Shear bond strength of four resin cements used to lute ceramic core material to human dentin.
OBJECTIVE
This study evaluated the effect of four resin cements on the shear bond strength of a ceramic core material to dentin.


METHODS
One hundred twenty molar teeth were embedded in a self-curing acrylic resin. The occlusal third of the crowns were sectioned under water cooling. All specimens were randomly divided into four groups of 30 teeth each according to the resin cement used. One hundred twenty cylindrical-shaped, 2.7-mm wide, 3-mm high ceramic core materials were heat-pressed. The core cylinders were then luted with one of the four resin systems to dentin (Super-Bond C&B, Chemiace II, Variolink II, and Panavia F). Half of the specimens (n = 15) were tested after 24 hours; the other half (n = 15) were stored in distilled water at 37 degrees C for 1 day and then thermocycled 1000 times between 5 degrees C and 55 degrees C prior to testing. Shear bond strength of each specimen was measured using a universal testing machine at a crosshead speed of 1 mm/min. The bond strength values were calculated in MPa, and the results were statistically analyzed using a two-way analysis of variance (ANOVA) and Tukey HSD tests.


RESULTS
The shear bond strength varied significantly depending on the resin cement used (p < 0.05). The differences in the bond strengths after thermocycling were not remarkable as compared with the corresponding prethermal cycling groups (p > 0.05). Significant interactions were present between resin cement and thermocycling (p < 0.05). After 24 hours, the specimens luted with Variolink II (5.3 +/- 2.2 MPa) showed the highest shear bond strength, whereas the specimens luted with Chemiace II (1.6 +/- 0.4 MPa) showed the lowest. After thermocycling, the bond strength values of specimens luted with Chemiace II (1.1 +/- 0.1 MPa) and Super-Bond C&B (1.7 +/- 0.4 MPa) decreased; however, this was not statistically significant (p > 0.05). The increase in the shear bond strength values in the Panavia F (4.5 +/- 0.7 MPa) and Variolink II (5.5 +/- 2.1 MPa) groups after thermocycling was also not statistically significant (p > 0.05).


CONCLUSIONS
Variolink II and Panavia F systems showed higher shear bond strength values than Chemiace II and Super-Bond C&B. They can be recommended for luting ceramic cores to dentin surfaces.