Ultra-high oxidation resistance of suspended single-wall carbon nanotube bundles grown by an "all-laser" process.
Single-wall carbon nanotubes (SWCNTs) were laterally grown on SiO2/Si substrates by means of an "all-laser" growth process. Our "all-laser" process stands out by its exclusive use of the same pulsed UV laser, first, to deposit the CoNi nanocatalyst and, second, to grow SWCNTs through the laser ablation of a pure graphite target. The "all-laser" grown SWCNTs generally self-assemble into bundles (5-15 nm-diam.) sprouting from the CoNi nanocatalyst and laterally bridging the 2 microm gap separating adjacent catalysed electrodes (in either "suspended" or "on-substrate" geometries). A comparative study of the oxidation resistance of both suspended and on-substrate SWCNTs was achieved. The "all-laser" grown SWCNTs were subjected to annealing under flowing oxygen at temperatures ranging from 200 to 1100 degrees C. Systematic scanning electron microscopy observations combined with micro-Raman analyses revealed that more than 20% of suspended nanotubes were still stable at temperatures as high as 900 degrees C under flowing O2 while the on-substrate counterpart were completely burnt out at this temperature. Accordingly, the activation energy, as deduced from the Arrhenius plot, of the suspended SWCNTs is found to be as high as approximately 180 kJ mol(-1) (approximately 9 times higher than that of the on-substrate ones). The high quality (almost defect-free) of the nanotubes synthesized by the "all-laser" approach, their protected tips into the embedded CoNi catalyst nanolayer together with their suspended geometry are thought to be responsible for their unprecedented ultra-high oxidation resistance. This opens up new prospects for the use of these suspended nanotubes into nanodevices that have to operate under highly oxidizing environments.
Yi
J H
JH
Institut National de la Recherche Scientifique, INRS-Energie, Matériaux et Téléommunications 1650, Blvd. Lionel-Boulet, C.P 1020, Varennes, Ouébec, Canada.
Aïssa
B
B
El
Khakani M A
KM
D003460:Crystallization / Q000379:methods*; D007834:Lasers; D046911:Macromolecular Substances / Q000737:chemistry; D008422:Materials Testing; D008968:Molecular Conformation; D036103:Nanotechnology / Q000379:methods*; D037742:Nanotubes, Carbon / Q000737:chemistry* / Q000648:ultrastructure*; D010084:Oxidation-Reduction; D010316:Particle Size; D013499:Surface Properties; D013696:Temperature
D046911:Macromolecular Substances; D037742:Nanotubes, Carbon