The effects of tooth preparation cleansing protocols on the bond strength of self-adhesive resin luting cement to contaminated dentin.
This in vitro study evaluated the bond strength of a self-adhesive luting cement after using four different techniques to remove surface contamination on dentin. Extracted human molars were flattened to expose the dentin surface and prepared for full crown preparation. Acrylic temporary crowns were fabricated and placed using temporary cement. The specimens were stored at room temperature with 100% relative humidity for seven days. Following removal of the temporary crowns, the specimens were randomly divided into four groups, and excess provisional cement was removed with (1) a hand instrument (excavator), (2) prophy with a mixture of flour pumice and water (3) aluminous oxide abrasion with a particle size of 27 microm at 40 psi and (4) aluminous oxide abrasion with a particle size of 50 microm at 40 psi. The microstructure morphology of the tooth surface was evaluated and residual materials were detected using SEM and EDS analysis of randomly selected specimens. The ceramics were treated with 9.5% hydrofluoric acid-etch and silanized to the prepared dentin prior to cementing with self-adhesive resin cement (RelyX Unicem, 3M ESPE). The shear bond strength was determined at a crosshead speed of 0.5 mm/minute. The results were analyzed with one-way ANOVA, followed by Tukey's test. Particle abrasion treatment of dentin with an aluminous oxide particle provided the highest values of bond strength, while hand instrument excavation was the lowest (p < 0.05). Aluminous oxide particle size did not significantly influence the bond strength at 40 psi. The use of low pressure and small particle abrasion treated dentin as a mechanical cleansing protocol prior to definitive cementation increased the bond strength of self-adhesive resin-luting cement to dentin following eugenol-containing temporary cement.
Chaiyabutr
Yada
Y
Department of Restorative Dentistry, University of Washington, Kois Center, Seattle, WA, USA. yada@koiscenter.com
Kois
John C
JC
D000134:Acid Etching, Dental; D020906:Air Abrasion, Dental / Q000379:methods; D000537:Aluminum Oxide / Q000737:chemistry; D003442:Crowns; D001840:Dental Bonding; D017005:Dental Debonding / Q000295:instrumentation / Q000379:methods; D003794:Dental Restoration, Temporary; D003804:Dentin / Q000648:ultrastructure*; D004577:Electron Probe Microanalysis; D005054:Eugenol / Q000737:chemistry; D006801:Humans; D006813:Humidity; D008855:Microscopy, Electron, Scanning; D010316:Particle Size; D019279:Resin Cements / Q000737:chemistry*; D033081:Shear Strength; D012821:Silanes / Q000737:chemistry; D013314:Stress, Mechanical; D013696:Temperature; D013997:Time Factors; D019246:Tooth Preparation / Q000379:methods*; D019231:Tooth Preparation, Prosthodontic; D015034:Zinc Oxide / Q000737:chemistry; D015035:Zinc Oxide-Eugenol Cement / Q000737:chemistry
C483701:Rely X Unicem; D019279:Resin Cements; D012821:Silanes; D015035:Zinc Oxide-Eugenol Cement; D005054:Eugenol; C076899:Temp-Bond; D000537:Aluminum Oxide; D015034:Zinc Oxide