Patterning cells on optically transparent indium tin oxide electrodes.
The ability to exercise precise spatial and temporal control over cell-surface interactions is an important prerequisite to the assembly of multi-cellular constructs serving as in vitro mimics of native tissues. In this study, photolithography and wet etching techniques were used to fabricate individually addressable indium tin oxide (ITO) electrodes on glass substrates. The glass substrates containing ITO microelectrodes were modified with poly(ethylene glycol) (PEG) silane to make them protein and cell resistive. Presence of insulating PEG molecules on the electrode surface was verified by cyclic voltammetry employing potassium ferricyanide as a redox reporter molecule. Importantly, the application of reductive potential caused desorption of the PEG layer, resulting in regeneration of the conductive electrode surface and appearance of typical ferricyanide redox peaks. Application of reductive potential also corresponded to switching of ITO electrode properties from cell non-adhesive to cell-adhesive. Electrochemical stripping of PEG-silane layer from ITO microelectrodes allowed for cell adhesion to take place in a spatially defined fashion, with cellular patterns corresponding closely to electrode patterns. Micropatterning of several cell types was demonstrated on these substrates. In the future, the control of the biointerfacial properties afforded by this method will allow to engineer cellular microenvironments through the assembly of three or more cell types into a precise geometric configuration on an optically transparent substrate.
Shah
Sunny
S
Department of Biomedical Engineering, University of California, Davis, CA, USA. ssshah@ucdavis.edu
Revzin
Alexander
A
D000818:Animals; D002448:Cell Adhesion / Q000502:physiology; D002450:Cell Communication / Q000502:physiology*; D005898:Glass; D006801:Humans; D008839:Microelectrodes; D011092:Polyethylene Glycols; D017971:Tin Compounds
D017971:Tin Compounds; D011092:Polyethylene Glycols; C109984:indium tin oxide