Corrosion-related changes on Ti-based orthodontic brackets in acetic NaF solutions: surface morphology, microhardness, and element release.
This study sought to investigate the effects of acetic NaF solutions on titanium and Ti alloy brackets. To this end, two different brackets were immersed in various NaF-containing solutions for three days. The Equilibrium Ti (EQ) bracket was composed of Ti only, whereas the Ortho 2 (OR) bracket was composed of Ti (base) and Ti-6A1-4V (wings). Brackets that were immersed in the acetic NaF solution of pH 3.5 yielded no reliable surface microhardness values due to corrosion. In other test solutions, however, there was minimal reduction (at best 3%) in microhardness. Further on microhardness, the values of the OR bracket at the base and wings were different. On the release of elements, it was significant only in the acetic NaF solution of pH 3.5. However, the release of Al (6.11+/-0.93 ppm) and V (1.16+/-0.40 ppm) in this solution was low. In conclusion, an acetic NaF solution of low pH could damage Ti-based orthodontic brackets.
Kang
Eun-Hee
EH
Department of Orthodontics, College of Dentistry, Pusan National University, Busan, Korea.
Park
Soo-Byung
SB
Kim
Hyung-Il
HI
Kwon
Yong Hoon
YH
D019342:Acetic Acid / Q000737:chemistry; D000497:Alloys; D003343:Corrosion; D003722:Dental Alloys / Q000737:chemistry*; D006244:Hardness; D006863:Hydrogen-Ion Concentration; D008422:Materials Testing; D016382:Orthodontic Appliance Design; D016910:Orthodontic Brackets; D012969:Sodium Fluoride / Q000737:chemistry; D013499:Surface Properties; D014025:Titanium / Q000737:chemistry*
D000497:Alloys; D003722:Dental Alloys; C031462:titanium alloy (TiAl6V4); D012969:Sodium Fluoride; D014025:Titanium; D019342:Acetic Acid