[Study of the polyvinyl alcohol-collagen blend as wound dressing].
This study sought to explore a new compound polyvinyl alcohol-collagen as a wound dressing. To make the polymer, Polyvinyl alcohol (PVA) and collagen type I were put together in the ratio of 3:1, at the same time, polyethlene glycol as porogen was added, and the material was dried by air to be a membrane in shape. Then the ultimate tensile load, the hole diameter, porosity, and water absorption were measured. The cell biocompatibility was tested as well. The results showed the PVA-collagen blend had the average hole 100-150 microm in diameter, and the porosity about 90%. The ultimate tensile load reached 8.10 +/- 0.28 MPa, and water absorption was up to 185.42% +/- 6.93%. 3T3 cells grew well on the PVA-collagen member. Therefore, the PVA-collagen memberane is characterized not only by its ideal biomechanical ability and biocompability, but also by its ideal hole diameter, porosity and water absorption. It may have the potential for use as a wound dressing in vivo.
Ye
Chunting
C
Guangzhou Red Cross Hospital, The Affiliate of the Medical School of Jinan University, Guangzhou, 510220, China.
Chen
Honghui
H
Zou
Haiyan
H
Pan
Zhengjun
Z
Peng
Yanhao
Y
D001672:Biocompatible Materials / Q000138:chemical synthesis* / Q000737:chemistry; D003094:Collagen / Q000737:chemistry*; D006801:Humans; D009779:Occlusive Dressings; D011142:Polyvinyl Alcohol / Q000737:chemistry*
D001672:Biocompatible Materials; D011142:Polyvinyl Alcohol; D003094:Collagen