Transmission electron microscopy study of solvent-induced phase morphologies of environmentally responsive mixed homopolymer brushes on silica particles.
We report in this work a transmission electron microscopy study of phase morphologies of environmentally responsive mixed poly( t-butyl acrylate) (P tBA)/polystyrene (PS) brushes and mixed poly(acrylic acid) (PAA)/PS brushes on 180 nm silica particles after treatments with nonselective good solvents and selective solvents, respectively. Mixed P tBA/PS brushes were grown from Y-initiator-functionalized silica particles by sequential atom transfer radical polymerization and nitroxide-mediated radical polymerization. Mixed PAA/PS brushes were prepared from mixed P tBA/PS brushes by removal of the t-butyl groups. For mixed P tBA/PS brushes with P tBA M n of 24.2 kDa and PS M n of 23.0 kDa and the corresponding mixed PAA/PS brushes, random worm-like, nearly bicontinuous nanostructures were formed from lateral microphase separation when the particles were cast from nonselective good solvents (chloroform for mixed P tBA/PS brushes and N, N-dimethylformamide for mixed PAA/PS brushes). The feature sizes were on the order of polymer chain root-mean-square end-to-end distances ( approximately 10 nm). In contrast, mixed P tBA/PS brushes with lower molecular weights (P tBA M n = 10.4 kDa and PS M n = 11.9 kDa) did not strongly phase separate after being cast from chloroform. After the solvents in the particle dispersions were gradually changed to selective solvents ( n-octane for mixed P tBA/PS brushes and H2O for mixed PAA/PS brushes), isolated microdomains with an average size of 14-19 nm were formed as one grafted polymer collapsed and associated to form isolated microdomains, which were shielded by another grafted polymer yielding surface-tethered micellar structures. These results confirmed the theoretical predictions of the formation of "rippled" nanostructures and surface micellar structures of mixed homopolymer brushes induced by nonselective and selective solvents, respectively.
Zhu
Lei
L
Polymer Program, Institute of Materials Science and Department of Chemical, Materials and Biomolecular Engineering, University of Connecticut, Storrs, Connecticut 06269, USA. lei.zhu@uconn.edu
Zhao
Bin
B