title: A new premixed self-etch adhesive for bonding orthodontic brackets.
abstract: OBJECTIVE
  To determine if a new premixed self-etch adhesive can be used to successfully bond orthodontic brackets to enamel.
  
  
  METHODS
  Forty human molars were cleaned, mounted, and randomly divided into two groups. In group 1, 20 teeth were conditioned using the self-etching primer Transbond Plus (3M Unitek, Monrovia, Calif). In group 2, 20 teeth were conditioned using a new premixed self-etching adhesive, AdheSE One (Ivoclar Vivadent Inc, Amherst, NY). Both groups were bonded using brackets precoated with a composite adhesive. The teeth were debonded within half an hour following initial bonding using a universal testing machine. After debonding, the enamel surface was examined under 10x magnifications to determine the amount of residual adhesive remaining on the tooth. A Student's t-test was used to compare the shear bond strength (SBS) of the two groups, and the Chi-square test was used to compare the adhesive remnant index (ARI) scores for the two adhesive systems.
  
  
  RESULTS
  The mean SBS of the brackets bonded to the teeth using AdhesSE One was 3.6 +/- 1.3 MPa and was significantly lower (t = 2.80, P = .01) than the SBS of the brackets bonded using Transbond Plus (x = 5.9 +/- 3.2 MPa). The comparisons of the ARI scores between the two groups (chi2 = 19.26) indicated that bracket failure mode was also significantly different (P < .001), with more adhesive remaining on the teeth bonded using Transbond Plus.
  
  
  CONCLUSIONS
  The SBS of the new premixed self-etching adhesive needs to be increased for it to be successfully used for bonding orthodontic brackets.
authors.affiliation: Department of Orthodontics, University of Iowa, Iowa City, IA 52242, USA. sbishara@msn.com
authors.forename: Samir E
authors.initials: SE
authors.lastname: Bishara
authors.forename: Adam W
authors.initials: AW
authors.lastname: Otsby
authors.forename: Raed
authors.initials: R
authors.lastname: Ajlouni
authors.forename: John
authors.initials: J
authors.lastname: Laffoon
authors.forename: John J
authors.initials: JJ
authors.lastname: Warren
mesh_terms: D000180:Acrylic Resins / Q000737:chemistry; D017005:Dental Debonding; D003743:Dental Enamel / Q000648:ultrastructure; D006801:Humans; D055115:Light-Curing of Dental Adhesives; D008422:Materials Testing; D016910:Orthodontic Brackets; D019279:Resin Cements / Q000737:chemistry*; D033081:Shear Strength; D013314:Stress, Mechanical; D013499:Surface Properties; D013997:Time Factors
chemical_list: D000180:Acrylic Resins; C489662:AdheSE cement; D019279:Resin Cements; C429625:Transbond Plus Self-Etching Primer