Frequency dependence of viscoelastic properties of medical grade silicones.
Cylinders of medical grade silicone elastomers, (29 mm in diameter and 13 mm thick), immersed in physiological saline solution at 37 degrees C, were investigated by dynamic mechanical analysis (DMA). A sinusoidal cyclic compression of 40 +/- 5 N was applied over a frequency range, f, of 0.02-100 Hz. Values of the storage, E', and loss, E'', moduli for the cylinders were found to depend on f; the dependence of E' or E'' on the logarithm (base 10) of f was represented by a third-order polynomial. Above about 0.3 Hz, the cylindrical specimens appeared to be undergoing the onset of a transition from the rubbery to the glassy state. There was no significant difference between results obtained at 37 and 23 degrees C; pretreatment of specimens in physiological saline at 37 degrees C for 24 h and 29 days had no appreciable effect on the results.
Mahomed
A
A
School of Mechanical Engineering, University of Birmingham, Edgbaston, Birmingham, United Kingdom. axm503@bham.ac.uk
Chidi
N M
NM
Hukins
D W L
DW
Kukureka
S N
SN
Shepherd
D E T
DE
D001672:Biocompatible Materials / Q000737:chemistry*; D004548:Elasticity; D006801:Humans; D008422:Materials Testing; D019736:Prostheses and Implants; D033081:Shear Strength; D012826:Silicone Elastomers / Q000737:chemistry*; D013718:Tensile Strength; D055682:Viscoelastic Substances / Q000737:chemistry*
D001672:Biocompatible Materials; D012826:Silicone Elastomers; D055682:Viscoelastic Substances