Influence of hydroxyapatite on the corrosion resistance of the Ti-13Nb-13Zr alloy.
Electrochemical analyses on the biocompatible alloy Ti-13Nb-13Zr wt% in an electrolyte simulating physiological medium (PBS solution) are reported. Hydroxyapatite (HA) films were obtained on the alloy by electrodeposition at constant cathodic current. Samples of the alloy covered with an anodic-oxide film or an anodic-oxide/HA film were analyzed by open circuit potential and electrochemical impedance spectroscopy measurements during 180 days in the PBS electrolyte. Analyses of the open-circuit potential (E (oc)) values indicated that the oxide/HA film presents better protection characteristics than the oxide only. This behavior was corroborated by the higher film resistances obtained from impedance data, indicating that, besides improving the alloy osteointegration, the hydroxyapatite film may also increase the corrosion protection of the biomaterial.
Duarte
Laís T
LT
Departamento de Química, Universidade Federal de São Carlos, Sao Carlos, SP, Brazil.
Biaggio
Sonia R
SR
Rocha-Filho
Romeu C
RC
Bocchi
Nerilso
N
D000497:Alloys / Q000737:chemistry; D001672:Biocompatible Materials / Q000737:chemistry*; D020099:Coated Materials, Biocompatible / Q000737:chemistry; D003343:Corrosion; D017886:Durapatite / Q000737:chemistry*; D017097:Electric Impedance; D004563:Electrochemistry; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D014025:Titanium / Q000737:chemistry*
D000497:Alloys; D001672:Biocompatible Materials; D020099:Coated Materials, Biocompatible; C090153:titanium alloy (TiNb13Zr13); D017886:Durapatite; D014025:Titanium