Simple route to monodispersed silica-titania core-shell photocatalysts.
A monodispersed silica-titania core-shell photocatalyst was synthesized via a sol-gel route without the need of pH adjustment, cationic polyelectrolytes, or surfactants in a process where silica spheres were impregnated with hydrolyzed titanium tetrabutoxide, incubated at room temperature, and then condensed using an ethanol/water (1:1) solvent. Four coating cycles in a 10% v/v titania sol produced homogeneous titania shells. The quality of catalysts was assessed quantitatively using Rietveld analysis of powder X-ray diffraction patterns combined with X-ray fluorescence spectrometry. During calcination, the anatase-to-rutile transformation was delayed to 1000 degrees C, which is approximately 300 degrees C higher than usually observed. The thermal stability and surface area of titania were enhanced through the slow crystal growth of anatase. The photocatalytic activity of the core-shell photocatalysts calcined at 400-600 degrees C was found to be proportional to the thickness of titania but did not directly correlate with the surface area.
Lim
Suo Hon
SH
School of Materials Science and Engineering, Nanyang Technological University, Singapore 639798. shlim@ntu.edu.sg
Phonthammachai
Nopphawan
N
Pramana
Stevin S
SS
White
T J
TJ