Enhancement at the junction of silver nanorods.
The enhancement of surface enhanced Raman scattering (SERS) at the junction of linearly joined silver nanorods (31 nm in diameter) deposited in the pores of anodic aluminum oxide templates was studied systematically by excitation with a 632.8 nm laser line. The single and joined silver nanorod arrays showed a similar extinction spectrum when their length was the same. Maximum enhancement was observed from the junction system of two nanorods of the same size with a total length of 62 nm. This length also corresponded to the optimum length of single nanorods for SERS by excitation with a 632.8 nm laser line. The enhancement at the junction was approximately 40 times higher than that of the 31 nm single nanorod, while it was 4 times higher than that of the 62 nm single nanorod. The enhancement factor at the junction after oxide removal was approximately 3.9 x 10 (9).
Gu
Geun Hoi
GH
Nanomaterials Laboratory, Department of Chemistry, Seoul National University, Kwanak-ro 599, Kwanak-gu, Seoul, Republic of Korea.
Suh
Jung Sang
JS
D053768:Metal Nanoparticles / Q000737:chemistry*; D008855:Microscopy, Electron, Scanning; D043942:Nanotubes / Q000737:chemistry* / Q000648:ultrastructure; D012834:Silver / Q000737:chemistry*; D013057:Spectrum Analysis
D012834:Silver