Surface plasmon resonance biochip based on ZnO thin film for nitric oxide sensing.
In this study, the design of a novel optical sensor that comprises surface plasmon resonance sensing chip and zinc oxide nano-film was proposed for the detection of nitric oxide gas. The electrical and optical properties of zinc oxide film vary in the presence of nitric oxide. This effect was utilized to prepare biochemical sensors with transduction based on surface plasmon resonance. Due to the refractive index of the transparent zinc oxide film that was deposited on the gold film, however, changes will be observed in the surface plasmon resonance spectra. For this reason, the thickness of zinc oxide film will be investigated and determined in this study. The interaction of nitric oxide with a 20 nm zinc oxide layer on gold leads to the shift of the resonance angle. The analysis on the reflectance intensity of light demonstrates that such effect is caused by the variation of conductivity and permittivity of zinc oxide film. Finally, a shift in surface plasmon resonance angle was measured in 25 ppm nitric oxide at 180 C and a calibration curve of nitride oxide concentration versus response intensity was successfully obtained in the range of 250 to 1000 ppm nitric oxide at lower temperature of 150 C. Moreover, these effects are quasi-reversible.
Feng
Wei-Yi
WY
Institute of Biomedical Engineering, National Taiwan University, Taiwan.
Chiu
Nan-Fu
NF
Lu
Hui-Hsin
HH
Shih
Hsueh-Ching
HC
Yang
Dongfang
D
Lin
Chii-Wann
CW
D015374:Biosensing Techniques / Q000295:instrumentation*; D004867:Equipment Design; D019544:Equipment Failure Analysis; D008567:Membranes, Artificial; D009569:Nitric Oxide / Q000032:analysis*; D015203:Reproducibility of Results; D012680:Sensitivity and Specificity; D020349:Surface Plasmon Resonance / Q000295:instrumentation*; D015034:Zinc Oxide / Q000737:chemistry*
D008567:Membranes, Artificial; D009569:Nitric Oxide; D015034:Zinc Oxide