Controlled solvothermal synthesis of nanosheets, nanobelts, and ultralong nanobelt arrays with honeycomb-like micropatterns of ZnSe on zinc substrate.
Nanosheets, nanobelts, and ultralong nanobelt arrays with honeycomb-like micropatterns of ZnSe were synthesized via a solvothermal reaction of Zn with Se and KBH(4) in ethylenediamine at 200 degrees C for 24 h and subsequent annealing. The control over these nanostructures with different morphologies was achieved by adjusting the KBH(4)/Se molar ratio. The role of KBH(4) in the formation of ZnSe(en)(0.5) nanobelts with different length-to-width ratios was investigated, and a possible mechanism was also proposed to account for the growth and conversion of these precursor nanostructures into ZnSe nanostructures. Current-voltage behaviors of the ultralong nanobelt arrays with honeycomb-like micropatterns were investigated. In addition, variable-aspect ratio ZnS nanosheets and nanowires were also synthesized by adjusting the KBH(4)/thiourea molar ratio in the Zn-thiourea-KBH(4)-ethylenediamine solvothermal system. The results suggest that this method may be employed for the controllable synthesis of other II-VI semiconductor nanostructures such as ZnTe, NiS, MnS, and so forth and provides opportunities for both fundamental research and technological applications.
Zhang
Lihui
L
Key Laboratory of Macromolecular Science of Shaanxi Province, School of Chemistry and Materials Science, Shaanxi Normal University, Xi'an 710062, China.
Yang
Heqing
H
Li
Li
L
Zhang
Ruigang
R
Liu
Ruini
R
Ma
Junhu
J
Xie
Xiaoli
X
Gao
Fei
F