A solid-state NMR study of lead and vanadium substitution into hydroxyapatite.
A systematic study on cationic and anionic substitution in hydroxyapatite structures was carried out, with the aim of understanding the impact of ion exchange on the crystalline structure and properties of these materials. Lead and vanadium were chosen for the exchange, due to their known effects on the redox and catalytic properties of hydroxypatites. Hydroxyapatites with variable Pb and V contents, Pb(x)Ca(10-x)(VO(4))(y)(PO(4))(6-y)(OH)(2) (x = 0, 2, 4, 6, 8 and 10 for y = 1; y = 0, 0.5, 1, 2, 3 and 6 for x = 10) were synthesized and characterized by NMR spectroscopy. Solid-state NMR allowed an analysis of the chemical environment of every ion after substitution into the hydroxyapatite network. (43)Ca and (207)Pb NMR spectra at different lead concentrations provided clear evidence of the preferential substitution of lead into the Ca(II) site, the replacement of the Ca(I) site starting at x = 4 for y = 1. Two NMR distinguishable Pb(I) sites were observed in Pb(10)(PO(4))(6)(OH)(2), which is compatible with the absence of a local mirror plane perpendicular to the c direction. In contrast with (31)P NMR, for which only small variations related to the incorporation of Pb are observed, the strong change in the (51)V NMR spectrum indicates that lead perturbs the vanadium environment more than the phosphorus one. The existence of a wide variety of environments for OH in substituted apatites is revealed by (1)H NMR, and the mobility of the water molecules appears to vary upon introduction of lead into the structure.
Pizzala
Hélène
H
Universite Aix-Marseille I-CNRS, UMR 6264 Laboratoire Chimie Provence, Spectrometries Appliquees a la Chimie Structurale, F-13397 Marseille, France.
Caldarelli
Stefano
S
Eon
Jean-Guillaume
JG
Rossi
Alexandre Malta
AM
San Gil
Rosane A S
RA
Laurencin
Danielle
D
Smith
Mark E
ME