Conductive macroporous composite chitosan-carbon nanotube scaffolds.
Multiwalled carbon nanotubes (MWCNTs) were used as doping material for three-dimensional chitosan scaffolds to develop a highly conductive, porous, and biocompatible composite material. The porous and interconnected structures were formed by the process of thermally induced phase separation followed by freeze-drying applied to an aqueous solution of 1 wt % chitosan acetic acid. The porosity was characterized to be 97% by both mercury intrusion porosimetry measurements and SEM image analysis. When MWCNTs were used as a filler to introduce conductive pathways throughout the chitosan skeleton, the solubilizing hydrophobic and hydrophilic properties of chitosan established stable polymer/MWCNT solutions that yielded a homogeneous distribution of nanotubes throughout the final composite matrix. A percolation theory threshold of approximately 2.5 wt % MWCNTs was determined by measurement of the conductivity as a function of chitosan/MWCNT ratios. The powder resistivity of completely compressed scaffolds also was measured and was found to be similar for all MWCNT concentrations (0.7-0.15 Omega cm powder resistivity for MWCNTs of 0.8-5 wt %) and almost five times lower than the 20 k Omega cm value found for pure chitosan scaffolds.
Lau
Carolin
C
Hawaii Natural Energy Institute, University of Hawaii at Manoa, Manoa, HI 96822, USA.
Cooney
Michael J
MJ
Atanassov
Plamen
P
D048271:Chitosan / Q000737:chemistry*; D004553:Electric Conductivity; D008855:Microscopy, Electron, Scanning; D037742:Nanotubes, Carbon / Q000737:chemistry* / Q000648:ultrastructure*; D016062:Porosity
D037742:Nanotubes, Carbon; D048271:Chitosan