Solid-state P-31 NMR study of the formation of hydroxyapatite in the presence of glutaric acid.
We demonstrate that glutaric acid can be used to prepare nanorods of hydroxyapatite under hydrothermal condition at 100 degrees C with a Ca(2+):glutaric acid molar ratio of 1:4. Frequency-switched Lee-Goldburg irradiation is employed to obtain high-resolution (31)P{(1)H} correlation spectra of the reaction mixture at two different reaction periods, from which it is shown that octacalcium phosphate is the precursor phase of the final hydroxyapatite product. In addition, the spectra show that a substantial amount of water molecules is trapped between the glutaric acid and the hydroxyapatite surface, indicating that water molecules may play a prominent role in the noncovalent interaction of the glutaric acid and the HAp surface.
Tseng
Yao-Hung
YH
Department of Chemistry, National Taiwan University, No. 1, Section 4, Roosevelt Road, Taipei, Taiwan.
Mou
Yun
Y
Chen
Peng-Huan
PH
Tsai
Tim W T
TW
Hsieh
Cheng-I
CI
Mou
Chung-Yuan
CY
Chan
Jerry C C
JC
D017886:Durapatite / Q000138:chemical synthesis* / Q000737:chemistry*; D005977:Glutarates / Q000737:chemistry*; D009682:Magnetic Resonance Spectroscopy / Q000379:methods* / Q000592:standards; D008855:Microscopy, Electron, Scanning; D010316:Particle Size; D010759:Phosphorus Isotopes; D012015:Reference Standards; D014961:X-Ray Diffraction
D005977:Glutarates; D010759:Phosphorus Isotopes; D017886:Durapatite; C035736:glutaric acid