Photocatalytic reduction of NO with NH3 using Si-doped TiO2 prepared by hydrothermal method.
A series of Si-doped TiO2 (Si/TiO2) photocatalysts supported on woven glass fabric were prepared by hydrothermal method for photocatalytic reduction of NO with NH3. The photocatalytic activity tests were carried out in a continuous Pyrex reactor with the flow rate of 2000mL/min under UV irradiation (luminous flux: 1.1x10(4)lm, irradiated catalyst area: 160cm2). The photocatalysts were characterized by X-ray diffraction (XRD), BET, X-ray photoelectron spectroscopy (XPS), Fourier transform infrared (FT-IR) spectrophotometer, transmission electron microscopy (TEM), photoluminescence (PL) and temperature-programmed desorption (TPD). The experiment results showed that NO conversion on Si/TiO2 at 323K could exceed 60%, which was about 50% higher than that on Degussa P25 and pure TiO2. With the doping of Si, photocatalysts with smaller crystal size, larger surface area and larger pore volume were obtained. It was also found that Ti-O-Si bands were formed on the surface of Si/TiO2 and that the surface hydroxyl concentration was greatly increased. As a result, total acidity and NH3 chemisorption amount were enhanced for Si/TiO2 leading to its photocatalytic activity improvement.
Jin
Ruiben
R
Department of Environmental Engineering, Zhejiang University, Hangzhou 310027, China.
Wu
Zhongbiao
Z
Liu
Yue
Y
Jiang
Boqiong
B
Wang
Haiqiang
H
D002384:Catalysis; D004058:Diffusion; D046529:Microscopy, Electron, Transmission; D009569:Nitric Oxide / Q000032:analysis* / Q000737:chemistry*; D010084:Oxidation-Reduction; D010777:Photochemistry; D000644:Quaternary Ammonium Compounds / Q000737:chemistry*; D012825:Silicon / Q000737:chemistry*; D013053:Spectrophotometry; D013696:Temperature; D014025:Titanium / Q000737:chemistry*; D014867:Water / Q000737:chemistry*; D014961:X-Ray Diffraction
D000644:Quaternary Ammonium Compounds; D014867:Water; C009495:titanium dioxide; D009569:Nitric Oxide; D014025:Titanium; D012825:Silicon