Development of a microemulsion-based process for synthesis of cobalt (Co) and cobalt oxide (Co3O4) nanoparticles from submicrometer rods of cobalt oxalate.
Rod-shaped nanostructures of cobalt oxalate dihydrate were synthesized at room temperature by the microemulsion (reverse micellar) route. These rods are highly uniform in length and can be modified with temperature (from approximately 6.5 microm at 50 degrees C to approximately 2.5 microm at 150 degrees C) while keeping the diameter nearly constant (200-250 nm). Thermal decomposition of these rods in a controlled atmosphere (air and H(2)) leads to nanoparticles of Co(3)O(4) and Co, respectively, while in a helium atmosphere a mixture of Co and CoO nanoparticles is obtained. Co(3)O(4) nanoparticles (approximately 35 nm) were slightly agglomerated, while Co nanoparticles were monodispersed and highly uniform (approximately 25 nm). The oxalate rods and Co(3)O(4) nanoparticles show an antiferromagnetic ordering at 54 and 35 K, respectively.
Ahmed
Jahangeer
J
Department of Chemistry, Indian Institute of Technology, Hauz Khas, New Delhi 110016, India.
Ahmad
Tokeer
T
Ramanujachary
Kandalam V
KV
Lofland
Samuel E
SE
Ganguli
Ashok K
AK