title: [Test of carotid artery replacement by polyurethane artificial vascular graft with recombinant fibrinolytic enzyme factor II-modified lumina in dogs].
abstract: OBJECTIVE
  To evaluate the implantation effect of artificial vascular grafts with recombinant fibrinolytic enzyme factor II (rF II)-immobilized lumina in animal test.
  
  
  METHODS
  Four mm internal diameter (ID) polyurethane (PU) artificial vascular grafts were prepared by dipping and leaching method. The micro-pore size and morphology of the graft walls were observed by SEM. The graft lumina were immobilized with rF II. Twenty hybrid male dogs [weighing (20 +/- 1) kg] were used for animal model of carotid artery defect and were randomly divided into 3 groups: rF II -immobilized PU group, no rF II -immobilized PU group and expanded polytetrafluoroethylene (ePTFE) group. The vascular grafts were implanted for repairing injured segments of carotid artery in dogs. The general health state of animals was recorded. At 30 days and 60 days, the patency rate of every group was calculated. At 60 days IDs were measured, cell proliferation in neointima was inspected by light microscope, morphology on neointima was observed by SEM.
  
  
  RESULTS
  The ID of the PU vascular grafts was (3.74 +/- 0.06) mm, wall thickness was 0.4-0.6 mm, the wall density was 0.25 g/cm3, the porosity was 79.8%, racial compliance was 8.57%/100 mmHg. In the wall, micropores were well distributed and opened-pores structure was observed. Pore size was (140 +/- 41) microm in the outside layer, pore size was (100 +/- 3) microm in the inside layer, thickness ratio of outside / inside layers was 2 : 1, the pore size was (40 +/- 16) microm on the lumina surface. After operation the wounds on neck healed, all the animals survived and had no complication. At 30 days and 60 days after implantation, the patency rate for rF II -immobilized PU group were 100% and 66.7%, for no rF II -immobilized PU group were 66.7% and 33.3%, and for ePTFE group were 67.7% and 0 respectively, but at 60 days there were thrombosis at anastomotic sites of some grafts occluded. Before operation the IDs for rF II-immobilized PU group, no rF II -immobilized PU group and ePTFE group were (3.74 +/- 0.06), (3.74 +/- 0.06) and (4.00 +/- 0.03) mm, at 60 days after operation the IDs were (4.51 +/- 0.05), (4.31 +/- 0.24) and (4.43 +/- 0.12) mm respectively, showing no statistically significant differences between 3 groups (P > 0.05). Histological inspection indicated that at 15 days a layer of plasma protein deposited on the lumina, at 30 days some cells adhered to the lumina, at 60 days neointima could be observed on the lumina. Thickness of the neointima became larger with implantation time. At 60 days neointima thickness at proximal end, middle site and distal end of graft were (560 +/- 22), (78 +/- 5) and (323 +/- 31) microm respectively for rF II -immobilized PU group. The results of SEM showed that neointima surface consisted of flat and long cells which long axes ranged with blood flow direction and was similar to lumina morphology of carotid artery of dog.
  
  
  CONCLUSIONS
  Immobilization of rF II to lumina of grafts could enhance fibrinolytic activity and inhibited formation of thrombo-embolic which led to an increase in patency rate after implantation.
authors.affiliation: Department of Cardiovasology, the First Affiliated Hospital, Sun Yet-Sen University, Guangzhou Guangdong, 510080, PR China. gzpshr@163.com
authors.forename: Shirong
authors.initials: S
authors.lastname: Pan
authors.forename: Shengli
authors.initials: S
authors.lastname: Yin
authors.forename: Jianping
authors.initials: J
authors.lastname: Yao
authors.forename: Huanling
authors.initials: H
authors.lastname: Zheng
authors.forename: Wu
authors.initials: W
authors.lastname: Yi
authors.forename: Gang
authors.initials: G
authors.lastname: Dai
mesh_terms: D000818:Animals; D001807:Blood Vessel Prosthesis; D019917:Blood Vessel Prosthesis Implantation; D002339:Carotid Arteries / Q000601:surgery*; D003435:Crotalid Venoms; D004285:Dogs; D008297:Male; D011140:Polyurethanes; D011474:Prosthesis Design; D011516:Prothrombin; D011994:Recombinant Proteins
chemical_list: D003435:Crotalid Venoms; D011140:Polyurethanes; D011994:Recombinant Proteins; D011516:Prothrombin