Phosphoric acid modified-Y zeolites: a novel, efficient and versatile ion exchanger.
Large pore HY zeolite was modified with phosphoric acid by wet method. The modified zeolite was converted to Na(+) form using aqueous NaHCO(3) solution(.) The Na(+) form of modified zeolite, represented as PNa(2)Y, was characterized by XRD, BET surface area, SEM, and AAS techniques. The XRD analysis showed diffraction patterns same as that of parent HY zeolite, as a result there has been no structural degradation during modification. It was then tested for sorption of Cu(2+) ions from aqueous solution. The Cu(2+) content of the solution was analyzed by AAS. PNa(2)-Y shows higher sorption capacity ( approximately 40%) than the parent Na-Y ( approximately 23%) zeolite, which is attributed to the double of amount Na(+) content in PNa(2)-Y compared to the Na-Y zeolite. Equilibrium modeling data were found to fit more to the linear Langmuir model than the Freundlich model. The thermodynamic parameters such as change in free energy (DeltaG degrees ), enthalpy (DeltaH degrees ), and entropy (DeltaS degrees ), were also calculated. These parameters confirmed that the sorption of Cu(2+) is feasible, spontaneous and endothermic.
Panneerselvam
P
P
Environmental Management Laboratory, Department of Chemical Engineering, A.C. College of Technology, Anna University, Guindy, Chennai 600025, Tamil Nadu, India.
Thinakaran
N
N
Thiruvenkataravi
K V
KV
Palanichamy
M
M
Sivanesan
S
S
D000327:Adsorption; D004058:Diffusion; D006863:Hydrogen-Ion Concentration; D007474:Ion Exchange; D007475:Ion Exchange Resins / Q000737:chemistry*; D007700:Kinetics; D008855:Microscopy, Electron, Scanning; D010756:Phosphoric Acids / Q000737:chemistry*; D011522:Protons; D012964:Sodium / Q000737:chemistry; D017693:Sodium Bicarbonate; D013816:Thermodynamics; D017641:Zeolites / Q000737:chemistry*
D007475:Ion Exchange Resins; D010756:Phosphoric Acids; D011522:Protons; D017641:Zeolites; D017693:Sodium Bicarbonate; D012964:Sodium; C030242:phosphoric acid