Incorporating perylene moiety into poly(phenothiazine-co-bithiophene) backbone for higher charge transport.
Low band gap pi-conjugated polymers composed of phenothiazine, bithiophene, and perylene moieties were prepared in high yields by using a palladium-catalyzed Suzuki coupling reaction. The polymers were characterized by NMR, gel permeation chromatography, and elemental analysis. The characterizations revealed that high-molecular weight (weight-average molecular weight up to 42,400 g/mol) polymers were thermally stable with a decomposition temperature in the region of 338-354 degrees C and their glass transition temperatures (Tg) ranging from 124 to 136 degrees C. All polymers demonstrated broad optical absorption in the region of 300-550 nm with efficient blue-green light emission. The absorption was broadened further (for ca. 50 nm) when the perylene moiety was incorporated. Cyclic voltammograms displayed that the p- and n-doping processes of all the polymers were partially reversible and that electrochemical band gaps were as low as -2.30 eV with the incorporation of a perylene moiety. The hole mobility of polymers was evaluated by using the space-charge-limited current model with a device structure of ITO/PEDOT:PSS/polymer/Ca. The results show that the incorporation of perylene is beneficial for improving the hole mobility of the conjugated polymers.
Tang
Weihua
W
Institute of Materials Research and Engineering, 3 Research Link, Singapore 117602, Singapore.
Ke
Lin
L
Chen
Zhi-Kuan
ZK