[Synthesis and spectral characteristic of Ga-Fe3O4 at room temperature].
Gallium bearing ferrites with different gallium content were synthesized by oxidation of ferrous and gallium ions under alkaline condition and room temperature. The samples were subjected to IR, XRD, Mossbauer spectral analysis and magnetization characterization. The results indicated that the green-rust intermediate phase would be produced during the procedure of Ga-Fe3O4 formation, and the green-rust intermediate phase was converted to ferrites with spinel structure during the drying under hot-N2 atmosphere. With the introduction of gallium into the spinel structure, the interplanar crystal spacing of the spinel structure decreased, as indicated from XRD spectra, and the lattice vibration of M(T)-O-M(o) moved to the high-frequency resulting from IR spectra. A small amount gallium introduction entered the tetrahedral sites preferentially rather than the octahedral sites, and increasing gallium introduction would enhance the occupation of octahedral sites. Furthermore, a small content of gallium in the initial solution could prevent the formation of non-magnetic Fe2O3.
Wang
Jing
J
School of Pharmaceutical Sciences, Hebei Medical University, Shijiazhuang 050017, China. jingwang1972@hotmail.com
Deng
Tong
T
Yang
Cai-Qin
CQ
Lin
Yu-Long
YL
Wang
Wei
W
Wu
Hai-Yan
HY
D052203:Ferrosoferric Oxide / Q000032:analysis* / Q000138:chemical synthesis; D005708:Gallium / Q000737:chemistry*; D008280:Magnetics; D013055:Spectrophotometry, Infrared / Q000379:methods*; D015204:Spectroscopy, Mossbauer / Q000379:methods*; D013696:Temperature; D014961:X-Ray Diffraction / Q000379:methods*
D005708:Gallium; D052203:Ferrosoferric Oxide