Homoleptic copper(I) arylthiolates as a new class of p-type charge carriers: structures and charge mobility studies.
Polymeric homoleptic copper(I) arylthiolates [Cu(p-SC(6)H(4)-X)](infinity) (X=CH(3) (1), H (2), CH(3)O (3), tBu (4), CF(3) (5), NO(2) (6), and COOH (7)) have been prepared as insoluble crystalline solids in good yields (75-95 %). Structure determinations by powder X-ray diffraction analysis have revealed that 1-3 and 6 form polymers of infinite chain length, with the copper atoms bridged by arylthiolate ligands. Weak intra-chain pi***pi stacking interactions are present in 1-3, as evidenced by the distances (3.210 A in 1, 3.016 A in 2, 3.401 A in 3) between the mean planes of neighboring phenyl rings. In the structure of 6, the intra-chain pi***pi interactions (d=3.711 A) are insignificant and the chain polymers are associated through weak, non-covalent C-H...O hydrogen-bonding interactions (d=2.586 A). Samples of 1-7 in their polycrystalline forms proved to be thermally stable at 200-300 degrees C; their respective decomposition temperatures are around 100 degrees C higher than that of the aliphatic analogue [Cu(SCH(3))](infinity). Data from in situ variable-temperature X-ray diffractometry measurements indicated that the structures of both 1 and 7 are thermally more robust than that of [Cu(SCH(3))](infinity). TEM analysis revealed that the solid samples of 1-5 and [Cu(SCH(3))](infinity) contained homogeneously dispersed crystalline nanorods with widths of 20-250 nm, whereas smaller plate-like nanocrystals were found for 6 and 7. SAED data showed that the chain polymers of 1-3 and [Cu(SCH(3))](infinity) similarly extend along the long axes of their nanorods. The nanorods of 1-5 and [Cu(SCH(3))](infinity) have been found to exhibit p-type field-effect transistor behavior, with charge mobility (micro) values of 10(-2)-10(-5) cm(2) V(-1) s(-1). Polycrystalline solid samples of 6 and 7 each showed a low charge mobility (<10(-6) cm(2) V(-1) s(-1)). The charge mobility values of field-effect transistors made from crystalline nanorods of 1-3 and [Cu(SCH(3))](infinity) could be correlated with their unique chain-like copper-sulfur networks, with the para-substituent of the arylthiolate ligand influencing the charge-transport properties.
Che
Chi-Ming
CM
Coordination Chemistry Institute and the State Key Laboratory of Coordination Chemistry, School of Chemistry and Chemical Engineering, Nanjing University, Nanjing 210093, PR China. cmche@hku.hk
Li
Cheng-Hui
CH
Chui
Stephen Sin-Yin
SS
Roy
V A L
VA
Low
Kam-Hung
KH
D003300:Copper / Q000737:chemistry*; D004553:Electric Conductivity; D008958:Models, Molecular; D015394:Molecular Structure; D009942:Organometallic Compounds / Q000138:chemical synthesis / Q000737:chemistry*; D010316:Particle Size; D013438:Sulfhydryl Compounds / Q000737:chemistry*; D013696:Temperature; D014173:Transistors, Electronic
D009942:Organometallic Compounds; D013438:Sulfhydryl Compounds; D003300:Copper