p-Type ZnO nanowire arrays.
Well-aligned ZnO nanowire (NW) arrays with durable and reproducible p-type conductivity were synthesized on alpha-sapphire substrates by using N2O as a dopant source via vapor-liquid-solid growth. The nitrogen-doped ZnO NWs are single-crystalline and grown predominantly along the [110] direction, in contrast to the [001] direction of undoped ZnO NWs. Electrical transport measurements reveal that the nondoped ZnO NWs exhibit n-type conductivity, whereas the nitrogen-doped ZnO NWs show compensated highly resistive n-type and finally p-type conductivity upon increasing N2O ratio in the reaction atmosphere. The electrical properties of p-type ZnO NWs are stable and reproducible with a hole concentration of (1-2) x 10(18) cm(-3) and a field-effect mobility of 10-17 cm2 V(-2) s(-1). Surface adsorptions have a significant effect on the transport properties of NWs. Temperature-dependent PL spectra of N-doped ZnO NWs show acceptor-bound-exciton emission, which corroborates the p-type conductivity. The realization of p-type ZnO NWs with durable and controlled transport properties is important for fabrication of nanoscale electronic and optoelectronic devices.
Yuan
G D
GD
Centre Of Super-Diamond and Advanced Films (COSDAF), City University of Hong Kong, Hong Kong SAR, People's Republic of China.
Zhang
W J
WJ
Jie
J S
JS
Fan
X
X
Zapien
J A
JA
Leung
Y H
YH
Luo
L B
LB
Wang
P F
PF
Lee
C S
CS
Lee
S T
ST