title: [Fabrication and physical properties of porous individual beta-TCP scaffold to reconstruct residual alveolar ridge in dog].
abstract: OBJECTIVE
  To fabricate porous individual beta-tricalcium phosphate scaffold and test its properties in dog.
  
  
  METHODS
  A model of residual alveolar ridge in mandible of a dog was made and CT scanned after 3 months.The data of CT was transformed to 3-D format by MIMICS 7.0 and was made to resin model by rapid prototype technique.The residual alveolar ridge was reconstructed using silicon rubber, and its impression was made.Porous individual beta-tricalcium phosphate scaffold and 5 samples were fabricated for precision and properties test.Porosity, water absorbing capacity and compressive strength of samples were tested with crystalling phase and pore structure were analysed by XRD and scanning electron microscope.
  
  
  RESULTS
  We successfully fabricated a scaffold which fit the resin model well and consisted of beta-TCP. Its porosity was 74%,water absorbing capacity was 48%,compressive strength was 4 MPa,diameter of pore was 150 to 400 microm,connecting diameter was 40 microm.
  
  
  CONCLUSIONS
  We can fabricate individual beta-TCP scaffold which fit the model well by combination of traditional method and rapid prototype technique.Supported by Shanghai Leading Academic Discipline Project(Grant No.T0202).
authors: Department of Prosthodontics, College of Stomatology, Ninth People's Hospital, School of Medicine, Shanghai Jiao Tong University, Shanghai 200011, China.
authors: Xiang-Yong
authors: XY
authors: Han
authors: Fu-Qiang
authors: FQ
authors: Zhang
authors: Yuan-Fei
authors: YF
authors: Fu
authors: De-Min
authors: DM
authors: Chen
mesh_terms: D000539:Alveolar Process; D000818:Animals; D002130:Calcium Phosphates; D019245:Compressive Strength; D004285:Dogs; D008422:Materials Testing; D016062:Porosity; D012117:Resins, Synthetic
chemical_list: D002130:Calcium Phosphates; D012117:Resins, Synthetic; C485817:beta-tricalcium phosphate