Synthesis of PbTe nanowire arrays using lithographically patterned nanowire electrodeposition.
We describe the preparation by electrodeposition of arrays of lead telluride (PbTe) nanowires using the lithographically patterned nanowire electrodeposition (LPNE) method. PbTe nanowires had a rectangular cross-section with adjustable width and height ranging between 60-400 nm (w) and 20-100 nm (h). The characterization of these nanowire arrays using X-ray diffraction, transmission electron microscopy and electron diffraction, scanning electron microscopy, atomic force microscopy, and X-ray photoelectron spectroscopy (XPS) is reported. PbTe nanowires were electrodeposited using a cyclic electrodeposition-stripping technique that produced polycrystalline, stoichiometric, face-centered cubic PbTe with a mean grain diameter of 10-20 nm. These nanowires were more than 1 mm in length and two additional processing steps permitted their suspension across 25 microm air gaps microfabricated on these surfaces. The LPNE synthesis of lithographically patterned PbTe nanowires was carried out in unfiltered laboratory air. Nanowires with lengths of 70-100 microm showed an electrical resistivity comparable to bulk PbTe. XPS reveals that exposure of PbTe nanowires to air causes the formation on the nanowire surface of approximately one monolayer of a mixed lead oxide and tellurium oxide within a few minutes.
Yang
Y
Y
Department of Chemistry and Institute for Surface and Interface Science (ISIS), University of California, Irvine, California 92697-2025, USA.
Kung
S C
SC
Taggart
D K
DK
Xiang
C
C
Yang
F
F
Brown
M A
MA
Güell
A G
AG
Kruse
T J
TJ
Hemminger
J C
JC
Penner
R M
RM