Crystallization and dissolution of flow-induced precursors.
We make use of a specially synthesized linear high density polyethylene with a bimodal molecular weight distribution (MWD) to demonstrate that it is possible to produce a suspension of extended-chain (shish) crystals only. Such a suspension can be generated at high temperatures, above but close to the equilibrium melting temperature of the unconstrained extended-chain crystals (T(m)(0)=141.2 degrees C) and requires stretch of the longest chains of the MWD. After the application of a shear flow of 120 s(-1) for 1 s at 142 degrees C, x-ray scattering suggests the presence of a large number of metastable needlelike precursors with limited or no crystallinity. Precursors that are too small dissolve on a timescale that correlates perfectly with the reptation time of the longest polymer molecules. Whereas, precursors that exceed a critical size crystallize forming extended-chain shishes.
Balzano
Luigi
L
Department of Chemical Engineering, Eindhoven University of Technology, P.O. Box 513, 5600 MB, Eindhoven, The Netherlands.
Kukalyekar
Nileshkumar
N
Rastogi
Sanjay
S
Peters
Gerrit W M
GW
Chadwick
John C
JC