Characterization of flux-grown PZN-PT single crystals for high-performance piezo devices.
Relaxor ferroelectric Pb(Zn(1/3)Nb(2/3))O(3-x)PbTiO(3) (PZN-PT) and Pb(Mg(1/3)Nb(2/3))O(3)-PbTiO(3)(PMN-PT) single crystals are the potential candidates for future high-performance piezoelectric devices due to their exceptionally high dielectric and piezoelectric properties. Characterization on flux-grown PZN-PT single crystals of different orientations revealed that PZN-(6-7)%PT single crystals show good homogeneity in dielectric and electromechanical properties and composition. When poled in [001] direction, these crystals exhibit high longitudinal-mode properties with dielectric constant (K(T)) approximately equal to 7000, piezoelectric coefficients (d(33)) approximately equal to 2800 pC/N, and electromechanical coupling factors (k(33)) > or = 0.92. For [011]-cut crystals, optimally poled PZN-7%PT single crystal exhibits very high transverse-mode dielectric and piezoelectric properties with K(T) > or = 5000, d(32) approximately equal to -3800 pC/N and k(32) > or = 0.90. [011]- poled PZN 6%PT has d(32) approximately equal to -3000 pC/N and comparable k(32) and K(T) values. In comparison with melt-grown PMNPT single crystals, flux-grown PZN-PT single crystals show good compositional homogeneity, superior and consistent dielectric and electromechanical properties, and higher depolarization temperatures (TDP).
Lim
Leong Chew
LC
Ministry of Education, Singapore, and National University of Singapore, Singapore 119260.
Rajan
Kotam Kalidindi
KK
Jin
Jing
J