Recovering obliterated engraved marks on aluminium surfaces by etching technique.
A study has been made of the characteristics of restoration of obliterated engraved marks on aluminium surfaces by etching technique. By etching different reagents on 0.61mm thick sheets of aluminium (99wt%) on which some engraved marks had been erased to different depths it was found that the reagent 60% hydrochloric acid and 40% sodium hydroxide on alternate swabbing on the surfaces was found to be the most sensitive one for these metal surfaces. This reagent was able to restore marks in the above plates erased down to 0.04mm below the bottom of the engraving. The marks also presented excellent contrast with the background. This reagent was further experimented with similar aluminium surfaces, but of relatively greater thickness of 1.5mm. It was noticed that the recovery depth increased slightly to 0.06mm; this suggested the dependence of recovery depth on the thickness of the sheet metal. Further, the depth of restoration decreased in cases where the original number was erased and over which a new number was engraved; the latter results are similar to those of steel surfaces reported earlier [M.A.M. Zaili, R. Kuppuswamy, H. Harun, Restoration of engraved marks on steel surfaces by etching technique, Forensic Sci. Int. 171 (2007) 27-32].
Baharum
Mohd Izhar Mohd
MI
Forensic Science Programme, School of Health Sciences, Universiti Sains Malaysia, Kampus Kesihatan, 16150 Kubang Kerian, Kelantan, Malaysia.
Kuppuswamy
R
R
Rahman
Azari Abd
AA