Investigation of boundary conditions for biomimetic HA deposition on titanium oxide surfaces.
To improve the clinical outcome of metal implants, i.e. earlier loading and reduction of the incidence of revision surgery, better bone bonding ability is wanted. One method to achieve this is to change the surface chemistry to give a surface that facilitates bone bonding in vivo, i.e. a bioactive surface. Crystalline titanium oxide has recently been proven to be bioactive in vitro and is an interesting option to the more common hydroxylapatite (HA) coatings on implants. A materials possible in vitro bioactivity is tested through soaking in simulated body fluid and studies of possible HA formation on the surface. For bioactive materials, the formed HA layer can also be used as a coating. The aim of the current paper is to investigate some boundary conditions for HA formation on crystalline titanium oxide surfaces regarding influence from coating thickness, soaking time and soaking temperature. The influence from soaking time and temperature on the HA growth were investigated on oxidised Ti samples, (24 h at 800 degrees C) resulting in a rutile surface structure. The oxidised samples were tested at three temperatures (4, 37 and 65 degrees C) and four times (1 h, 1 day, 1 week and 4 weeks). The influence from titanium coating thickness on the HA growth was investigated via depositing thin films of crystalline titanium dioxide on Ti plates using a reactive magnetron sputtering process. Four different PVD runs with coating thicknesses between 19 and 74 nm were tested. The soaking temperature had an effect on the HA formation and growth on both rutile surfaces and native oxide on Ti substrates. Higher temperatures lead to easier formation of HA. It was even possible, at 65 degrees C, to grow HA on native titanium oxide from soaking in PBS. The coating quality was better for HA formed at 65 degrees C compared to 37 degrees C. All PVD-coatings showed HA growth after 1 week in PBS at 37 degrees C, thus even very thin coatings of crystalline titanium oxide coatings are bioactive.
Lindgren
M
M
Department of Engineering Sciences, Materials Science, Uppsala University, Uppsala, Sweden.
Astrand
M
M
Wiklund
U
U
Engqvist
H
H
D032701:Biomimetics / Q000379:methods*; D020099:Coated Materials, Biocompatible / Q000737:chemistry*; D003460:Crystallization / Q000379:methods*; D017886:Durapatite / Q000737:chemistry*; D008422:Materials Testing; D010084:Oxidation-Reduction; D013499:Surface Properties; D013696:Temperature; D014025:Titanium / Q000737:chemistry*
D020099:Coated Materials, Biocompatible; C009495:titanium dioxide; D017886:Durapatite; D014025:Titanium