Viscoelastic properties of an exopolysaccharide: Aeromonas gum, produced by Aeromonas nichidenii 5797.
The viscoelastic properties of Aeromonas (A) gum in water were investigated by using the Rheometric Scientific ARES controlled strain rheometer. An intrinsic viscosity of 8336 ml/g was obtained according to the Fuoss-Straus equation. The effect of salt concentration on intrinsic viscosity revealed that the A gum exists as semiflexible chain. Typical shear-thinning (pseudoplastic) behavior was observed at concentrations higher than 0.52%. The zero shear viscosity (eta(0)) increased with increasing polysaccharide concentration (c) showing a gradient of approximately 1.0, 2.9 and 4.8 in different concentration domains. The critical concentrations c* and c**, at which the transitions from a dilute solution of independently moving chains to semidilute and then concentrated domains occurred, were determined roughly to be 1.2% and 3.5%. The results from dynamic experiments revealed that the A gum solution shows characteristics of polymer solutions without any evidence of gel-like character. All the results from steady and dynamic tests suggest that the A gum is a non-gelling polysaccharide. The temperature dependence of apparent viscosity was described by Arrhenius equation and the flow activation energy was estimated to be 45.2 kJ/mol, which is independent on polymer concentration.
Xu
Xiaojuan
X
Department of Chemistry, Wuhan University, Wuhan, China. xuxj626@263.net
Chen
Pan
P
Zhang
Lina
L
D000333:Aeromonas / Q000378:metabolism*; D001704:Biopolymers / Q000096:biosynthesis / Q000737:chemistry*; D004548:Elasticity; D011135:Polysaccharides, Bacterial / Q000096:biosynthesis / Q000737:chemistry*; D012212:Rheology; D033081:Shear Strength; D013314:Stress, Mechanical; D013696:Temperature; D014783:Viscosity
D001704:Biopolymers; D011135:Polysaccharides, Bacterial