Ion-beam-induced collective rotation of nanocrystals.
Vapor-deposited nanocrystalline titanium layers have been irradiated at room temperature with 350-MeV-Au ions up to 4x10;{15} Au/cm;{2}. Bombardment-induced texture changes were determined at the BESSY synchrotron light source. During off-normal irradiation, the nanocrystals undergo grain alignment and rotation up to approximately 90 degrees at the highest ion fluence. At the same time, the whole layer exhibits shear flow very similar to that observed previously in amorphous materials. Below 1x10;{15} Au/cm;{2}, a reversal of the ion incidence angle leads to a back rotation of the grains. These effects are absent or immeasurably small in coarse-grained titanium but have also been found in nanocrystalline TiN and NiO. The observations can be modeled by assuming that grain boundaries behave during ion bombardment like amorphous matter or by assuming a generation of disclination dipoles moving along grain boundaries.
Zizak
Ivo
I
Berliner Elektronenspeicherring-Gesellschaft für Synchrotronstrahlung mbH, Albert-Einstein-Strasse 15, 12489 Berlin, Germany. ivo.zizak@bessy.de
Darowski
Nora
N
Klaumünzer
Siegfried
S
Schumacher
Gerhard
G
Gerlach
Jürgen W
JW
Assmann
Walter
W