title: Effect of zirconia surface treatments on the shear strength of zirconia/veneering ceramic composites.
abstract: Aim of the investigation was to assess the effect of different surface treatments on the bond strength of veneering ceramics to zirconia. In a shear test, the influences of polishing, sandblasting, and silica-coating of the zirconia surface on bonding were assessed with five different veneering ceramics. In addition the effect of liner application was examined. With one veneering ceramic, the impact of regeneration firing of zirconia was also evaluated. Statistical analysis was performed with one-way ANOVA and post hoc Scheffé's test. Failure in every case occurred in the veneering ceramic adjacent to the interface with a thin layer of ceramic remaining on the zirconia surface, indicating that bond strength was higher than the cohesive strength of the veneering ceramic. Shear strength ranged from 23.5 +/- 3.4 MPa to 33.0 +/- 6.8 MPa without explicit correlation to the respective surface treatment. Regeneration firing significantly decreased the shear strength of both polished and sandblasted surfaces. Findings of this study revealed that bonding between veneering ceramics and zirconia might be based on chemical bonds. On this note, sandblasting was not a necessary surface pretreatment to enhance bond strength and that regeneration firing was not recommended.
authors: Clinic for Fixed and Removable Prosthodontics and Dental Materials Science, University of Zurich, Plattenstrasse 11, CH-8032 Zurich, Switzerland. jens.fischer@zzmk.uzh.ch
authors: Jens
authors: J
authors: Fischer
authors: Philipp
authors: P
authors: Grohmann
authors: Bogna
authors: B
authors: Stawarczyk
mesh_terms: D000537:Aluminum Oxide / Q000737:chemistry; D001840:Dental Bonding; D003738:Dental Cements / Q000737:chemistry; D045662:Dental Etching / Q000379:methods; D003764:Dental Materials / Q000737:chemistry*; D003775:Dental Polishing / Q000379:methods; D003776:Dental Porcelain / Q000737:chemistry*; D003801:Dental Veneers; D006358:Hot Temperature; D006801:Humans; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D033081:Shear Strength; D012822:Silicon Dioxide / Q000737:chemistry; D013314:Stress, Mechanical; D013499:Surface Properties; D015019:Yttrium / Q000737:chemistry; D015040:Zirconium / Q000737:chemistry*
chemical_list: D003738:Dental Cements; D003764:Dental Materials; C520133:IPS e.max CAD LT; C076811:Rocatec; C096474:Vintage Porcelain; C499362:yttria stabilized tetragonal zirconia; D003776:Dental Porcelain; D015019:Yttrium; D012822:Silicon Dioxide; D015040:Zirconium; D000537:Aluminum Oxide; C028541:zirconium oxide