Biodegradation of crosslinked acrylic polymers by a white-rot fungus.
Two synthetic superabsorbent crosslinked acrylic polymers were mineralized by the white-rot fungus Phanerochaete chrysosporium. The amount of polymer converted to CO(2) increased as the amount of polymer added to the cultures increased. In the presence of sufficiently large amounts of the superabsorbents, such that all of the culture fluid was absorbed and a gelatinous matrix was formed, the fungus still grew and mineralization was observed. Neither the polymers, nor their degradation products were toxic to the fungus. While the rates of mineralization were low, all of the polymers incubated in the liquid fungal cultures were completely depolymerized to water soluble products within 15-18 days. The depolymerization of the polymers was observed only in nitrogen limited cultures of the fungus which secrete the lignin degradation system, however, the water soluble products of depolymerization were mineralized in both nutrient limited and sufficient cultures of the fungus. The rate of mineralization of the depolymerized metabolites was more than two times greater in nutrient sufficient cultures. Following longer incubation periods, most (> 80 %) of the radioactivity was recovered in the fungal mycelial mat suggesting that carbon of the polymer had been converted to fungal metabolites.
Sutherland
G R
GR
Biotechnology Center, Utah State University, Logan, UT 84322-4705, USA.
Haselbach
J
J
Aust
S D
SD