Solvent-induced porosity in ultrathin amine plasma polymer coatings.
Plasma polymers deposited from n-heptylamine onto silicon wafers have been found to form a porous microstructure when immersed in water and other solvents, with pores of dimensions and densities that vary considerably between coatings deposited under different plasma conditions. This solvent-induced pore formation was found to correlate with the observed percentage of extractable material. With low radio frequency (rf) power inputs, the resultant softer coatings possess considerably more extractable material than coatings deposited at higher applied power levels. The porosity is thus proposed to result from the formation of voids created by the extraction of soluble low-molecular-weight polymeric material, which produces shrinkage stress that the coating, firmly attached to the substrate, cannot relieve by macroscopic contraction. The microscopic contraction of plasma polymer volume creates voids that appear to span the entire film thickness. The effect of aging plasma polymers in air was also investigated. For films deposited at low power it led to reduced extraction of soluble material and different pore morphology, whereas for films deposited at higher rf power levels, the extracted amounts and pore formation were the same for aged coatings. It was also found that the density of surface amine groups was lower for films deposited under the two lowest power settings, in contrast to the commonly held belief that the use of minimal applied rf power aids retention of functional groups. These porous plasma polymer coatings with surface groups suitable for further interfacial chemical immobilization reactions may be useful for various membrane and biotechnology applications.
Vasilev
Krasimir
K
Ian Wark Research Institute, University of South Australia, Mawson Lakes, SA 5095, Adelaide, Australia. Krasimir.Vasilev@unisa.edu.au
Britcher
Leanne
L
Casanal
Ana
A
Griesser
Hans J
HJ