title: Morphological evolution in dewetting polystyrene/polyhedral oligomeric silsesquioxane thin film bilayers.
abstract: Morphological evolution in dewetting thin film bilayers of polystyrene (PS) and a polyhedral oligomeric silsesquioxane (POSS), trisilanolphenyl-POSS (TPP), was studied as a function of annealing temperature and annealing time. The results demonstrate unique dewetting morphologies in PS/TPP bilayers at elevated temperatures that are significantly different from those typically observed in dewetting polymer/polymer bilayers. During temperature ramp studies by optical microscopy (OM) in the reflection mode, PS/TPP bilayers form cracks with a weak optical contrast at approximately 130 degrees C. The crack formation is attributed to tensile stresses within the upper TPP layer. The weak optical contrast of the cracks observed in the bilayers for annealing temperatures below approximately 160 degrees C is consistent with the cracking and dewetting of only the upper TPP layer from the underlying PS layer. The optical contrast of the morphological features is significantly enhanced at annealing temperatures of >160 degrees C. This observation suggests dewetting of both the upper TPP and the lower PS layers that results in the exposure of the silicon substrate. Upon annealing the PS/TPP bilayers at 200 degrees C in a temperature jump experiment, the upper TPP layer undergoes instantaneous cracking as observed by OM. These cracks in the upper TPP layer serve as nucleation sites for rapid dewetting and aggregation of the TPP layer, as revealed by OM and atomic force microscopy (AFM). X-ray photoelectron spectroscopy (XPS) results indicated that dewetting of the lower PS layer ensued for annealing times >5 min and progressed up to 90 min. For annealing times >90 min, OM, AFM, and XPS results revealed complete dewetting of both the layers with the formation of TPP encapsulated PS droplets.
authors.affiliation: Macromolecules and Interfaces Institute and the Department of Chemistry (0212), Virginia Polytechnic Institute and State University, Blacksburg, Virginia 24061, USA.
authors.forename: Rituparna
authors.initials: R
authors.lastname: Paul
authors.forename: Ufuk
authors.initials: U
authors.lastname: Karabiyik
authors.forename: Michael C
authors.initials: MC
authors.lastname: Swift
authors.forename: John R
authors.initials: JR
authors.lastname: Hottle
authors.forename: Alan R
authors.initials: AR
authors.lastname: Esker
mesh_terms: D018625:Microscopy, Atomic Force; D015394:Molecular Structure; D017646:Organosilicon Compounds / Q000737:chemistry*; D011137:Polystyrenes / Q000737:chemistry*; D013696:Temperature; D013997:Time Factors
chemical_list: D017646:Organosilicon Compounds; D011137:Polystyrenes