Evaluation of monomer leaching from a dual cured resin cement.
OBJECTIVE
An increasing number of inlay cavities is restored with tooth-colored materials, especially ceramics are cemented with resin cements. The comonomer TEGDMA and other monomers Bis-GMA and UDMA have been identified as the main compounds released from polymerized resin cements into aqueous media. The present investigation was conducted to clarify the leaching behavior of the monomers of dual polymerized resin cement.


METHODS
Ten freshly extracted caries and restoration free molar teeth were used in this study. Standardized Class I preparations were prepared in all teeth. Lithium disilicate based (IPS Empress Esthetic) ceramic inlays were cemented with dual polymerized resin cement (Variolink II). After cementation, specimens were stored in 75% ethanol solution. High-performance liquid chromatography (HPLC) was used to analyze the amounts of three monomers in the solution (after 10 min, 1 h, 24 h, 3, 7, 14, and 21 days). Two-way ANOVA and Tukey HSD tests were used to evaluate the results (p < 0.05).


RESULTS
There were statistically significant differences among the amounts of the monomers (p < 0.01) and also among time periods (p < 0.01). While the TEGDMA resulted in significantly higher amount than Bis-GMA and UDMA, there were no statistically significant differences between amounts of Bis-GMA, UDMA (p = 0.06). The cumulative amount of monomers was the highest after 21 days (p < 0.01).


CONCLUSIONS
In the case of resin cement, leaching of TEGDMA was the highest and the cumulative amount of leaching monomers from resin cement was influenced by the time.
Altintas
Subutay Han
SH
Department of Prosthodontics, Karadeniz Technical University, Trabzon, Turkey. subutayhan@yahoo.com
Usumez
Aslihan
A
D017438:Bisphenol A-Glycidyl Methacrylate; D002484:Cementation; D002516:Ceramics; D002851:Chromatography, High Pressure Liquid; D006801:Humans; D007284:Inlays / Q000379:methods*; D008963:Molar; D010539:Permeability; D011092:Polyethylene Glycols; D011109:Polymethacrylic Acids; D019279:Resin Cements / Q000737:chemistry* / Q000592:standards
C095997:DCR cement; D011109:Polymethacrylic Acids; D019279:Resin Cements; C020946:triethylene glycol dimethacrylate; C103502:Variolink; D011092:Polyethylene Glycols; D017438:Bisphenol A-Glycidyl Methacrylate