Synthesis and characterisation of a Ni4 single-molecule magnet with S4 symmetry.
[Ni4Cl4(HL)4] () {H2L=HN(CH2CH2OH)2} has S4 symmetry and crystallises in the tetragonal space group I4(1)/a. Two exchange couplings are observed between the four Ni(II) centres, with J1=7.29 cm(-1) and J2=-2.08 cm(-1), leading to an S=4 ground state. The Ni4 complex shows the onset of frequency dependent signals in the out-of-phase ac susceptibility below 3 K. In single-crystal measurements carried out using a micro-SQUID, hysteresis loops are observed below 0.5 K, confirming that shows slow relaxation of magnetisation. The loops are temperature dependent but only weakly sweep rate dependent due to the presence of small intermolecular interactions, which hinder quantum tunnelling. This exchange bias between Ni4 molecules is also seen in high-frequency high-field EPR measurements, which give the parameters D=-0.75 cm(-1), B4 degrees=-6.7x10(-5) cm(-1) and gz=2.275.
Ferguson
Alan
A
WestCHEM, Department of Chemistry, University of Glasgow, University Avenue, Glasgow, UK G12 8QQ.
Lawrence
Jon
J
Parkin
Andrew
A
Sanchez-Benitez
Javier
J
Kamenev
Konstantin V
KV
Brechin
Euan K
EK
Wernsdorfer
Wolfgang
W
Hill
Stephen
S
Murrie
Mark
M