The effects of light intensity and light-curing time on the degree of polymerization of dental composite resins.
The aim of this study was to investigate the effects of light intensity and light-curing time on the polymerization of composite resins. Four composite resins were light-cured with different light-curing conditions. In the non-thermocycled case, specimens showed almost the same or similar microhardness values if energy density was identical or similar. As the energy density decreased, maximum polymerization shrinkage decreased. At higher energy densities, specimens had a lower coefficient of thermal expansion than at lower energy densities. At the same or similar energy density, most resin products showed coefficient values which were not statistically different. After 10,000 thermocycles, specimens showed decreases of 2.4-16.5% and 4.6-25.2% in microhardness and coefficient of thermal expansion respectively. Within the limitations of the present study, it was found that light-curing composite resins with higher energy density was beneficial to acquiring higher microhardness values and lower coefficients of thermal expansion.
Baek
Chang-Jun
CJ
Department of Dental Materials, College of Dentistry and Medical Research Institute, Pusan National University, Busan 602-739, Korea.
Hyun
Seok-Hee
SH
Lee
Sang-Kyu
SK
Seol
Hyo-Joung
HJ
Kim
Hyung-Il
HI
Kwon
Yong Hoon
YH
D000704:Analysis of Variance; D003188:Composite Resins / Q000737:chemistry / Q000528:radiation effects*; D055117:Curing Lights, Dental; D001840:Dental Bonding / Q000295:instrumentation*; D003793:Dental Restoration, Permanent / Q000295:instrumentation; D004307:Dose-Response Relationship, Radiation; D006244:Hardness / Q000528:radiation effects; D008422:Materials Testing; D010777:Photochemistry; D011108:Polymers / Q000737:chemistry / Q000528:radiation effects; D013814:Thermal Conductivity; D013997:Time Factors
D003188:Composite Resins; D011108:Polymers