Visible light induced electron transfer process over nitrogen doped TiO(2) nanocrystals prepared by oxidation of titanium nitride.
Nitrogen doped TiO(2) nanocrystals with anatase and rutile mixed phases were prepared by incomplete oxidation of titanium nitride at different temperatures. The as-prepared samples were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), high resolution transmission electron microscopy (HRTEM), core level X-ray photoelectron spectroscopy (CL XPS), valence band X-ray photoelectron spectroscopy (VB XPS), UV-vis diffuse reflectance spectra (UV-vis DRS), and visible light excited photoluminescence (PL). The photocatalytic activity was evaluated for photocatalytic degradation of toluene in gas phase under visible light irradiation. The visible light absorption and photoactivities of these nitrogen doped TiO(2) nanocrystals can be clearly attributed to the change of the additional electronic (N(-)) states above the valence band of TiO(2) modified by N dopant as revealed by the VB XPS and visible light induced PL. A band gap structure model was established to explain the electron transfer process over nitrogen doped TiO(2) nanocrystals under visible light irradiation, which was consistent with the previous theoretical and experimental results. This model can also be applied to understand visible light induced photocatalysis over other nonmetal doped TiO(2).
Wu
Zhongbiao
Z
Department of Environmental Engineering, Zhejiang University, Hangzhou 310027, China.
Dong
Fan
F
Zhao
Weirong
W
Guo
Sen
S
D008027:Light; D053758:Nanoparticles / Q000737:chemistry* / Q000528:radiation effects; D009584:Nitrogen / Q000737:chemistry*; D010084:Oxidation-Reduction; D014025:Titanium / Q000737:chemistry* / Q000528:radiation effects
C009495:titanium dioxide; C041500:titanium nitride; D014025:Titanium; D009584:Nitrogen