gallium-centered Cu4Ga6 icosahedra that are condensed into zigzag chains. The arrangement of these building blocks exhibits a topologic relationship to Mg2Cu6Ga5. Further studies reveal that the quaternary compound exhibits incommensurate modulations along a, with q=(0.694, 0, 0). Structure refinements with superspace group Xmmm(a00)000 led to saw-tooth modulations for two fractional or mixed sites that avoid short Cu-Ga distances. Band structure analyses reveal that the Fermi surface and bonding are sensitive to the incommensurately modulated atoms.
Lin
Qisheng
Q
Department of Chemistry, Iowa State University, Ames, Iowa 50010, USA.
Lidin
Sven
S
Corbett
John D
JD