Effect of erosive pH cycling on different restorative materials and on enamel restored with these materials.
This in vitro study evaluated the effect of erosive pH cycling on the percentage of surface micro-hardness change (%SMHC) and wear of different restorative materials and bovine enamel restored with these materials. Eighty enamel specimens were randomly divided into eight groups according to the restorative materials and immersion media used: GI/GV-resin-modified glass-ionomer, GII/GVI-conventional glass-ionomer, GIII/GVII-resin composite and GIV/GVIII-amalgam. Over a period of seven days, groups GI to GIV were immersed in a cola drink (ERO) for 5 minutes, 3x/day and kept in artificial saliva between erosive cycles. Groups GV to GVIII were immersed in artificial saliva (SAL) throughout the entire experimental period (control). Data were tested for significant differences using ANOVA and Tukey's tests (p<0.05). For %SMHC, considering the restorative materials, no significant differences were detected among the materials and immersion media. Mean wear was higher for the resin modified glass ionomer cement when compared to conventional cement, but those materials did not significantly differ from the others. For enamel analyses, erosive pH cycling promoted higher wear and %SMHC compared to saliva. There were no significant differences in wear and %SMHC of enamel around the different restorative materials, regardless of the distance from the restorative material (50, 150 or 300 microm). In conclusion, there were only subtle differences among the materials, and these differences were not able to protect the surrounding enamel from erosion.
Francisconi
Luciana Fávaro
LF
Department of Operative Dentistry, Endodontics and Dental Materials, Bauru School of Dentistry, University of São Paulo, Bauru/SP, Brazil.
Honório
Heitor Marques
HM
Rios
Daniela
D
Magalhães
Ana Carolina
AC
Machado
Maria Aparecida de Andrade Moreira
MA
Buzalaf
Marília Afonso Rabelo
MA
D000818:Animals; D002253:Carbonated Beverages; D002417:Cattle; D003188:Composite Resins / Q000737:chemistry; D003723:Dental Amalgam / Q000737:chemistry; D003743:Dental Enamel / Q000473:pathology*; D003764:Dental Materials / Q000737:chemistry*; D019554:Dental Restoration Wear / Q000145:classification*; D003793:Dental Restoration, Permanent; D005899:Glass Ionomer Cements / Q000737:chemistry; D006244:Hardness; D006863:Hydrogen-Ion Concentration; D008422:Materials Testing; D011897:Random Allocation; D019279:Resin Cements / Q000737:chemistry; D012464:Saliva, Artificial / Q000737:chemistry; D013499:Surface Properties; D013997:Time Factors; D014077:Tooth Erosion / Q000503:physiopathology*
D003188:Composite Resins; D003764:Dental Materials; D005899:Glass Ionomer Cements; D019279:Resin Cements; D012464:Saliva, Artificial; D003723:Dental Amalgam