Synthesis and characterisation of morin-functionalised silica gel for the enrichment of some precious metal ions.
Silica gel was firstly functionalised with aminopropyltrimethoxysilane obtaining the aminopropylsilica gel (APSG). The APSG was reacted subsequently with morin yielding morin-bonded silica gel (morin-APSG). The structure was investigated and confirmed by elemental and thermogravimetric analyses, IR and (13)C NMR spectral studies. Morin-APSG was found to be highly stable in common organic solvents, acidic medium (<2molL(-1) HCl, HNO(3)) or alkaline medium up to pH 8. The separation and preconcentration of Ag(I), Au(III), Pd(II), Pt(II) and Rh(III) from aqueous medium using morin-APSG was studied. The optimum pH values for the separation of Ag(I), Au(III), Pd(II), Pt(II) and Rh(III) on the sorbent are 5.7, 2.2, 3.7, 3.7 and 6.8, giving rise to separation efficiencies of 43.9, 85.9, 97.7, 60.9 and 91.0%, respectively, where the activity was found to be >90% in the presence of acetate ion. The ion sorption capacity of morin-APSG towards Cu(II) at pH 5.5 was found to be 0.249mmolg(-1) where the sorption capacities of Ag(I) and Pd(II) were 0.087 and 0.121mmolg(-1) and 0.222 and 0.241mmolg(-1) at pH 2.2 and 5.7, respectively. This indicates a 1:1 and 1:2 morin/metal ratios at pH 2.2 and 5.7, respectively. Complete elution of the sorbed metal ions was carried out using 10mL (0.5molL(-1) HCl+0.01molL(-1) thiourea) in case of Au(III), Pd(II), Pt(II) and Rh(III) and 10mL 0.5molL(-1) HNO(3) in case of Ag(I). Morin-APSG was successfully employed in the separation and preconcentration of the investigated precious metal ions from some spiking water samples yielding 100-folds concentration factor. The relative standard deviation (R.S.D.) and the T-test (|t|(1)) were calculated.
Hassanien
Mohamed M
MM
Department of Chemistry, Industrial Education College, Beni-Suef, Egypt.
Abou-El-Sherbini
Khaled S
KS