Evaluation of flowable resin composite surfaces eroded by acidic and alcoholic drinks.
The purpose of this study was to evaluate the morphological changes of the surfaces of flowable resins eroded by orange juice and alcohol drinks. The tested products were Beautifil Flow BF02 and BF10, Clearfil Majesty LV, Filtek Supreme XT Flowable Restorative, Unifil LoFlo Plus and Filtek Supreme. Filler percentages of flowable resins were calculated after the latter were incinerated at 750 degrees C. Specimens were shaped into a disk form with a diameter of 10 mm and a thickness of 1 mm. Morphological changes were evaluated for the following types of flowable resin surfaces: polished surface, surfaces eroded by 100% orange juice, wine and whisky. Filler percentages of the tested flowable resins ranged between 42 and 78%. Surface degradation was observed for the specimens immersed in acidic and alcoholic drinks, and it was thought that the lower the filler percentage, the greater was the surface degradation. Decomposition of the matrix resin and fallout of the fillers were observed in flowable resins that eroded with acidic and alcoholic drinks.
Han
Linlin
L
Division of Cariology, Operative Dentistry and Endodontics, Department of Oral Health Science, Niigata University Graduate School of Medical and Dental Sciences, 5274 Gakkocho-dori, 2-bancho, Chuo-ku, Niigata 951-8514, Japan. han4378@yahoo.co.jp
Okamoto
Akira
A
Fukushima
Masayoshi
M
Okiji
Takashi
T
D000434:Alcoholic Beverages; D001628:Beverages; D017438:Bisphenol A-Glycidyl Methacrylate / Q000737:chemistry; D032084:Citrus sinensis; D003188:Composite Resins / Q000737:chemistry*; D003764:Dental Materials / Q000737:chemistry*; D003775:Dental Polishing; D005638:Fruit; D006801:Humans; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D011109:Polymethacrylic Acids / Q000737:chemistry; D013499:Surface Properties; D014920:Wine
C470433:Beautifil composite resin; D003188:Composite Resins; D003764:Dental Materials; C467913:Filtek Flow; C474035:Filtek Supreme; D011109:Polymethacrylic Acids; C501418:Unifil LoFlo Plus; C111840:flowable hybrid composite; D017438:Bisphenol A-Glycidyl Methacrylate