Vertically aligned single crystal TiO2 nanowire arrays grown directly on transparent conducting oxide coated glass: synthesis details and applications.
Single-crystal one-dimensional (1D) semiconductor architectures are important in materials-based applications requiring a large surface area, morphological control, and superior charge transport. Titania has widespread utility in applications including photocatalysis, photochromism, photovoltaics, and gas sensors. While considerable efforts have focused on the preparation of 1D TiO2, no methods have been available to grow crystalline nanowire arrays directly onto transparent conducting oxide (TCO) substrates, greatly limiting the performance of TiO2 photoelectrochemical devices. Herein, we present a straightforward low temperature method to prepare single crystal rutile TiO2 nanowire arrays up to 5 microm long on TCO glass via a non-polar solvent/hydrophilic substrate interfacial reaction under mild hydrothermal conditions. The as-prepared densely packed nanowires grow vertically oriented from the TCO glass substrate along the (110) crystal plane with a preferred (001) orientation. In a dye sensitized solar cell, N719 dye, using TiO2 nanowire arrays 2-3 microm long we achieve an AM 1.5 photoconversion efficiency of 5.02%.
Feng
Xinjian
X
Department of Electrical Engineering and The Materials Research Institute, The Pennsylvania State University, University Park, Pennsylvania 16802, USA.
Shankar
Karthik
K
Varghese
Oomman K
OK
Paulose
Maggie
M
Latempa
Thomas J
TJ
Grimes
Craig A
CA