A study on physical and chemical properties of cellulose paper immersed in various solvent mixtures.
The cellulose paper treated in proportional mixture systems showed higher liquid absorption compare to only EtOH and MeOH treatments. It was approximately 40-70% and 50-91% higher for EtOH-NaOH and MeOH-NaOH treated papers, respectively. All conditions apparently bring about an effect of decreased strength for papers. The lowest tensile strength of 13.0 N/mm was found with EtOH and NaOH treated samples after 5(th) repeating wetting-drying stage. But, some conditions gave approximately 21-59.5% higher stretch than untreated samples. The pore size distributions of papers were evaluated with Simons stain procedure and experimental results usually consisted with sorption data. The less intense CH(2)-CH(2)- vibrations (1450-1700 cm(-1)) and C-C and C-O-C peak areas in FTIR spectra indicates lowering H-bonds in solvent treated and dried paper network structure.
Sahin
Halil Turgut
HT
Suleyman Demirel University, Forestry Faculty, Department of Forest Products Engineering, 32260 Isparta, Turkey..
Arslan
Mustafa Burak
MB
Suleyman Demirel University, Forestry Faculty, Department of Forest Products Engineering, 32260 Isparta, Turkey..