Enhancement of leaching copper by electro-oxidation from metal powders of waste printed circuit board.
Oxidation leaching copper from metal powders of waste printed circuit boards (PCBs) was conducted at room temperature in sulfuric acid solution. The result showed that the copper in metal powders was oxidized by Cu(2+) to form CuCl(2)(-) in the presence of chloride ion without electrochemical oxidation. Then, CuCl(2)(-) was oxidized into CuSO(4) by oxygen derived from the air insufflated into leaching solution. The leaching rate of copper reached 100%. The whole reaction took 5.5h because it was limited by the low solubility of the air in water. In the electro-oxidation conditions, the chloride ion was electro-oxidized into ClO(-), which oxidized CuCl(2)(-) into CuSO(4) and ClO(-) was reduced into Cl(-) itself again at the same time. Since Cl(-) was recycled in the solution not only as a complexing agent but also as an oxidant, which made the reaction speed up to 3.5h to reach 100% leaching rate. Leaching solution was concentrated to crystallize CuSO(4).5H(2)O, and crystal liquor was reused to leach copper from metal powders.
Ping
Zhu
Z
College of environmental and chemical Engineering, Shanghai University, Shanghai 200444, China. xhnzp@staff.shu.edu.cn
ZeYun
Fan
F
Jie
Lin
L
Qiang
Liu
L
Guangren
Qian
Q
Ming
Zhou
Z
D003247:Conservation of Natural Resources / Q000379:methods; D003300:Copper / Q000302:isolation & purification*; D055664:Electrochemical Techniques; D004581:Electronics; D007220:Industrial Waste / Q000517:prevention & control*; D010084:Oxidation-Reduction; D013464:Sulfuric Acids / Q000737:chemistry
D007220:Industrial Waste; D013464:Sulfuric Acids; D003300:Copper; C033158:sulfuric acid