Pyrolysis, crystallization, and sintering of mesostructured titania thin films assessed by in situ thermal ellipsometry.
In-situ thermal ellipsometric analysis is used to elucidate new and fine-scale details on the thermally driven densification, pyrolysis, crystallization, and sintering of dense and ordered mesoporous titania thin films prepared by evaporation-induced self-assembly. The role of the heating schedule, initial film thickness, nature of the substrate and templating agent, solution aging, and presence of water and other additives in the calcination environment is examined. Each of these parameters is shown to have unique and often substantial effects on the final film structure, while the technique itself provides detailed insight into the chemical origin and evolution of these effects. In-situ monitoring and control over the governing chemical processes, such as high-temperature adsorption phenomena that impact nanocrystal growth, is also demonstrated. The evolution of both the porosity and chemical processes occurring inside these materials are evaluated, including extraction of kinetic parameters for the pyrolysis of the template and crystallization of the matrix walls. The latter is shown to be strongly dependent on the presence of mesoscale ordering with ordered cubic films indicating a 1D diffusion-limited crystallization process and dense films following a 3D diffusion-limited process. Less well-ordered mesoporous films, despite similarities in pore volume and pore size distributions, are kinetically more reminiscent of dense films in terms of crystallization. In-situ thermal ellipsometry, by detailing the evolution of the thermally driven chemistry and ceramization that dictate the final film properties, provides immensely important insight into the synthesis and optimization of advanced functional materials based on titania and other metal oxide thin films.
Laboratoire de Chimie de la Matière Condensée de Paris, Université Pierre et Marie Curie-Paris 6 and CNRS, 4 place Jussieu, 75252 Paris 05, France.
John D
JD
Bass
David
D
Grosso
Cédric
C
Boissiere
Clément
C
Sanchez
D003460:Crystallization; D006358:Hot Temperature; D008422:Materials Testing; D016062:Porosity; D013499:Surface Properties; D014025:Titanium / Q000737:chemistry*
C009495:titanium dioxide; D014025:Titanium