Mesostructured tin oxide as sensitive material for C(2)H(5)OH sensor.
Mesostructured tin oxide with high specific surface area was synthesized using cationic surfactant (cetyltrimethylammonium bromide, CTAB: CH(3)(CH(2))(15)N(+)(CH(3))(3)Br(-)) as the organic template and hydrous tin chloride (SnCl(4).5H(2)O) and NH(4)OH as the inorganic precursors under acidic conditions at ambient temperature. Thermogravimetric analysis (TGA), Fourier transformed infrared (FTIR), X-ray diffraction analysis (XRD), X-ray photoelectron spectrum (XPS) and N(2)-sorption isotherms were used to characterize the mesostructured tin oxide that was formed at room temperature as well as calcined at different temperature. The surface area of mesostructured tin oxide calcined at 400 degrees C is 136 m(2) g(-1). The indirect heating sensor using this material as sensitive body was fabricated on an alumna tube with Au electrodes and platinum wires. Electrical and sensing properties of such a sensor were investigated. It was found that the mesostructured tin oxide with high surface area had higher sensitivity to C(2)H(5)OH and selectivity to gasoline than commercial sample of polycrystalline tin(IV) oxide.
Wang
Yu-De
YD
Department of Materials Science and Engineering, Tsinghua University, 100084 Beijing, PR China; Department of Materials Science and Engineering, Yunnan University, 650091 Kunming, PR China.
Ma
Chun-Lai
CL
Wu
Xing-Hui
XH
Sun
Xiao-Dan
XD
Li
Heng-De
HD