Selective precipitation of Cu from Zn in a pS controlled continuously stirred tank reactor.
Copper was continuously and selectively precipitated with Na(2)S to concentrations below 0.3 ppb from water containing around 600 ppm of both Cu and Zn in a Continuously Stirred Tank Reactor. The pH was controlled at 3 and the pS at 25 (pS=-log(S(2-))) by means of an Ag(2)S sulfide selective electrode. Copper's recovery and purity were about 100%, whereas the total soluble sulfide concentration was below 0.02 ppm. X-ray diffraction (XRD) analysis showed that copper precipitated as hexagonal CuS (covellite). The mode of the particle size distribution (PSD) of the CuS precipitates was around 36 microm. The PSD increased by high pS values and by the presence of Zn. Depending on the turbulence, the CuS precipitates can grow up to 200 microm or fragment in particles smaller than 3 microm in a few seconds. Zn precipitation with Na(2)S at pH 3 and 4, in batch, always lead to Zn concentrations above 1 ppm. Zn precipitated as cubic ZnS (spharelite).
Sampaio
R M M
RM
Sub-department of Environmental Technology, Wageningen University, Biotechnion, Wageningen, The Netherlands.
Timmers
R A
RA
Xu
Y
Y
Keesman
K J
KJ
Lens
P N L
PN
D011232:Chemical Precipitation; D003300:Copper / Q000302:isolation & purification*; D013440:Sulfides / Q000737:chemistry*; D015032:Zinc; D017967:Zinc Compounds
D013440:Sulfides; D017967:Zinc Compounds; D003300:Copper; D015032:Zinc; C017846:cupric sulfide; C031238:zinc sulfide