Amperometric uric acid sensors based on polyelectrolyte multilayer films.
Uricase (UOx) and polyelectrolyte were used for preparation of a permselective multilayer film and enzyme multilayer films on a platinum (Pt) electrode, allowing the detection of uric acid amperometrically. The polyelectrolyte multilayer (PEM) film composed of poly(allylamine) (PAA) and poly(vinyl sulfate) (PVS) were prepared via layer-by-layer assembly on the electrode, functioning as H(2)O(2)-selective film. After deposition of the permselective film (PAA/PVS)(2)PAA, UOx and PAA were deposited via layer-by-layer sequential deposition up to 10 UOx layers to prepare amperometric sensors for uric acid. Current response to uric acid was recorded at +0.6 V vs. Ag/AgCl to detect H(2)O(2) produced from the enzyme reaction. The response current increased with increasing the number of UOx layers. Even in the presence of ascorbic acid, uric acid can be detected over the concentration range 10(-6)-10(-3) M. The response current and deposited amount of UOx were affected by deposition bath pH and the addition of salt. The deposition of PAA/UOx film prepared in 2 mg ml(-1) solution (pH 11) of PAA with NaCl (8 mg ml(-1)) and 0.1 mg ml(-1) solution (pH 8.5) of UOx with borate (100 mM) resulted in an electrode which shows the largest response to uric acid. The response of the sensor to uric acid was decreased by 40% from the original activity after 30 days.
Hoshi
Tomonori
T
Graduate School of Pharmaceutical Sciences, Tohoku University, Aramaki Aoba-ku, Sendai 980-8578, Japan.
Saiki
Hidekazu
H
Anzai
Jun-Ichi
J