Smooth muscle cell adhesion in surface-modified three-dimensional copolymer scaffolds prepared from co-continuous blends.
In this article, tissue-engineering scaffolds were fabricated from P(epsilon-CL-co-D,L-LA)-PEG-P(epsilon-CL-co-D,L-LA) copolymers using co-continuous blends with polystyrene as the porogen phase. By means of static annealing and following extraction of the porogen phase, pore sizes (channel widths) in the range of 15-350 microm were obtained. Smooth muscle cells were seeded in three-dimensional fibronectin-modified scaffolds of two different pore sizes. Considerably enhanced cell seeding efficiency was found for scaffolds with larger pore sizes, indicating the importance of this parameter to promote effective cell intrusion into bulk materials. Compressive moduli ranged from 2.3 +/- 0.3 to 67 +/- 15 MPa and decreased with increasing pore size. The reverse trend was found for scaffold permeability (kappa), which ranged from 8.5 x 10(-16) to 6.7 x 10(-11) m(2). This was comparable with permeabilities previously reported for scaffolds with higher pore sizes and void volumes, but more irregular pore morphologies. Taken together, the results obtained in this study motivate further investigation for possible future applications in tissue engineering.
Bramfeldt
Hanna
H
Laboratoire de Bioingénierie et de Biophysique de l'Université de Sherbrooke, Department of Chemical Engineering, Université de Sherbrooke, 2500 Blvd de l'Université, Sherbrooke, Quebec J1K2R1, Canada.
Sarazin
Pierre
P
Vermette
Patrick
P
D002448:Cell Adhesion; D002478:Cells, Cultured; D019245:Compressive Strength; D004867:Equipment Design; D005353:Fibronectins / Q000737:chemistry; D006801:Humans; D019344:Lactic Acid / Q000737:chemistry; D032389:Myocytes, Smooth Muscle / Q000166:cytology*; D010539:Permeability; D011091:Polyesters / Q000737:chemistry; D011092:Polyethylene Glycols / Q000737:chemistry; D011108:Polymers / Q000737:chemistry*; D011137:Polystyrenes / Q000737:chemistry; D016062:Porosity; D013499:Surface Properties; D023822:Tissue Engineering / Q000295:instrumentation*; D054457:Tissue Scaffolds / Q000737:chemistry*; D014469:Umbilical Arteries / Q000166:cytology
D005353:Fibronectins; D011091:Polyesters; D011108:Polymers; D011137:Polystyrenes; C016240:polycaprolactone; D019344:Lactic Acid; D011092:Polyethylene Glycols; C033616:poly(lactide)