title: [Preparation of Cu/ZrO2/S2O8(2-)/gamma-Al2O3 solid acid catalyst and its catalytic activity to selective reduction of NO].
abstract: Cu/ZrO2/S2O8(2-)/gamma-Al2O3 solid acid catalyst was prepared by loading of (NH4)2S2O8, ZrOCl2, and Cu(NO3)2 onto gamma-Al2O3 step by step, which was obtained from calcining of pseudoboehmite. The catalytic property of Cu/ZrO2/S2O8(2-)/gamma-Al2O3 on the selective reduction of NO by C3H6 in excess oxygen was investigated. The relationship between the structure and the catalytic property of Cu/ZrO2/S2O8(2-)/gamma-Al2O3 catalyst was also explored by means of SEM, XRD, Py-IR and TPR. The experimental results of catalytic activity of the title catalyst indicated that the maximum conversion rate of NO could reach 82.9% in the absence of water and was up to 80.2% even in the presence of 10% water vapor. The results of the structural characterization toward the catalyst showed that S2O8(2-) and ZrO2 could restrain the sinteration of gamma-Al2O3 particles and the formation of CuAl2O4 spinelle, and also facilitate the formation of new acidic sites (Brönsted acid) and the enhance of the acidity on the surface of the catalyst. In addition, ZrO2 could increase the reducibility of Cu on the catalyst. Consequently, the catalytic activity and hydrothermal stability of the catalyst were improved effectively.
authors.affiliation: Department of Chemistry, Shantou University, Shantou 515063, China. xkguo@stu.edu.cn
authors.forename: Xi-kun
authors.initials: XK
authors.lastname: Guo
authors.forename: Xiao-ming
authors.initials: XM
authors.lastname: Wang