Electrochemical degradation of polycyclic aromatic hydrocarbons in creosote solution using ruthenium oxide on titanium expanded mesh anode.
In this study, expanded titanium (Ti) covered with ruthenium oxide (RuO(2)) electrode was used to anodically oxidize polycyclic aromatic hydrocarbons (PAH) in creosote solution. Synthetic creosote-oily solution (COS) was prepared with distilled water and a commercial creosote solution in the presence of an amphoteric surfactant; Cocamidopropylhydroxysultaine (CAS). Electrolysis was carried out using a parallelepipedic electrolytic 1.5-L cell containing five anodes (Ti/RuO(2)) and five cathodes (stainless steel, 316 L) alternated in the electrode pack. The effects of initial pH, temperature, retention time, supporting electrolyte, current density and initial PAH concentration on the process performance were examined. Experimental results revealed that a current density of 9.23 mA cm(-2) was beneficial for PAH oxidation. The sum of PAH concentrations for 16 PAHs could be optimally diminished up to 80-82% while imposing a residence time in the electrolysis cell of 90 min. There was not a significant effect of the electrolyte (Na(2)SO(4)) concentration on oxidation efficiency in the investigated range of 500-4000 mg/L. However, an addition of 500 mg Na(2)SO(4)L(-1) was required to reduce the energy consumption and the treatment cost. Besides, there was no effect of initial PAH concentration on oxidation efficiency in the investigated range of 270-540 mg PAHL(-1). Alkaline media was not favourable for PAH oxidation, whereas high performance of PAH degradation could be recorded without initial pH adjustment (original pH around 6.0). Likewise, under optimal conditions, 84% of petroleum hydrocarbon (C(10)-C(50)) was removed, whereas removal yields of 69% and 62% have been measured for O&G and COD, respectively. Microtox and Daphnia biotests showed that electrochemical oxidation using Ti/RuO(2) could be efficiently used to reduce more than 90% of the COS toxicity.
Tran
Lan-Huong
LH
Institut National de la Recherche Scientifique, Centre Eau Terre et Environnement, Université du Québec, Québec, Canada.
Drogui
Patrick
P
Mercier
Guy
G
Blais
Jean-François
JF
D003407:Creosote / Q000737:chemistry*; D004566:Electrodes; D004572:Electrolysis; D006863:Hydrogen-Ion Concentration; D011084:Polycyclic Aromatic Hydrocarbons / Q000737:chemistry*; D017975:Ruthenium Compounds / Q000737:chemistry*; D012996:Solutions; D013501:Surface-Active Agents; D013696:Temperature; D014025:Titanium
D011084:Polycyclic Aromatic Hydrocarbons; D017975:Ruthenium Compounds; D012996:Solutions; D013501:Surface-Active Agents; D003407:Creosote; C027646:ruthenium tetraoxide; D014025:Titanium