title: A study on in vitro degradation behavior of a poly(glycolide-co-L-lactide) monofilament.
abstract: The in vitro degradation behaviors of a poly(glycolide-co-l-lactide) 90/10 monofilament were investigated in phosphate buffer solution at pH 7.4 over a temperature range of 27.5-47.5 degrees C. The property changes of the monofilament with time at different temperatures were evaluated by tensile mechanical test, gel permeation chromatography analysis, and image techniques (optical microscopy, scanning electron microscopy and atomic force microscopy). The interrelationships among material properties, in vitro time and experimental conditions were explored. The results showed that the polymer monofilament gradually lost its tensile strength and molecular weight with increasing in vitro time. The hydrolytic degradation of the monofilaments followed a first order behavior. Higher temperatures accelerated the degradation process significantly. It was found that for a given tensile breaking strength retention (BSR), the dependence of degradation time on temperature could be illustrated by an Arrhenius-type equation, from which the activation energy was derived. Further analysis indicated that there are well-defined relationships between molecular weight and tensile strength, which could be illustrated mathematically. Finally, the microscopic evaluation of the monofilament samples revealed visible changes in morphology on the surface and cross-section area during degradation process. The results from atomic force microscopy showed that the surface roughness of the monofilament tended to increase with the in vitro time.
authors.affiliation: R&D Division, ETHICON, Inc., Johnson & Johnson Company, P.O. Box 151, Somerville, NJ 08876, USA. mdeng@ethus.jnj.com
authors.forename: Meng
authors.initials: M
authors.lastname: Deng
authors.forename: Gavin
authors.initials: G
authors.lastname: Chen
authors.forename: Daniel
authors.initials: D
authors.lastname: Burkley
authors.forename: Jack
authors.initials: J
authors.lastname: Zhou
authors.forename: Dennis
authors.initials: D
authors.lastname: Jamiolkowski
authors.forename: Yunmei
authors.initials: Y
authors.lastname: Xu
authors.forename: Robert
authors.initials: R
authors.lastname: Vetrecin
mesh_terms: D020341:Absorbable Implants; D001672:Biocompatible Materials / Q000737:chemistry*; D001826:Body Fluids / Q000737:chemistry*; D004548:Elasticity; D019344:Lactic Acid / Q000737:chemistry*; D008422:Materials Testing; D008970:Molecular Weight; D010316:Particle Size; D011100:Polyglycolic Acid / Q000737:chemistry*; D000077182:Polylactic Acid-Polyglycolic Acid Copolymer; D013314:Stress, Mechanical; D013499:Surface Properties; D013718:Tensile Strength
chemical_list: D001672:Biocompatible Materials; D000077182:Polylactic Acid-Polyglycolic Acid Copolymer; D011100:Polyglycolic Acid; D019344:Lactic Acid