Architecture of linear arrays of fluorinated co-oligomeric nanocomposite-encapsulated gold nanoparticles: a new approach to the development of gold nanoparticles possessing an extremely red-shifted absorption characteristic.
Fluoroalkyl end-capped co-oligomeric nanoparticles, which were prepared by the reaction of fluoroalkanoyl peroxide with 2-acrylamido-2-methylpropanesulfonic acid (AMPS) and 1-hydroxy-5-adamantylacrylate (Ad-HAc), were applied to the preparation of novel fluorinated co-oligomeric nanocomposite-encapsulated gold nanoparticles. These fluorinated gold nanocomposites were easily prepared by the reductions of gold ions with poly(methylhydrosiloxane) (PMHS) in the presence of the corresponding fluorinated nanoparticles and tri -n-octylamine (TOA) in 1,2-dichloroethane (DE) at room temperature. These fluorinated gold nanoparticles were isolated as wine-red powders and were found to exhibit good dispersibility in a variety of traditional organic solvents such as DE, methanol, and t-butyl alcohol to afford transparent wine-red solutions. The morphology and stability of these fluorinated co-oligomeic nanocomposite-encapsulated gold nanoparticles were characterized using transmission electron microscopy (TEM), dynamic light scattering measurements (DLS), and UV-vis spectroscopy. DLS measurements and UV-vis spectroscopy showed that these particles are nanometer-size-controlled very fine nanoparticles (185-218 nm) that exhibit a plasmon absorption band at around 530 nm. TEM images also showed that gold nanoparticles are tightly encapsulated into fluorinated co-oligomeric nanoparticle cores. Interestingly, these fluorinated co-oligomeric nanocomposites-encapsulated gold nanoparticles were found to afford linear arrays of these fluorinated nanoparticles with increases in the feed amounts of TOA. More interestingly, these fluorinated gold nanoparticles were able to afford the extremely red-shifted plasmon absorption band at around 960 nm.
Mugisawa
Masaki
M
Department of Frontier Materials Chemistry, Graduate School of Science and Technology, Hirosaki University, Hirosaki 036-8561, Japan.
Sawada
Hideo
H