The effect of post-core and ferrule on the fracture resistance of endodontically treated maxillary central incisors.
OBJECTIVE
To evaluate the effect of post reinforcement, post type and ferrule on the fracture resistance of endodontically treated maxillary central incisors.


METHODS
Sixty central incisor teeth were selected and grouped into six groups, viz. A, B, C, D, E, and F, each consisting of 10 specimens. Group A specimens were not subjected to any restorative treatment. Group B specimens were endodontically treated and crowned. Specimens of groups C and D were restored with custom cast post and core. Specimens of groups E and F were treated with prefabricated titanium post and composite core. Specimens of groups C and E were restored with porcelain-fused metal (PFM) crown having 2 mm ferrule. Specimens of groups D and F were restored with PFM crown having no ferrule. All the specimens were subjected to load (newton, N) on the lingual surface at a 135 degree angle to the long axis with a universal testing machine until it fractured. The fracture load and mode of fracture of each specimen were noted. One-way analysis of variance with Tukey honestly significant difference procedure was employed to identify the significant difference among the groups at 5% level (P < 0.05).


RESULTS
There were significant differences among the six groups studied (P < 0.0001). The highest fracture strength was recorded with specimen of group C (1376.7 N). There were significant differences between groups A and D versus groups B, E, and F. There were no significant differences between groups B, E, and F. Cervical root fracture was the predominant mode of failure in all the groups except group A.


CONCLUSIONS
The results showed that endodontically treated teeth restored with custom cast post core were as strong as the untreated group. Teeth restored with custom cast post core were better resistant to fracture than teeth restored with prefabricated titanium post and composite core. Ferrule is more important in custom cast post core than in prefabricated post and composite core.
Sendhilnathan
Dakshinamurthy
D
Department of Prosthodontics, Meenakshi Ammal Dental College, Maduravoyal, Chennai, Tamil Nadu, India. drdsendhil04@yahoo.co.in
Nayar
Sanjna
S
D000704:Analysis of Variance; D003442:Crowns; D017267:Dental Prosthesis Design; D003799:Dental Stress Analysis; D006801:Humans; D007180:Incisor; D008437:Maxilla; D016876:Metal Ceramic Alloys; D011176:Post and Core Technique; D014082:Tooth Fractures / Q000517:prevention & control*; D019553:Tooth, Nonvital
D016876:Metal Ceramic Alloys