A morphology-related study on photodegradation of protein fibres.
The wool fibre has a complex morphology, consisting of an outer layer of cuticle scales surrounding an inner cortex. These two components are hard to separate effectively except by using harsh chemical treatments, making it difficult to determine the susceptibility of the different components of the fibre to photoyellowing. An approach to this problem based on mechanical fibre modification is described. To expose the inner cortex of wool to different degrees, clean wool fibres were converted into 'powders' of various fineness via mechanical chopping, air-jet milling, ball milling or their combination. Four types of powdered wool (samples A, B, C and D) were produced with reducing particle size distributions and an increasing level of surface damage as observed using SEM. Sample A contained essentially intact short fibre snippets and sample D contained a large amount of exposed cortical materials. Samples B and C contained a mixture of short fibre snippets and cortical materials. Solid wool discs were then compressed from the corresponding powder samples in a polished stainless steel die to enable colour measurement and UV irradiation studies. ATR-FTIR studies on powder discs demonstrated a small shift in the amide I band from 1644cm(-1) for disc A to 1654cm(-1) for disc D due to the different structures of the wool cuticle and cortex, in agreement with previous studies. Similarly an increase in the intensity ratio of the amide I to amide II band (1540cm(-1)) was observed for disc D, which contains a higher fraction of cortical material at the surface of the disc. Discs prepared from sample D appeared the lightest in colour before exposure and had the slowest photoyellowing rate, whereas discs made from powders A-C with a higher level of cuticle coverage were more yellow before exposure and experienced a faster rate of photoyellowing. This suggests that the yellow chromophores of wool may be more prevalent in cuticle scales, and that wool photoyellowing occurs to a greater extent in the cuticle than in the cortex. Photo-induced chemiluminescence measurements showed that sample D had a higher chemiluminescence intensity after exposure to UVA radiation and a faster decay rate than samples A and B. Thus one of the roles of the wool cuticle may be to protect the cortex by quenching of free radical oxidation during exposure to the UV wavelengths present in sunlight.
Zhang
Hu
H
Centre for Material and Fibre Innovation, Deakin University, Geelong VIC 3217, Australia. hzha@deakin.edu.au
Millington
Keith R
KR
Wang
Xungai
X
D000818:Animals; D003116:Color; D049449:Luminescence; D008855:Microscopy, Electron, Scanning; D010316:Particle Size; D010777:Photochemistry; D011506:Proteins / Q000737:chemistry / Q000528:radiation effects* / Q000648:ultrastructure; D012756:Sheep; D017550:Spectroscopy, Fourier Transform Infrared; D014466:Ultraviolet Rays; D014935:Wool / Q000737:chemistry / Q000528:radiation effects* / Q000648:ultrastructure
D011506:Proteins