Study on photocatalytic performance and degradation kinetics of X-3B with lanthanide-modified titanium dioxide under solar and UV illumination.
The present work was focused on photocatalytic oxidation of the model molecule reactive brilliant X-3B by lanthanide-modified TiO(2) samples under artificial solar and UV irradiation. Experimental results showed that the TiO(2) samples doping with lanthanide (Ce and Gd) could greatly enhance the activity of pure TiO(2), and could extend the absorption range to visible region. The optimum doping amount was 0.2 and 0.5at.% for Ce- and Gd-doped TiO(2) particles, respectively. The degradation kinetics of X-3B on Ce-doped TiO(2), Gd-doped TiO(2), and pure TiO(2) were studied as well. The results exhibited that the degradation of X-3B on all the samples were in accordance with the first-order model. The trend of apparent reaction rate constants k(app) was as follows, Gd-doped TiO(2)>Ce-doped TiO(2)>pure TiO(2), under solar illumination. Scatchard plot analysis was used to evaluate the adsorption phenomena of as-prepared samples, and it indicated that lanthanide doping can improve the efficiency of interfacial adsorption of TiO(2) samples. The trend was the same as that of photocatalytic activity.
Xu
Jingjing
J
State Key Laboratory of Bioelectronics, Southeast University, Nanjing, China. xujj@seu.edu.cn
Ao
Yanhui
Y
Fu
Degang
D
Yuan
Chunwei
C
D001391:Azo Compounds / Q000737:chemistry* / Q000528:radiation effects; D002384:Catalysis; D007700:Kinetics; D028581:Lanthanoid Series Elements / Q000737:chemistry*; D009282:Naphthalenesulfonates / Q000737:chemistry* / Q000528:radiation effects; D010084:Oxidation-Reduction; D055668:Photochemical Processes; D013472:Sunlight; D014025:Titanium / Q000737:chemistry*; D014466:Ultraviolet Rays
D001391:Azo Compounds; D028581:Lanthanoid Series Elements; D009282:Naphthalenesulfonates; C520101:Reactive brilliant red X-3B; C009495:titanium dioxide; D014025:Titanium