Poly(lactic-co-glycolic acid) bone scaffolds with inverted colloidal crystal geometry.
Controllability of scaffold architecture is essential to meet specific criteria for bone tissue engineering implants, including adequate porosity, interconnectivity, and mechanical properties to promote bone growth. Many current scaffold manufacturing techniques induce random porosity in bulk materials, requiring high porosities (>95%) to guarantee complete interconnectivity, but the high porosity sacrifices mechanical properties. Additionally, the stochastic arrangement of pores causes scaffold-to-scaffold variation. Here, we introduce a biodegradable poly(lactic-co-glycolic acid) (PLGA) scaffold with an inverted colloidal crystal (ICC) structure that provides a highly ordered arrangement of identical spherical cavities. Colloidal crystals (CCs) were constructed with soda lime beads of 100-, 200-, and 330-mum diameters. After the CCs were annealed, they were infiltrated with 85:15 PLGA. The method of construction and highly ordered structure allowed for ease of control over cavity and interconnecting channel diameters and for full interconnectivity at lower porosities. The scaffolds demonstrated high mechanical properties for PLGA alone (>50 MPa), in vitro biocompatibility, and maintenance of osteoblast phenotype, making them promising for a highly controllable bone tissue engineering scaffold.
Cuddihy
Meghan J
MJ
Department of Chemical Engineering, University of Michigan, Ann Arbor, Michigan 48109, USA.
Kotov
Nicholas A
NA
D000199:Actins / Q000378:metabolism; D001672:Biocompatible Materials / Q000737:chemistry*; D001861:Bone Regeneration / Q000502:physiology; D002460:Cell Line; D002470:Cell Survival / Q000502:physiology; D024042:Collagen Type I / Q000378:metabolism; D004247:DNA / Q000378:metabolism; D006801:Humans; D019344:Lactic Acid / Q000737:chemistry*; D018613:Microscopy, Confocal; D008855:Microscopy, Electron, Scanning; D010006:Osteoblasts / Q000166:cytology / Q000378:metabolism / Q000648:ultrastructure; D011091:Polyesters; D011100:Polyglycolic Acid / Q000737:chemistry; D011108:Polymers / Q000737:chemistry*; D013696:Temperature; D023822:Tissue Engineering / Q000379:methods*; D054457:Tissue Scaffolds / Q000737:chemistry
D000199:Actins; D001672:Biocompatible Materials; D024042:Collagen Type I; D011091:Polyesters; D011108:Polymers; D011100:Polyglycolic Acid; D019344:Lactic Acid; C033616:poly(lactide); D004247:DNA