Fabrication of low-crystallinity hydroxyapatite foam based on the setting reaction of alpha-tricalcium phosphate foam.
Low-crystallinity hydroxyapatite (HAP) foam is an ideal material for bone substitutes and scaffolds for bone tissue regeneration, because its interconnected pores provide the space for cell growth and tissue penetration, and its composition induces excellent tissue response and good osteoconductivity. In this study, the feasibility of low-crystallinity HAP foam fabrication was evaluated based on the phase transformation reaction or the so-called dissolution-reprecipitation reaction of alpha-tricalcium phosphate (alpha-TCP) foam granules. When alpha-TCP foam granules were placed in water at 37 degrees C for 1 day, no reaction was observed. However, alpha-TCP foam granules set to form low-crystallinity HAP by treating it hydrothermally at 200 degrees C. The network of fully interconnected pores was retained, and porosity was as high as 82%. Pore size ranged from 50 to 300 mum with an average pore size of 160 mum. Compressive strength was 207 kPa. Although no setting reaction was observed at 37 degrees C, the setting reaction caused by the hydrothermal treatment of alpha-TCP foam granules allowed the fabrication of any shape of low-crystallinity HAP. Therefore, this method may be useful for the fabrication of bone substitutes and scaffolds in bone tissue regeneration.
Karashima
Satoshi
S
Section of Biomaterials, Division of Oral Rehabilitation, Faculty of Dental Science, Kyushu University, 3-1-1 Maidashi, Higashi-ku, 812-8582 Fukuoka, Japan.
Takeuchi
Akari
A
Matsuya
Shigeki
S
Udoh
Koh-Ichi
K
Koyano
Kiyoshi
K
Ishikawa
Kunio
K
D002130:Calcium Phosphates / Q000737:chemistry*; D003460:Crystallization; D017886:Durapatite / Q000737:chemistry*; D006863:Hydrogen-Ion Concentration; D008855:Microscopy, Electron, Scanning; D017550:Spectroscopy, Fourier Transform Infrared; D013285:Strabismus; D014867:Water / Q000737:chemistry; D014961:X-Ray Diffraction
D002130:Calcium Phosphates; C485828:alpha-tricalcium phosphate; D014867:Water; D017886:Durapatite