In situ pH within particle beds of bioactive glasses.
The in vitro behavior of three bioactive glasses with seven particle size distributions was studied by measuring the in situ pH inside the particle beds for 48h in simulated body fluid (SBF). After immersion, the surface of the particles was characterized with a field emission scanning electron microscope equipped with an energy-dispersive X-ray analyzer. In addition, the results were compared with the reactions of the same glasses formed as plates. A similar trend in pH as a function of immersion time was observed for all systems. However, the pH inside the particle beds was markedly higher than that in the bulk SBF of the plates. The pH decreased as power functions with increasing particle size, i.e. with decreasing surface area. The in vitro reactivity expressed as layer formation strongly depended on the particle size and glass composition. The average thickness of the total reaction layer decreased with the increase in sample surface area. Well-developed silica and calcium phosphate layers typically observed on glass plates could be detected only on some particles freely exposed to the solution. No distinct reaction layers were observed on the finest particles, possibly because the layers spread out on the large surface area. Differences in the properties of the bulk SBF and the solution inside the particle bed were negligible for particles larger than 800microm. The results enhance our understanding of the in vitro reactions of bioactive glasses in various product forms and sizes.
Zhang
Di
D
Process Chemistry Centre, Abo Akademi University, Piispankatu 8, FI-20500 Turku, Finland.
Hupa
Mikko
M
Hupa
Leena
L
D001672:Biocompatible Materials / Q000737:chemistry*; D001826:Body Fluids / Q000737:chemistry*; D002516:Ceramics; D005898:Glass / Q000737:chemistry*; D006863:Hydrogen-Ion Concentration; D008422:Materials Testing; D008863:Microspheres; D010316:Particle Size
D001672:Biocompatible Materials; C425330:bioactive glass 45S5; C403922:bioactive glass S53P4