title: Postimplant behavior of lightweight polypropylene meshes in an experimental model of abdominal hernia.
abstract: BACKGROUND
  Over the years, reticular prostheses have undergone changes in their structure and composition to give rise to today's partially absorbable lightweight meshes. This study was designed to assess the biological and biomechanical behavior of these prostheses to establish whether they offer any advantages over nonabsorbable lightweight polypropylene prostheses.
  
  
  METHODS
  7 x 5 cm defects were created in the anterior abdominal wall of New Zealand White rabbits and repaired by securing different prostheses to the edges of the defect with a running 4/0 polypropylene suture. The lightweight biomaterials compared were two nonabsorbable meshes: Parietene and Optilene elastic, and two partially absorbable prostheses: Vypro II and Ultrapro. At 14 and 90 days postimplant, tissue/prosthesis specimens were subjected to histological, immunohistochemical, shrinkage, and biomechanical analyses.
  
  
  RESULTS
  Adhesion formation on the peritoneum-facing surface of the meshes was significantly less extensive in the meshes with absorbable components at 90 days postimplant. The newly formed tissue around the prosthetic filaments was comprised of collagen fibers, fibroblasts, blood vessels, and macrophages. The partially absorbable meshes showed higher macrophage proportions (due to remnants of absorbable material and their structure) than the nonabsorbable meshes at 90 days, although differences were not significant. At 90 days postimplant, similar tensile strengths were recorded for all the implants.
  
  
  CONCLUSIONS
  All the prosthetic materials induced good host tissue ingrowth, with no significant differences in tensile strength observed. Our findings suggest that partially absorbable lightweight prostheses could offer advantages over nonabsorbable lightweight meshes since less foreign material persists in the recipient, improving abdominal wall compliance.
authors.affiliation: Department of Surgery, Faculty of Medicine, Networking Research Center on Bioengineering, Biomaterials and Nanomedicine (CIBER-BBN), Alcala University, Alcala de Henares, Madrid, Spain. juanm.bellon@uah.es
authors.forename: Juan M
authors.initials: JM
authors.lastname: Bellon
authors.forename: Marta
authors.initials: M
authors.lastname: Rodriguez
authors.forename: Natalio
authors.initials: N
authors.lastname: Garcia-Honduvilla
authors.forename: Veronica
authors.initials: V
authors.lastname: Gomez-Gil
authors.forename: Gemma
authors.initials: G
authors.lastname: Pascual
authors.forename: Julia
authors.initials: J
authors.lastname: Bujan
mesh_terms: D000818:Animals; D001672:Biocompatible Materials; D001696:Biomechanical Phenomena; D004195:Disease Models, Animal; D046449:Hernia, Abdominal / Q000473:pathology / Q000503:physiopathology / Q000601:surgery*; D008297:Male; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D011126:Polypropylenes; D011817:Rabbits; D013526:Surgical Mesh; D013718:Tensile Strength; D000267:Tissue Adhesions / Q000517:prevention & control
chemical_list: D001672:Biocompatible Materials; D011126:Polypropylenes